Thermodynamic properties and atomistic structure of the dry amorphous silica surface from a reactive force field model

A force field model of the Keating type supplemented by rules to break, form, and interchange bonds is applied to investigate thermodynamic and structural properties of the amorphous SiO2 surface. A simulated quench from the liquid phase has been carried out for a silica sample made of 3888 silicon and 7776 oxygen atoms arranged on a slab similar to 40 angstrom thick, periodically repeated along two directions. The quench results into an amorphous sample, exposing two parallel square surfaces of similar to 42 nm(2) area each. Thermal averages computed during the quench allow us to determine the surface thermodynamic properties as a function of temperature. The surface tension turns out to be gamma=310 +/- 20 erg/cm(2) at room temperature and gamma=270 +/- 30 at T=2000 K, in fair agreement with available experimental estimates. The entropy contribution Ts-s to the surface tension is relatively low at all temperatures, representing at most similar to 20% of the surface energy. Almost without exceptions, Si atoms are fourfold coordinated and oxygen atoms are twofold coordinated. Twofold and threefold rings appear only at low concentration and are preferentially found in proximity of the surface. Above the glass temperature T-g=1660 +/- 50 K, the mobility of surface atoms is, as expected, slightly higher than that of bulk atoms. The computation of the height-height correlation function shows that the silica surface is rough in the equilibrium and undercooled liquid phase, becoming smooth below the glass temperature T-g.

Cytotoxicity Evaluation of Si-Diatom Frustules in a Mouse Model

Silica additives in bone substitute materials are topical, clinically interesting and have significant support in the Orthopaedic field. Biosilica, e.g isolated from diatoms, has many advantages over its synthetic counterparts, e.g. it is amorphous, thus will be absorbed by the body, however, issues such as purity, presence of endotoxins and cytotoxicity need to be addressed before it can be further exploited. Biosilica isolated from Cyclotella Meneghiniana was then tested in a mouse model, to test the immunological response, organ toxicity (kidney, spleen, liver) and route of metabolism/excretion of silica. Five-week-old Balb-c mice were injected subcutaneously with a single high dose (50mg/ml) of Si-frustules, Si-frustules + organic linker and vehicle only control. Animals were sacrificed at 1d and 28d. The animal studies were conducted under an ethically approved protocol at Queen’s University, Belfast. The animals showed no adverse stress during the experiment and remained healthy until sacrifice. Blood results using ICP-OES analysis suggest the frustules were metabolized between comparator groups at different rates, and clearly showed elevated levels of silicon in groups injected with frustules relative to control. The histology of organs showed no variation in morphology of mice injected frustules relative compared to the control group.
Acknowledgements: The authors would like to thank Marie Curie International Outgoing Fellowships from the EU and Beaufort Marine Biodiscovery Award as part of the Marine Biotechnology Ireland Programme for providing financial support to this project.