Indoor and Outdoor monitoring of photocatalytic activity using a mobile phone app. and a photocatalytic activity indicator ink (paii)

A resazurin (Rz) based photocatalyst activity indicator ink (paii) is used to test the activity of commercial self-cleaning materials. The semiconductor photocatalyst driven colour change of the ink is monitored indoors and outside using a simple mobile phone application that measures the RGB colour components of the digital image of the paii-covered, irradiated sample in real time. The results correlate directly with those generated using a traditional, lab-bound method of analysis (UV–vis spectrophotometry).

Antibacterial titania-based photocatalytic extruded plastic films

Photocatalytic antibacterial low density polyethylene (LDPE)–TiO2 films are produced by an extrusion method and tested for photocatalytic oxidation activity, via the degradation of methylene blue (MB) and photocatalytic antibacterial activity, via the destruction of Escherichia coli. The MB test showed that extruded LDPE films with a TiO2 loading 30 wt.% were of optimum activity with no obvious decrease in film strength, although the activity was less than that exhibited by the commercial self-cleaning glass, Activ®. UVC pre-treatment (9.4 mW cm−2) of the latter film improved its activity, with the level of surface sites available for MB adsorption increasing linearly with UVC dose. Although the MB test revealed an optimum exposure time of ca. 60 min photocatalytic oxidation activity, only 30 min was used in the photocatalytic antibacterial tests in order to combine minimal reduction in film integrity with maximum film photocatalytic activity. The photocatalytic antibacterial activity of the latter film was over 10 times that of a non-UVC treated 30 wt.% TiO2 film, which, in turn was over 100 times more active than Activ®.

The nitric oxide ISO photocatalytic reactor system: Measurement of NOx removal activity and capacity

Although the NO removal-based air-purification ISO method ISO 22197-1:2007 is well established, its preconditioning requirements mean that only the initial activity of the photocatalyst under test is measured owing to the often-reported, gradual alteration of the surface kinetics for NO oxidation by air through the accumulation of surface HNO3. Herein, we compare the photocatalytic NO removal abilities of a number of different, common TiO2 materials, surface-saturated with photogenerated HNO3, with their behaviours observed during the typical 5 h-long ISO standard test. It is found that all the TiO2 materials studied eventually become largely NO to NO2 converters after sufficient exposure to NO under irradiation (>5 h) due to the accumulation of surface HNO3. The UV exposure time, t*, necessary to reach this HNO3 saturated condition is different for each different catalyst. As a consequence, an alternative preconditioning process for the ISO method is proposed which can be used to provide a more realistic measure of the photocatalytic activity of the underlying material and provide a measure of the NOx removing capacity of the photocatalytic material under test.

Powder semiconductor photocatalysis in aqueous solution: An overview of kinetics-based reaction mechanisms

A brief, historical overview of 10 apparently different, although in some cases, upon inspection, closely related, popular proposed reaction mechanisms and their associated rate equations, is given and in which the rate expression for each mechanism is derived from basic principles, Appendix A. In Appendix B, each of the 5 main mechanisms are tested using datasets, comprising initial reaction rate vs. organic pollutant concentration, [P] and incident irradiance, ρ, data, reported previously for TiO2, where P is phenol, 4-chlorophenol and formic acid. The best of those tested, in terms of overall fit, simplicity, usefulness and versatility is the disrupted adsorption kinetic model proposed by Ollis. The usual basic assumptions made in constructing these mechanisms are reported and the main underlying concerns explored.

Targeting of photooxidative damage on single-stranded DNA representing the bcr-abl chimeric gene using oligonucleotide-conjugates containing [Ru(phen)3](2+)-like photosensitiser groups

Photooxidative damage was induced predominantly at a single guanine base in a target DNA by irradiation (lambda > 330 nm) in the presence of complementary oligodeoxynucleotide conjugates (ODN-5'-linker-[Ru(phen)3]2+) (phen = 1,10-phenanthroline). The target DNA represents the b2a2 variant of the chimeric bcr-abl gene implicated in the pathogenesis of chronic myeloid leukaemia, and the sequence of the 17mer ODN component of the conjugate (3' G G T A G T T A T T C C T T C T T 5') was complementary to the junction region of the sense strand sequence of this oncogene. Two different conjugates were prepared, both of them by reaction of the appropriate succinimide ester with 5'-hexylamino-derivatised 17mer ODN. In Ru-ODN-1 (7) the linker was -(CH2)6-NHCO-bpyMe (-bpyMe = 4'-[4-methyl-2,2'-bipyridyl]), whereas in Ru-ODN-2 (13) it was -(CH2)6-NHCO-(CH2)3-CONH-phen. Photoexcitation of either of the conjugates when hybridised with the 32P-5'-end-labelled target 34mer 5'T G A C C A T C A A T A A G G A A G A A G21 C C C T T C A G C G G C C 3' (ODN binding site underlined) led to an alkali-labile site predominantly (> 90%) at the G21 base, which is at the junction of double-stranded and single-stranded regions of the hybrid. Greater yields were found with Ru-ODN-1 (7) than with Ru ODN-2 (13). In contrast to this specific cleavage with Ru-ODN-1 (7) or Ru-ODN-2 (13), alkali-labile sites were generated at all guanines when the 34mer was photolysed in the presence of the free sensitiser [Ru(phen)3]2+. Since [Ru(phen)3]2+ was shown to react with 2'-deoxyguanosine to form the diastereomers of a spiroiminodihydantoin derivative (the product from 1O2 reaction), 1O2 might also be an oxidizing species in the case of Ru-ODN-1 (7) and Ru-ODN-2 (13). Therefore to determine the range of reaction, a series of 'variant' targets was prepared, in which G21 was replaced with a cytosine and a guanine substituted for a base further towards the 3'-end (e.g. Variant 3; 5'T G A C C A T C A A T A A G G A A G A A C C G23 C T T C A G C G G32 C C3'). While it was noted that efficient reaction took place at distances apparently remote from the photosensitiser (e.g at G32, but not G23 for Variant 3), this effect could be attributed to hairpinning of the single-stranded region of the target. These results are therefore consistent with the photooxidative damage being induced by a reaction close to the photosensitiser rather than by a diffusible species such as 1O2.

Controlled periodic illumination in semiconductor photocatalysis

Controlled periodic illumination is a hypothesis postulated in the early 1990s for enhancing the efficiency of semiconductor photocatalytic reactions. This technique has been proposed to improve photocatalytic efficiency by the nature of photon introduction alone. Before its application in semiconductor photocatalysis, controlled periodic illumination had been investigated in other fields including photosynthesis. This paper presents a detailed review of the state of the art research undertaken on the application of controlled periodic illumination in semiconductor photocatalysis. The review briefly introduces semiconductor photocatalysis, and then presents a detailed explanation of this technique, its importance to photocatalytic efficiency, an overview of previous results of its application in significant studies and present knowledge. Results from previous as well as some of the most recent studies indicate potential applications of controlled periodic illumination in areas other than just the improvement of the efficiency of the photocatalytic process.

Kinetics of the photocatalysed oxidation of NO in the ISO 22197 reactor

The photocatalytic reactor described in the NOx removal ISO 22197-1:2007 is used to study the kinetics of the process, using a film of P25 TiO2 which has either been conventionally pre-irradiated in a stream of air, or unconventionally in a stream of NO (1 ppmv). In the former case it is shown that the system does not achieve steady state exit levels of NO, probably due to the gradual accumulation of HNO3 on the surface of the photocatalyst. The NO-preconditioned TiO2 film demonstrated excellent steady-state levels when monitored as a function of NO concentration, [NO] and UV irradiance, ρ. However, in this case the photocatalytic reaction under study is NOT NOx removal, but the conversion of NO to NO2. It is shown that the kinetics of this steady state process fit very well to a kinetic expression based on a disrupted adsorption reaction mechanism, which has also been used by others to fit their observed (non-steady state) kinetics for NOx removal on conventionally-(air) preconditioned films of P25. The appropriateness of this model for either system is questioned, since in both systems the kinetics appear to have a significant mass transport element. These findings suggest that mass transport and non-steady-state kinetics are likely to be significant features for most active photocatalytic samples, where the %NO conversion is >7%, and so limits the usefulness of the NOx removal ISO 22197-1:2007.

Correlation between the photocatalysed oxidation of methylene blue in solution and the reduction of resazurin in a photocatalyst activity indicator ink (Rz Paii)

Assessment of Activity of 'Transparent and Clear' and 'Opaque and Highly Coloured' Photocatalytic Samples using a Fluorescent Photocatalytic Activity Indicator Ink, FPaii.

The photocatalytic activity of self-cleaning glass is assessed using a resazurin (Rz) photocatalyst activity indicator ink, i.e. Rz paii, via both the rate of change in the colour of the ink (blue to pink), R(Abs), and the rate of change in the fluorescence intensity, R(Fl), (λ(excitation) = 593 nm; λ(emission) = 639 nm) of the ink. In both cases the kinetics are zero order. Additional work with a range of glass samples of different photocatalytic activity reveal R(Abs) is directly related to R(Fl), thereby showing that the latter, like the former, can be used to provide a measure of the photocatalytic activity of the sample under test. The measured value of R(Fl) is found to be the same for 5 pieces of, otherwise identical, selfcleaning glass with: black, red, blue, yellow and no coloured tape stuck to their backs, which demonstrates that R(Fl) measurements can be used to measure photocatalytic activity under conditions of high colour and opacity under which R(Abs) cannot be measured. The relevance of this novel, fluorescence-based paii to the assessment of the activity of highly coloured, opaque photocatalytic samples, such as paints and tiles, is discussed briefly.