Fluorescence based fibre optic pH sensor for the pH 10–13 range suitable for corrosion monitoring in concrete structures

The design, development and evaluation of an optical fibre pH sensor for monitoring pH in the alkaline region are discussed in detail in this paper. The design of this specific pH sensor is based on the pH induced change in fluorescence intensity of a coumarin imidazole dye which is covalently attached to a polymer network and then fixed to the distal end of an optical fibre. The sensor provides a response over a pH range of 10.0–13.2 with an acceptable response rate of around 50 min, having shown a very good stability over a period of longer than 20 months thus far. The sensor has also demonstrated little cross-sensitivity to ionic strength (IS) and also excellent photostability through a series of laboratory tests. These features make this type of sensor potentially well suited for in situ long term monitoring of pH in concrete structures, to enhance structural monitoring in the civil engineering sector

Influence of compressive loading on chloride ingress through concrete

Chloride-induced corrosion of steel in concrete is one of most important durability and safety concern for reinforced concrete structures. To study chloride ingress into concrete is thus very important. However, most of the researchers focus on the studying chloride ingress through concrete samples without any loading. In reality concrete structures are subjected to different kinds of loads and therefore studying the effect of such loads on chloride transport is critical. In this work, 28 different concrete mixes were subjected to three levels of compressive load (0%, 50% and 75% of compressive failure load – f) for 24 hours. Further to unloading, these samples were subjected to non-steady state chloride diffusion test as per NT Build 443. The results were compared against the diffusion coefficient obtained for concrete samples that had no previous loading. D value for concretes subjected to 75% f showed a significant increase compared to 0% loading condition, but the increase was insignificant for 50% f. The results indicate that the influence of concrete mixes variables on D is more significant than that of loading level. Surface chloride concentration also increased with the loading level, which might be due to the increased concrete surface area caused by micro cracking.

Chloride ingress and carbonation in concrete exposed to cyclic wetting and drying

Carbonation and chloride ingress are the two main causes of corrosion in reinforced concrete structures. An investigation to monitor the ingress of chlorides and carbonation during a 9 month wetting and drying exposure regime to simulate conditions in which multiple mode transport mechanisms are active was conducted on a variety of binders. The penetration was evaluated using water and acid soluble chloride profiles, and phenolphthalein indicator. X-ray diffraction was also used to determine the presence of bound chlorides and carbonation. The results indicated that acid extraction of chlorides is quantitatively reliable and practical for assessing penetration. The effect of carbonation on binding capability was observed and the relative quantity of chlorides also showed a correlation with the amount of chlorides bound in the form of Friedel’s salt.

Influence of service loading and the resulting micro-cracks on chloride resistance of concrete

Chloride-induced corrosion of steel in reinforced concrete structures is one of the main problems affecting their durability, but most previous research projects and case studies have focused on concretes without cracks or not subjected to any structural load. Although it has been recognised that structural cracks do influence the chloride transport and chloride induced corrosion in reinforced concrete structures, there is little published work on the influence of micro-cracks due to service loads on these properties. Therefore the effect of micro-cracks caused by loading on chloride transport into concrete was studied. Four different stress levels (0%, 25%, 50% and 75% of the stress at ultimate load – fu) were applied to 100 mm diameter concrete discs and chloride migration was measured using a bespoke test setup based on the NT BUILD 492 test. The effects of replacing Portland cement CEMI by ground granulated blast-furnace slag (GGBS), pulverised fuel ash (PFA) and silica fume (SF) on chloride transport in concrete under sustained loading were studied. The results have indicated that chloride migration coefficients changed little when the stress level was below 50% of the fu; however, it is desirable to keep concrete stress less than 25% fu if this is practical. The effect of removing the load on the change of chloride migration coefficient was also studied. A recovery of around 50% of the increased chloride migration coefficient was found in the case of concretes subjected to 75% of the fu when the load was removed.

Effect of Cyclic Carbonation on Chloride Ingression in GGBS Concrete

Carbonation and chloride ingress are the two main causes of corrosion in reinforced concrete structures. An investigation to monitor the ingress of chlorides and the effect of carbonation on chloride ingression during an accelerated 12 month cyclic wetting and drying exposure regime that simulates conditions in which multiple mode transport mechanisms are active was conducted on ground granulated blast furnace slag (GGBS) concrete. The penetration of chloride and carbon dioxide was evaluated using water and acid soluble chloride profiles and phenolphthalein indicator, respectively. The results indicated that when chloride and carbon dioxide ingress concomitantly the effects can be adverse. Carbonation has a detrimental effect on the binding capacity of the concrete, increasing the concentration of free (water soluble) chlorides. This contributed to greater concentration and greater penetration of chlorides and thus an increased corrosion risk.

Monitoring of Corrosion in Structural Reinforcing Bars: performance comparison using in-situ fibre optic and electric wire strain gauge systems

Abstract This work addresses the problems of effective in situ measurement of the initiation or the rate of steel corrosion in reinforced concrete structures through the use of optical fiber sensor systems. By undertaking a series of tests over prolonged periods, coupled with acceleration of corrosion, the performance of fiber Bragg grating-based sensor systems attached to high-tensile steel reinforcement bars (ldquorebarsrdquo), and cast into concrete blocks was determined, and the results compared with those from conventional strain gauges where appropriate. The results show the benefits in the use of optical fiber networks under these circumstances and their ability to deliver data when conventional sensors failed.

Exposure of mortars to cyclic chloride ingress and carbonation

The presence of chloride ions is one of the primary factors causing the degradation of reinforced concrete structures. An investigation to monitor ingress of chlorides during a 24-week wetting and drying exposure regime to simulate conditions in which multiple-mode transport mechanisms are active was conducted on a variety of binders. Penetration was evaluated using free and total chloride profiles. Acid extraction of chlorides is quantitatively reliable and practical for assessing penetration. X-ray diffraction was used to determine the presence of bound chlorides and carbonation. The ability of the cement blends to resist chloride penetration was, from best to worst, ground granulated blast-furnace slag, microsilica, pulverised-fuel ash, Portland cement. The effect of carbonation on binding capability was observed and the relative quantity of chlorides also showed a correlation with the amount of chlorides bound in the form of Friedel’s salt.

Characterization of physio-chemical processes and hydration kinetics in concretes containing supplementary cementitious materials using electrical property measurements

The current study monitors both the short- and long-term hydration characteristics of concrete using discretized conductivity measurements from initial gauging, through setting and hardening, the latter comprising both the curing and post-curing periods. In particular, attention is directed to the near-surface concrete as it is this zone which protects the steel from the external environment and has a major influence on durability, performance and service-life. A wide range of concrete mixes is studied comprising both plain Portland cement concretes and concretes containing fly-ash and ground granulated blast furnace slag. The parameter normalised conductivity was used to identify four distinct stages in the hydration process and highlight the influence of supplementary cementitious materials (SCM) on hydration and hydration kinetics. A relationship has been presented to account for the temporal decrease in conductivity, post 10-days hydration. The testing procedure and methodology presented lend itself to in-situ monitoring of reinforced concrete structures. (c) 2013 Elsevier Ltd. All rights reserved.