The use of short time-on-stream in situ spectroscopic transient kinetic isotope techniques to investigate the mechanism of hydrocarbon selective catalytic reduction (HC-SCR) of NOx at low temperatures

The problem of differentiating between active and spectator species that have similar infrared spectra has been addressed by developing short time-on-stream in situ spectroscopic transient isotope experimental techniques (STOS-SSITKA). The techniques have been used to investigate the reaction mechanism for the reduction of nitrogen oxides (NOx) by hydrocarbons under lean-burn (excess oxygen) conditions on a silver catalyst. Although a nitrate-type species tracks the formation of isotopically labeled dinitrogen, the results show that this is misleading because a nitrate-type species has the same response to an isotopic switch even under conditions where no dinitrogen is produced. In the case of cyanide and isocyanate species, the results show that it is possible to differentiate between slowly reacting spectator isocyanate species, probably adsorbed on the oxide support, and reactive isocyanate species, possibly on or close to the active silver phase. The reactive isocyanate species responds to an isotope switch at a rate that matches that of the rate of formation of the main product, dinitrogen. It is concluded that these reactive isocyanates could potentially be involved in the reduction of NOx whereas there is no evidence to support the involvement of nitrate-type species that are observable by infrared spectroscopy.

In situ study of ozone and hybrid plasma Ag-Al catalysts for the oxidation of toluene: Evidence of the nature of the active sites

Silver colloids have been prepared by reducing AgNO3 in aqueous solution and embeded in alumina following a sol-gel procedure in the presence of Pluronic 84 ((EO)(19)(PO)(39)(EO)(19)), as surfactant. Plasma-catalytic experiments aimed at the mineralization of toluene showed that the selectivity to CO2 was significantly increased in the presence of Ag catalysts compared with results obtained using the plasma alone. In-situ studies of the ozone interaction with catalysts provide an insight into the nature of the active sites of supported silver colloids for mineralization reactions. It is noticeable that when ozone is chemisorbed on embedded Ag colloidal catalysts no change in the silver oxidation state or size is found. The population of the chemisorbed species is higher at lower temperatures, where the non-selective decomposition of ozone is smaller. The catalysts exhibit high stability, preserving the structural and textural properties after the catalytic tests, that is indeed very important in the presence of ozone. (C) 2011 Elsevier B.V. All rights reserved.

Investigating the mechanism of the H 2-assisted selective catalytic reduction (SCR) of NOx with octane using fast cycling transient in situ DRIFTS-MS analysis

A mechanistic study of the H-2-assisted Selective Catalytic Reduction (SCR) of NOx with octane as reductant over a Ag/Al2O3 catalyst was carried out using a modified DRIFTS cell coupled to a mass spectrometer Using fast transient cycling switching of H-2 with a time resolution of a few seconds It was possible to differentiate potential reaction intermediates from other moieties that are clearly spectator species Using such a periodic operation mode effects were uncovered that are normally hidden in conventional transient studies which typically consist of a single transient In experiments based on a single transient addition of H-2 to or removal of H-2 from the SCR feed it was found that the changes in the concentrations of gaseous species (products and reactants) were not matched by changes at comparable timescales of the concentration of surface species observed by IR This observation indicates that the majority of sur face species observed by DRIFTS under steady-state reaction conditions are spectators In contrast under fast cycling experimental conditions It was found that a surface isocyanate species had a temporal response that matched that of N-15(2) This suggests that some of the isocyanate species observed by infrared spectroscopy could be important intermediates in the hydrogen-assisted SCR reaction although it is emphasised that this may be dependent on the way in which the infrared spectra are obtained It is concluded that the use of fast transient cycling switching techniques may provide useful mechanistic information under certain circumstances.

Facile in situ synthesis of nanofluids based on ionic liquids and copper oxide clusters and nanoparticles

Two stable nanofluids comprising of mixed valent copper(_I,_II) oxide clusters (<1 nm) suspended in 1-butyl-3-methylimidazolium acetate, [C(₄)mim][OAc], and copper(_II) oxide nanoparticles (<50 nm) suspended in trioctyl(dodecyl) phosphonium acetate, [P-₈₈₈₁₂][OAc], were synthesised in a facile one-pot reaction from solutions of copper(_II) acetate hydrate in the corresponding ionic liquids. Formation of the nanostructures was studied using ¹³C NMR spectroscopy and differential scanning calorimetry (DSC). From a solution of Cu(OAc)₂ in 1-ethyl-3-methylimidazolium acetate, [C₂mim][OAc], crystals were obtained that revealed the structure of [C₂mim][Cu₃(OAc)₅(OH)₂(H₂O)]center dot H₂O, indicating the formation of copper hydroxo-clusters in the course of the reaction. Synthesised nanostructures were studied using transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). Physical properties of the prepared IL-nanofluids were examined using IR and UV-VIS spectroscopy, thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and densitometry. 

Multiaxial Deformation of Polyethylene and Polyethylene/Clay Nanocomposites: In Situ Synchrotron Small Angle and Wide Angle X-Ray Scattering Study

A unique in situ multiaxial deformation device has been designed and built specifically for simultaneous synchrotron small angle X-ray scattering (SAXS) and wide angle X-ray scattering (WAXS) measurements. SAXS and WAXS patterns of high-density polyethylene (HDPE) and HDPE/clay nanocomposites were measured in real time during in situ multiaxial deformation at room temperature and at 55 degrees C. It was observed that the morphological evolution of polyethylene is affected by the existence of clay platelets as well as the deformation temperature and strain rate. Martensitic transformation of orthorhombic into monoclinic crystal phases was observed under strain in HDPE, which is delayed and hindered in the presence of clay nanoplatelets. From the SAXS measurements, it was observed that the thickness of the interlamellar amorphous region increased with increasing strain, which is due to elongation of the amorphous chains. The increase in amorphous layer thickness is slightly higher for the nanocomposites compared to the neat polymer. (C) 2011 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 49: 669-677, 2011

Method for the in situ preparation of a single layer of zeolite Beta crystals on a molybdenum substrate for microreactor applications

A method for the hydrothermal synthesis of a single layer of zeolite Beta crystals on a molybdenum substrate for microreactor applications has been developed. Before the hydrothermal synthesis, the surface of the substrate was modified by an etching procedure that increases the roughness at the nanoscale level without completely eliminating the surface lay structure. Then, thin films of Al2O3 (170 nm) and TiO2 (50 nm) were successively deposited by atomic layer deposition (ALD) on the substrate. The internal Al2O3 film protects the Mo substrate from oxidation up to 550 degrees C in an oxidative environment. The high wettability of the external TiO2 film after UV irradiation increases zeolite nucleation on its surface. The role of the metal precursor (TiCl4 vs TiI4), deposition temperature (300 vs 500 degrees C), and film thickness (50 vs 100 nm) was investigated to obtain titania films with the slowest decay in the superhydrophilic behavior after UV irradiation. Zeolite Beta coatings with a Si/Al ratio of 23 were grown at 140 degrees C for 48 It. After ion exchange with a 10(-4) M cobalt acetate solution, the activity of the coatings was determined in the ammoxidation of ethylene to acetonitrile in a microstructured reactor. A maximum reaction rate of 220 mu mol C2H3N g(-1) s(-1) was obtained at 500 degrees C, with 42% carbon selectivity to acetonitrile. (C) 2007 Elsevier Inc. All rights reserved.

In situ, continuous monitoring of the photoinduced superhydrophilic effect: Influence of UV-type and ambient atmospheric and droplet composition

A controlled-atmosphere chamber, combined with a CCTV system, is used to monitor continuously the change in shape of water droplets on the self-cleaning commercial glass, Activ, and a sol-gel TiO2 substrate during their irradiation with either UVA or UVC light. This system allows the photoinduced superhydrophilic effect (PSH) exhibited by these materials to be studied in real time under a variety of different conditions. UVA was less effective than UVC in terms of PSH for both titania-coated glasses, and plain glass was unaffected by either form of UV irradiation and so showed no PSH activity. With UVA, ozone increased significantly the rate of PSH for both substrates, but had no effect on the wettability of plain glass. For both titania substrates and plain glass, no PSH activity was observed under an O-2-free atmosphere. A more detailed study of the PSH effect exhibited by Activ revealed that doping the water droplet with either an electron acceptor (Na2S2O8), electron donor (Na2S2O4), or simple electrolyte (KCl) in the absence of oxygen did not promote PSH. However, when Activ was UV irradiated, while immersed in a deoxygenated KCl solution, prior to testing for PSH activity, only a small change in contact angle was observed, whereas under the same conditions, but using a deoxygenated persulfate-containing immersion solution, it was rendered superhydrophilic. The correlation between organic contaminant removal and surface wetting was also investigated by using thick sol-gel films coated with stearic acid; the destruction of SA was monitored by FTIR and sudden wetting of the surface was seen to coincide with the substantial removal of the organic layer. The results of this work are discussed in the context of the current debate on the underlying cause of PSH.

Increased diagnosis and detection rates of carcinoma in situ of the breast

The purpose of this study was to identify trends in the diagnosis of carcinoma in situ (CIS) of the breast in the United Kingdom (UK) and the Republic of Ireland (ROI) and to examine the impact of mammography. Data on cases of newly diagnosed CIS of the breast and mode of detection (screen detected or not) were obtained, where available, from regional cancer registries between 1990 and 2007. Age-standardised diagnosis rates for the UK and the ROI, and regional screen detected diagnosis rates were compared by calculating the annual percentage change (APC) over time. The APC of the diagnosis rate amongst women aged 50-64 years (original screening age group) showed a significant 5.9% increase in the UK (1990-2007) and 11.5% increase in the ROI (1994-2007). The rate of diagnosis (50-64 years) stabilized in the UK between 2005 and 2007 and was substantially higher than in other western populations with national screening programmes. The APC of the diagnosis rate amongst those aged 65-69 years showed a significant 12.4% increase in the UK (1990-2007) and 10.3% increase in the ROI (1994-2007). amongst women aged 50-74 years in the UK, approximately 4,300 cases of CIS (˜90% ductal carcinoma in situ) were diagnosed in 2007. Our analyses have shown that screen detected CIS contributed primarily to the increase in diagnosis of CIS of the breast. The high diagnosis rate of screen detected CIS of the breast underlines the need for further research into lesion and patient characteristics that are related to progression of CIS to invasive disease to better target treatment. © 2012 Springer Science+Business Media, LLC.