Investigation of moisture condition and Autoclam sensitivity on air permeability measurements for both normal concrete and high performance concrete

While on site measurement of air permeability provides a useful approach for assessing the likely long term durability of concrete structures, no existing test method is capable of effectively determining the relative permeability of high performance concrete (HPC). Lack of instrument sensitivity and the influence of concrete moisture are proposed as two key reasons for this phenomenon. With limited systematic research carried out in this area to date, the aim if this study was to investigate the influence of instrument sensitivity and moisture condition on air permeability measurements for both normal concrete and HPC. To achieve a range of moisture conditions, samples were dried initially for between one and 5 weeks and then sealed in polythene sheeting and stored in an oven at 50 C to internally distribute moisture evenly. Moisture distribution was determined throughout using relative humidity probe and electrical resistance measurements. Concrete air permeability was subsequently measured using standardised air permeability (Autoclam) and water penetration (BS EN: 12390-8) tests to assess differences between the HPCs tested in this study. It was found that for both normal and high performance concrete, the influence of moisture on Autoclam air permeability results could be eliminated by pre-drying (50 ± 1 C, RH 35%) specimens for 3 weeks. While drying for 5 weeks alone was found not to result in uniform internal moisture distributions, this state was achieved by exposing specimens to a further 3 weeks of sealed pre-conditioning at 50 ± 1 C. While the Autoclam test was not able to accurately identify relative HPC quality due to low sensitivity at associated performance levels, an effective preconditioning procedure to obtain reliable air permeability of HPC concretes was identified. © 2013 The Authors

Establishment of a preconditioning regime for air permeability and sorptivity of alkali-activated slag concrete

This study reports an experimental investigation designed to assess the influence of near-surface moisture contents on permeation properties of alkali-activated slag concrete (AASC). Five different drying periods (5, 10, 15, 20 and 25 days) and three AASC and normal concretes with compressive strength grades ranging from C30 to C60 were considered. Assessment of moisture distribution was
achieved using 100 mm diameter cores with drilled cavities. Results indicate that air permeability of AASC is very sensitive to the moisture content and its spatial distribution, especially at relative humidity above 65%. To control the influence of moisture on permeation testing, the recommendation of this paper is that AASC specimens should be dried in controlled conditions at 40 C for 10 days prior to testing. It was also concluded from this study that AASC tends to perform less well, in terms of air permeability and sorptivity, than normal concrete for a given strength grade. This conclusion reinforces the need to further examine AASC properties prior to its widespread practical use.

The influence of reusing ‘Formtex’ controlled permeability

The effects of the reuse of ‘Formtex’ Controlled Permeability Formwork (CPF) liner on strength and durability properties of concrete were investigated at two different water-cement ratios and the results are reported in this paper. Test blocks were cast using the CPF on one side and impermeable formwork (IF) on the opposite side of the mould so that direct comparisons could be made between the two. The strength was assessed using the Limpet pulloff tester and both the air permeability and the water absorption (sorptivity) were measured using the Autoclam Permeability System. Both these instruments measured the ‘covercrete’ properties. In addition, cores cut from the test specimens were subjected to an accelerated carbonation test and a chloride exposure test. The results showed that the ‘Formtex’ CPF increases the surface strength and the durability of concrete compared to the IF. There was an almost complete elimination of blowholes. The permeability of concrete decreased and its resistance to the ingress of both carbon dioxide and chlorides increased when CPF was used. The beneficial effects of the Formtex CPF were most evident in concrete of higher water-cement ratio. With the reuse of the Formtex liner twice, that is a total of three uses, the performance of the CPF to improve the properties of concrete remained almost the same. In this research the CPF liner was cleaned thoroughly between each use, which must be adhered to for site applications for reproducing the beneficial effects observed in the laboratory.

Transport Properties of Self-Consolidating Concrete

The permeability of concrete is influenced by the porosity and the interconnectivity of the pores in the cement paste and the microcracks in concrete, especially in the interface of paste-aggregate. The movements of gases, liquids, and ions through concrete is important because of their interactions with concrete constituents, including pore water, which can alter the integrity of concrete directly and indirectly, leading to the deterioration of structures. This study reports the findings from an investigation carried out to study the effect of the mixture variations on the durability of medium- and high-strength self-consolidating concrete (SCC). The mixture variations studied include the type of mineral admixtures, such as limestone powder (LSP) and pulverized fuel ash (PFA), and viscositymodifying admixtures (VMA) for both medium- and high-strength SCC. Air permeability, water permeability, capillary absorption, and chloride diffusivity were used to assess the durability of SCC mixtures in comparison with normal, vibrated concretes. The results showed that SCC mixtures, for medium- and high-strength grades using PFA followed by LSP, have lower permeability properties compared with normal concretes. SCC made with VMA had a higher sorptivity, air permeability, and water permeability compared with other SCC mixtures, which can be attributed to higher watercement ratio (w/c) and lack of pore filling effect. An in-place migration coefficient was obtained using the in-place ion migration test. This was used to compare the potential diffusivity of different concretes. The results indicated that SCC, for both grades of strength, made with PFA showed much lower diffusivity values in comparison with other mixtures, whereas the SCC mixtures with VMA showed higher diffusivity.

EFFECTS OF 3 DURABILITY ENHANCING PRODUCTS ON SOME PHYSICAL-PROPERTIES OF NEAR-SURFACE CONCRETE

This paper investigates the influence of three fundamentally different durability enhancing products, viz. microsilica, controlled permeability formwork and silane, on some of the physical proper ties of near surface concrete. Microsilica (silica fume) is a pozzolan, controlled permeability formwork (CPF) is used to provide a free draining surface to a concrete form, while silane is a surface treatment applied to hardened concrete to reduce the ingress of water. Comparisons are made between the products when used individually and used in conjunction with each other, with a view to assessing whether the use of combinations of products may be desirable to improve the durability of concrete in certain circumstances. The effect of these materials on various durability parameters, such as freeze-thaw deterioration, carbonation resistance and chloride ingress, is considered in terms of their effect on permeation properties and surface strength. The results indicated that a combination of silane and CPF produces concrete with very low air permeability and sorptivity values. The influence of microsilica was more pronounced in increasing the surface strength of concrete.

‘CLAM’ tests for measuring in-situ permeation properties of concrete

This paper descirbes a simple test measuring the sorptivity (a measure of the absorption property if concrete) and the air and water permeability of concrete on site. Using this test, the decay of pressure is monitired for the air permeability test.whereas water penetrating into the concrete at a constant pressure of 0.01 bar and 1.5 bar are recorded for the sorptivity and the water permeability tests respectively. These tests are essentially non-destructive in nature and a skilled operator is not needed. It is possible to carry out a number of tests quickly and efficiently on site without prior planning. It has been found that statistically satisfactory results can be obtained from a mean of three tests. As the flow lines are largely concentrated within 40 mm from the surface, reasonably reliable results can be obtained by drying the surface even if the surface under test is initially wet.

Repeatability and reliability of new air and water permeability tests for assessing the durability of high-performance concretes

This paper reports on the accuracy of new test methods developed to measure the air and water permeability of high-performance concretes (HPCs). Five representative HPC and one normal concrete (NC) mixtures were tested to estimate both repeatability and reliability of the proposed methods. Repeatability acceptance was adjudged using values of signal-noise ratio (SNR) and discrimination ratio (DR), and reliability was investigated by comparing against standard laboratory-based test methods (i.e., the RILEM gas permeability test and BS EN water penetration test). With SNR and DR values satisfying recommended criteria, it was concluded that test repeatability error has no significant influence on results. In addition, the research confirmed strong positive relationships between the proposed test methods and existing standard permeability assessment techniques. Based on these findings, the proposed test methods show strong potential to become recognized as international methods for determining the permeability of HPCs.