Theoretical analysis on microwave heating of oil–water emulsions supported on ceramic, metallic or composite plates

A detailed theoretical analysis has been carried out to study efficient heating due to microwaves for one-dimensional (1D) oil–water emulsion samples placed on various ceramic, metallic (reflective) and ceramic–metallic composite supports. Two typical emulsion systems are considered such as oil-in-water (o/w) and water-in-oil (w/o). A preliminary study has been carried out via average power vs emulsion thickness diagram to estimate microwave power absorption within emulsion samples for various cases. The maxima in average power, also termed as ‘resonances’, are observed for specific emulsion thicknesses and the two consecutive resonances of significant magnitudes are termed as R1 and R2 modes. For both o/w and w/o emulsions, it is observed that microwave power absorption is enhanced in presence of metallic and composite supports during both R1 and R2 modes. The efficient heating strategies characterized by ‘large heating rates’ with ‘minimal thermal runaway’ i.e. uniform temperature distributions within the sample have been assessed for each type of emulsion. Based on the detailed spatial distributions of power and temperature for various cases, SiC-metallic composite support may be recommended as an optimal heating strategy for o/w samples with higher oil fractions (0.45) whereas metallic and Alumina-metallic composite supports may be favored for samples with smaller oil fractions (=0.3) during R1 mode. For w/o samples, SiC-metallic composite support may be suitable heating strategy for all ranges of water fractions during R1 mode. During R2 mode, metallic and Alumina-metallic composite supports are favored for both o/w and w/o emulsion samples. Current study recommends the efficient way to use microwaves in a single mode waveguide and the heating strategy can be suitably extended for heating of any other emulsions for which dielectric properties are easily measurable or available in the literature.

Anisotropic optical properties of arrays of gold nanorods embedded in alumina

A series of thin films comprising gold nanorods embedded in an alumina matrix have been fabricated with lengths ranging from 75 to 330 nm. Their optical properties, expressed in terms of extinction - In(T), where T is optical transmittance, have been measured as a function of wavelength, rod length, angle of incidence, and incident polarization state. The results are compared to a Maxwell-Garnett based theory modified to take into account the strongly anisotropic nature of the medium. Transverse and longitudinal plasmon resonances are observed. The interaction between the nanorods leads to the splitting of the longitudinal resonance with the longer-wavelength resonance being forbidden for direct optical observations. The shorter-wavelength resonance related to the symmetric coupling between longitudinal plasma excitations in the nanorods depends on rod length, polarization state, and angle of incidence of the probing light. The impact of electron confinement on the optical properties of the gold rods is also seen and may be incorporated into the Maxwell-Garnett theory by restricting the mean free path of the conduction electrons to produce excellent agreement between observations and the complete theory. Annealing experiments that modify the physical structure of the gold confirm this conclusion.

Growth and properties of gold and nickel nanorods in thin film alumina

Arrays of nickel and gold nanorods have been grown on glass and silicon substrates using porous alumina templates of less than 500 nm thickness. A method is demonstrated for varying the diameter of the nanorods whilst keeping the spacing constant. Optical extinction spectra for the gold nanorods show two distinct maxima associated with the transverse and longitudinal axes of the rods. Adding small quantities of oxygen to the aluminium before anodization is found to improve the sharpness of the extinction peaks. The spectral position of the longitudinal peak is shown to be sensitive to the nanorod diameter for constant length and spacing. For the nickel nanorods it is shown that the magnetic properties are governed by both interactions between the wires and shape anisotropy.

Transesterification of vegetable oils on basic large mesoporous alumina supported alkaline fluorides-Evidences of the nature of the active site and catalytic performances

KF, LiF and CsF/A(2)O(3) catalysts with different loadings from 1 to 20 wt% were prepared using aqueous solutions of the alkaline fluoride compounds by wet impregnation of basic mesoporous MSU-type alumina. The catalysts were activated under At at 400 degrees C for 2 h and monitored by in situ XRD measurements. The catalysts were also characterized using several techniques: N-2 adsorption/desorption isotherms at -196 degrees C, FTIR, DR-UV-vis, CO2-TPD, XRD, Al-27 CP/MAS NMR. These characterizations led to the conclusion that the deposition of alkaline fluorides on the alumina surface generates fluoroaluminates and aluminate species. The process is definitivated at 400 degrees C. The fluorine in these structures is less basic than in the parent fluorides, but the oxygen becomes more basic. The catalysts were tested for the transesterification of fatty esters under different experimental conditions using conventional heating, microwave and Ultrasound irradiation. Recycling experiments showed that these catalysts are stable for a limited number of cycles. (C) 2009 Elsevier Inc. All rights reserved.

Liquid Structure and Dynamics of Aqueous Isopropanol over gamma-Alumina

The liquid structures of thin films of aqueous solutions of 0, 7, 19, 50, and 100 mol % isopropanol above O/Al-terminated gamma-alumina surfaces have been investigated by means of classical molecular dynamics simulations. The structuring effect of the oxide oil the liquid mixtures is strong and heavily dependent on the local structure of the oxide. Two distinct re-ions are found oil the oxide Surface characterized by the degree of coordination of Al atoms. Above octahedral Al atoms, water and isopropanol molecules adsorb via the oxygen atoms to maximize the electrostatic interaction, whereas above tetrahedral Al sites the solvent molecules adsorb via hydrogen atoms with the oxygen atoms away front the surface. More mobility is found in the second layer compared with the first; however, its structure is still influenced significantly by the orientation of molecules in the first adsorbed layer. Qualitatively, the displacement of water from the surface by the adsorption of isopropanol occurs with 2.6 Water molecules lost for every alcohol molecule present based on the effective surface areas of the two species calculated from the pure simulations.