A density functional theory study of hydrogen dissociation and diffusion at the perimeter sites of Au/TiO2

Reactivity of supported gold catalysts is a hot topic in catalysis for many years. This communication reports an investigation on the dissociation of molecular hydrogen at the perimeter sites of Au/TiO2 and the spillover of hydrogen atoms from the gold to the support using density functional theory calculations. It is found that the heterolytic dissociation is favoured in comparison with homolytic dissociation of molecular hydrogen at the perimeter sites. However, the surface oxygen of the rutile TiO2(110) surface at these sites can be readily passivated by the formed OH, suggesting that further dissociation of molecular hydrogen may occur at pure gold sites.

Exchange between sub-surface and surface oxygen vacancies on CeO2(111):a new surface diffusion mechanism

Using first principles calculations for O vacancy diffusion on CeO2(111), we locate a surface diffusion mechanism, the two-step O vacancy exchange one, which is more favored than the most common hopping mechanism. By analyzing the results, we identify quantitatively the physical origin of why the two-step exchange mechanism is preferred.

Observation of the inhomogeneous spatial distribution of MeV ions accelerated by the hydrodynamic ambipolar expansion of clusters

An inhomogeneous spatial distribution of laser accelerated carbon/oxygen ions produced via the hydrodynamic ambipolar expansion of CO₂ clusters has been measured by using CR-39 detectors. An inhomogeneous etch pits spatial distribution has appeared on the etched CR-39 detector installed on the laser propagation direction, while homogeneous ones are appeared on those installed at 45°and 90°from the laser propagation direction. From the range of ions in CR-39 obtained by using the multi-step etching technique, the averaged energies of carbon/oxygen ions for all directions are determined as 0.78 ± 0.09 MeV/n. The number of ions in the laser propagation direction is about 1.5 times larger than those in other directions. The inhomogeneous etch pits spatial distribution in the laser propagation direction could originate from an ion beam collimation and modulation by the effect of electromagnetic structures created in the laser plasma.

Modifications of Surface Properties of Beta Ti by Laser Gas Diffusion Nitriding

Beta-type Ti-alloy is a promising biomedical implant material as it has a low Young’s modulus and is also known to have inferior surface hardness. Various surface treatments can be applied to enhance the surface hardness. Physical vapor deposition and chemical vapor deposition are two examples of this but these techniques have limitations such as poor interfacial adhesion and high distortion. Laser surface treatment is a relatively new surface modification method to enhance the surface hardness but its application is still not accepted by the industry. The major problem of this process involves surface melting which results in higher surface roughness after the laser surface treatment. This paper will report the results achieved by a 100 W continuous wave (CW) fiber laser for laser surface treatment without the surface being melted. Laser processing parameters were carefully selected so that the surface could be treated without surface melting and thus the surface finish of the component could be maintained. The surface and microstructural characteristics of the treated samples were examined using x-ray diffractometry, optical microscopy, three-dimensional surface profile and contact angle measurements, and nanoindentation test.