Preparation and surface modification of submicron YAl2 particles by mixed milling with magnesium for fabricating YAl2p/MgLiAl composites

A new process for the preparation and surface modification of submicron YAl2 intermetallic particles was proposed to control the agglomeration of ultrafine YAl2 particles and interface in the fabrication of YAl2p/MgLiAl composites. The morphological and structural evolution during mechanical milling of YAl2 powders (< 30 μm) with magnesium particles (~ 100 μm) has been characterized by scanning electron microscopy, transmission electron microscopy, and X-ray diffraction. The results show that YAl2 particles are refined to submicron scale and separately cladded in magnesium coatings after mixed milling with magnesium particles for 20 h. Mechanical and metallurgical bonds have been found in YAl2/Mg interfaces without any interface reactions. Both the refining and mechanical activation efficiencies for YAl2 particles are enhanced, which may be related to the addition of magnesium particles leading to atomic solid solution and playing a role as “dispersion stabilizer”.

Microstructure, properties and application of YAl2 intermetallic compound as particle reinforcements

An yttrium aluminum (YAl2) intermetallic compound ingot was prepared in an induction furnace under vacuum. The microstructure of YAl2 ingot was characterized by optical microscopy, scanning electron microscopy, and X-ray diffraction. The load bearing response of YAl2 intermetallic was investigated and compared with SiC ceramic by indentation combined with optical microscopy and scanning electron microscopy. Additionally, the tensile properties of the Mg–Li matrix composites reinforced with ultrafine YAl2 particles fabricated by planet ball milling were tested. The results show that the intermetallic compound ingot in this experiment is composed of a main face-centered-cubic structure YAl2 phase, a small amount of YAl phase, and minor Y and Al-rich phases. YAl2 intermetallic compound has excellent stability and shows better capability in crack resistance than SiC ceramic. The YAl2 intermetallic compound has better deformation compatibility with the Mg–14Li–3Al matrix than SiC reinforcement with the matrix, which leads to the superior resistance to crack for YAl2p/Mg–14Li–3Al composite compared to SiCp/Mg–14Li–3Al composite.