Delamination and wear in drilling of carbon-fiber reinforced plastic composites using multilayer TiAlN/TiN PVD-coated tungsten carbide tools

This study aims to investigate drilling process in carbon-fiber reinforced plastic (CFRP) composites with multilayer TiAlN/TiN PVD-coated tungsten carbide drill. The effect of process parameters have been investigated in drilling of Hexcel M21-T700GC. Thrust force and torque were measured online throughout the drilling experiments. Delamination were observed using optical microscope and analyzed via a developed algorithm based on digital image processing technique. Surface roughness of each hole was measured using a surface profilometer. In addition, the progression of tool wear in various surfaces of drill was observed using tool microscope and measured using image software. Our results indicate that the thrust force and torque increased with the increasing cutting speed and feed rate. Delamination and average surface roughness that rose with the increase in feed rate, however, decreased with the increasing cutting speed. The average surface roughness tended to increase with the increase in feed rate and decrease with the increasing cutting speed in drilling of carbon-fiber reinforced plastic (CFRP). Feed rate was found as the predominant factor on the drilling outputs. Abrasive wear was observed on both flank and relief surfaces, which created edge wear on cutting edges. No sign of chipping or plastic deformation has been observed on the surfaces of drills. © 2012 The Author(s).

Physical and electrochemical evaluation of ATO supported IrO2 catalyst for proton exchange membrane water electrolyser

Antimony doped tin oxide (ATO) was studied as a support material for IrO₂ in proton exchange membrane water electrolyser (PEMWE). Adams fusion method was used to prepare the IrO₂-ATO catalysts. The physical and electrochemical characterisation of the catalysts were carried out using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), powder conductivity, cyclic voltammetry (CV) and membrane electrode assembly (MEA) polarisation. The BET surface area and electronic conductivity of the supported catalysts were found to be predominantly arisen from the IrO₂. Supported catalyst showed higher active surface area than the pristine IrO₂ in CV analysis with 85% H₃PO₄ as electrolyte. The MEA performance using Nafion®−115 membrane at 80 °C and atmospheric pressure showed a better performance for IrO₂ loading ≥60 wt.% than the pristine IrO₂ with a normalised current density of 1625 mA cm⁻² @1.8 V for the 60% IrO₂-ATO compared to 1341 mA cm⁻² for the pristine IrO₂ under the same condition. The higher performance of the supported catalysts was mainly attributed to better dispersion of active IrO₂ on electrochemically inactive ATO support material, forming smaller IrO₂ crystallites. A 40 wt.% reduction in the IrO₂ was achieved by utilising the support material.

Viscosity and Carbon Dioxide Solubility for LiPF6, LiTFSI, and LiFAP in Alkyl Carbonates: Lithium Salt Nature and Concentration Effect

Cyclic nanoindentation and nano-impact fatigue characterisation of functionally graded TiN/TiNi shape memory film

This paper investigates the mechanism of nanoscale fatigue of functionally graded TiN/TiNi films using nano-impact and multiple-loading-cycle nanoindentation tests. The functionally graded films were deposited on silicon substrate, in which TiNi films maintain shape memory and pseudo elastic behavior, while a modified TiN surface layer provides tribological and anti-corrosion properties. Nanomechanical tests were performed to comprehend the localized film performance and failure modes of the functionally graded film using NanoTestTM equipped with Berkovich and conical indenter between 100 μN to 500 mN loads. The loading mechanism and load history are critical to define film failure modes (i.e. backward depth deviation) including the shape memory effect of the functionally graded layer. The results are sensitive to the applied load, loading type (e.g. semi-static, dynamic) and probe geometry. Based on indentation force-depth profiles, depth-time data and post-test surface observations of films, it is concluded that the shape of the nanoindenter is critical in inducing the localized indentation stress and film failure, including shape recovery at the lower load range. Elastic-plastic finite element (FE) simulation during nanoindentation loading indicated that the location of subsurface maximum stress near the interface influences the backward depth deviation type of film failure. A standalone, molecular dynamics simulation was performed with the help of a long range potential energy function to simulate the tensile test of TiN nanowire with two different aspect ratios to investigate the theory of its failure mechanism.

First comprehensive peat depositional records for tin, lead and copper associated with the antiquity of Europe's largest cassiterite deposits

Tin, as a constituent of bronze, was central to the technological development of early societies, but cassiterite (SnO2) deposits were scarce and located distantly from the centres of Mediterranean civilizations. As Britain had the largest workable ore deposits in the ancient Western world, this has led to much historical speculation and myth regarding the long-distance trading of tin from the Bronze Age onwards. Here we establish the first detailed chronology for tin, along with lead and copper deposition, into undisturbed ombrotrophic (rain-fed) peat bogs located at Bodmin Moor and Dartmoor in the centre of the British tin ore fields. Sustained elevated tin deposition is demonstrated clearly, with peaks occurring at 100-400 and 700-1000 calendar years AD - contemporaneous with the Roman and Anglo-Saxon periods respectively. While pre-Roman Iron Age tin exploitation undoubtedly took place, it was on a scale that did not result in convincingly enhanced deposition of the metal. The deposition of lead in the peat record provides evidence of a pre-Roman metal-based economy in southwest Britain. Emerging in the 4th century BC, this was centred on copper and lead ore processing that expanded exponentially and then collapsed upon Roman colonization during the 1st century AD. (C) 2011 Elsevier Ltd. All rights reserved.

Determining the Effect of Plasma Pre-Treatment on Antimony Tin Oxide to Support Pt@Pd and the Oxygen Reduction Reaction Activity

This article reveals the effect of plasma pre-treatment on antimony tin oxide (ATO) nanoparticles. The effect is to allow Pt@Pd to be deposited homogeneously on the ATO surface with high dispersion and narrow particle size distribution. The Pt@Pd core–shell catalyst was prepared using the polyol method and shows a dramatic improvement towards ORR activity and durability.

The photocatalytic decomposition of microcystin-LR using selected titanium dioxide materials

Microcystins (cyclic heptapeptides) produced by a number of freshwater cyanobacteria are a potential cause for concern in potable water supplies due to their acute and chronic toxicity. TiO₂ photocatalysis is a promising technology for removal of these toxins from drinking water. It is, however, necessary to have a sufficient knowledge of how the catalyst materials cause the degradation of the toxins through the photocatalytic process. The present study reports microcystin degradation products of the photocatalytic oxidation by using a number of commercial TiO₂ powder (P25, PC50, PC500 and UV100) and granular (KO1, KO3, TiCat-C, TiCat-S) materials, so aiding the mechanistic understanding of this process. Liquid chromatography-mass spectrometry analysis demonstrated that the major destruction pathway of microcystin for all the catalysts tested followed almost the same pathway, indicating the physical properties of the catalysts had little effects on the degradation pathway of microcystin-LR. 

Photocatalytic destruction of geosmin using novel pelleted titanium dioxide

Geosmin is produced by cyanobacteria and actinomycetes in surface waters. It causes undesirable earthy off-flavours in freshwater fish and is a major concern for the drinking water industry. This paper presents the first published study on the use of the novel pelleted Ti0₂ photocatalyst, Hombikat K01/C, for the removal of geosmin from water. Ti0₂ in pelleted form eliminates the requirement for the separation of the catalyst from the water following treatment which is normally the case with the widely used powdered catalysts. A laboratory reactor was designed to limit system loss since the compound adsorbs to a wide range of surfaces. Initial concentration, aeration rate and irradiation were evaluated. It was found that degradation of geosmin followed the Langmuir-Hinshelwood model. Elevated aeration had no effect on the photocatalytic removal of geosmin, but increasing irradiation was found to increase degradation rates. The catalyst proved effective within 10 min under optimum conditions. 

The application of Raman and anti-stokes Raman spectroscopy for in situ monitoring of structural changes in laser irradiated titanium dioxide materials

The use of Raman and anti-stokes Raman spectroscopy to investigate the effect of exposure to high power laser radiation on the crystalline phases of TiO₂ has been investigated. Measurement of the changes, over several time integrals, in the Raman and anti-stokes Raman of TiO₂ spectra with exposure to laser radiation is reported. Raman and anti-stokes Raman provide detail on both the structure and the kinetic process of changes in crystalline phases in the titania material. The effect of laser exposure resulted in the generation of increasing amounts of the rutile crystalline phase from the anatase crystalline phase during exposure. The Raman spectra displayed bands at 144 cm^-1 (A1g), 197 cm^-1 (Eg), 398 cm^-1 (B1g), 515 cm^-1 (A1g), and 640 cm^-1 (Eg) assigned to anatase which were replaced by bands at 143 cm^-1 (B1g), 235 cm^-1 (2 phonon process), 448 cm^-1 (Eg) and 612 cm^-1 (A1g) which were assigned to rutile. This indicated that laser irradiation of TiO₂ changes the crystalline phase from anatase to rutile. Raman and anti-stokes Raman are highly sensitive to the crystalline forms of TiO₂ and allow characterisation of the effect of laser irradiation upon TiO₂. This technique would also be applicable as an in situ method for monitoring changes during the laser irradiation process

On-line monitoring of laser modification of titanium dioxide using optical surface second harmonic

TiO₂ photocatalysis is a promising technology for the destruction of organic pollutants in both waste and potable waters with the mineralisation of a wide range of compounds having been reported. TiO ₂ has many advantages over other semiconductors, it is highly photoreactive, cheap, non-toxic, chemically and biologically inert, and photostable. The photocatalytic activity of TiO₂ has been shown to depend upon many criteria including the ratio of anatase/rutile crystal phase, particle size and oxidation state. This paper reports the use of optical surface second harmonic generation (SSHG) to monitor modifications in TiO ₂ powder induced following laser treatment. SSHG is a non-contact, non-destructive technique, which is highly sensitive to both surface chemical and physical changes. Results show that three different SSH intensities were observable as the TiO₂ samples were irradiated with the laser light. These regions were related to changes in chemical characteristics and particle size of the TiO₂ powder

The destruction of 2-methylisoborneol and geosmin using titanium dioxide photocatalysis

Geosmin (GSM) and 2-methylisoborneol (MIB) are semi-volatile compounds produced by cyanobacteria in surface waters. These compounds present problems to the drinking water industry and in aquaculture because they can taint water and fish producing an earthy-musty flavour. This paper presents an initial study on the use of TiO₂ photocatalysis for the destruction of these compounds in water. The process proved effective with the complete destruction of MIB and GSM being achieved within 60 min. These results suggest that TiO₂ photocatalysis will be a successful method for removal of taint compounds from potable water supplies and fish farms. 

Processes influencing surface interaction and photocatalytic destruction of microcystins on titanium dioxide photocatalysts

Microcystins are a family of hepatotoxic peptides produced by freshwater cyanobacteria. Their occurrence in drinking water is of concern since chronic exposure to these toxins causes tumor promotion. It is therefore essential to establish a reliable treatment strategy that will ensure their removal from potable water. We have previously described the rapid destruction of microcystin-LR using TiO₂ photocatalysis, however, since there are at least 70 microcystin variants it is essential that the destruction of a number of microcystins be evaluated. In this study the dark adsorption and destruction of four microcystins was followed over a range of pH. All four microcystins were destroyed although the efficiency of their removal varied. The two more hydrophobic microcystins (-LW and -LF) were found to have high dark adsorption (98 and 91% at pH 4) in contrast to microcystin-RR, which was found to have almost no (only 2-3%) dark adsorption across all pH. 

Hydrogen peroxide enhanced photocatalytic oxidation of microcystin-lR using titanium dioxide

Cyanobacterial toxins present in drinking water sources pose a considerable threat to human health. Conventional water treatment systems have proven unreliable for the removal of these toxins and hence new techniques have been investigated. Previous work has shown that TiO₂ photocatalysis effectively destroys microcystin-LR in aqueous solutions, however non-toxic by-products were detected. It has been shown that photocatalytic reactions are enhanced by utilisation of alternative electron acceptors. We report here enhanced photocatalytic degradation of microcystin-LR following the addition of hydrogen peroxide to the system. It was also found that hydrogen peroxide with UV illumination alone was capable of decomposing microcystin-LR although at a much slower rate than found for TiO₂. No HPLC detectable by-products were found when the TiO₂/UV/H₂O₂ system was used indicating that this method is more effective than TiO₂/UV alone. Results however indicated that only 18% mineralisation occurred with the TiO₂/UV/H₂O₂ system and hence undetectable by-products must still be present. At higher concentrations hydrogen peroxide was found to compete with microcystin-LR for surface sites on the catalyst but at lower peroxide concentrations this competitive adsorption was not observed. Toxicity studies showed that both in the presence and absence of H₂O₂ the microcystin solutions were detoxified. These findings suggest that hydrogen peroxide greatly enhances the photocatalytic oxidation of microcystin-LR.

Factors affecting the photoelectrochemical fixation of carbon dioxide with semiconductor colloids

Carbon dioxide was reduced photocatalytically using aqueous CdS or ZnS colloids containing tetramethylammonium chloride to give the dimeric and tetrameric products namely, oxalate, glyoxylate, glycolate and tartrate. A model is presented to explain the role of the tetramethylammonium ions. Studies were also performed using ZnO, SiC, BaTiO₃ and Sr TiO₃, which in the absence of tetramethylammonium ions produced formate and formaldehyde. The relative quantum efficiencies of the six semiconductors were related to their band gaps and conduction band potentials. The role and effectiveness of several 'hole acceptor' (electron donor) compounds in this process is shown to be related to their redox potentials.