Surface deformations as a necessary requirement for resistance switching at the surface of SrTiO3:N

Atomic force microscopy (AFM), conductive AFM and electrochemical strain microscopy were used to study the topography change at the defect surface of SrTiO3:N, breakdown in the electrical conduction of the tip/sample/electrode system and ionic motion. The IV curves show resistance switching behavior in a voltage range ±6 V < U <± 10 V and a current of maximum ±10 nA. A series of sweeping IV curves resulted in an increase in ionically polarized states (surface charging), electrochemical volume (surface deformations) and sequential formations of stable surface protrusions. The surface deformations are reversible (U <± 5 V) without IVpinched hysteresis and remained stable during the resistance switching (U >± 6 V), revealing the additional necessity (albeit insufficient due to 50% yield of working cells) of surface protrusion formation for resistance switching memory.

Water-mediated electrochemical nano-writing on thin ceria films

Bias dependent mechanisms of irreversible cathodic and anodic processes on a pure CeO2 film are studied using modified atomic force microscopy (AFM). For a moderate positive bias applied to the AFM tip an irreversible electrochemical reduction reaction is found, associated with significant local volume expansion. By changing the experimental conditions we are able to deduce the possible role of water in this process. Simultaneous detection of tip height and current allows the onset of conductivity and the electrochemical charge transfer process to be separated, further elucidating the reaction mechanism. The standard anodic/cathodic behavior is recovered in the high bias regime, where a sizable transport current flows between the tip and the film. These studies give insight into the mechanisms of the tip-induced electrochemical reactions as mediated by electronic currents, and into the role of water in these processes, as well as providing a different approach for electrochemical nano-writing.

Epitaxial ferroelectric Pb(Mg1/3Nb2/3)O3-PbTiO3 thin films on La0.7Sr0.3MnO3 bottom electrode

Epitaxial (001)-oriented 0.7Pb(Mg_0.33Nb_0.67)O₃-0.3PbTiO₃ (PMN-PT) thin films were deposited by pulsed laser deposition on vicinal SrTiO₃ (001) substrates using La_0.7Sr_0.3MnO₃ as bottom electrode. Detailed microstructural investigations of these films were carried out using X-ray diffraction (XRD), atomic force microscopy (AFM) and transmission electron microscopy (TEM). Polarization-field hysteresis curves were measured at room temperature. Spontaneous polarization P s , remnant polarization P r and coercive voltage V c were found to be 25 μC/cm², 15 μC/cm² and 0.81 V, respectively. Field dependent dielectric constant measurements exhibited butterfly shaped curves, indicating the true ferroelectric nature of these films at room temperature. The dielectric constant and the dielectric loss at 100 kHz were found to be 238 and 0.14, respectively. The local piezoelectric properties of PMN-PT films were investigated by piezoelectric force microscopy and were found to exhibit a local piezoelectric coefficient of 7.8 pm/V.

Influence of the interfacing with an electrically inhomogeneous bottom electrode on the ferroelectric properties of epitaxial PbTiO3

The influence of an electrically inhomogeneous epitaxial bottom layer on the ferroelectric and electrical properties has been explored in epitaxial PbTiO3 (PTO)/La0.7Sr0.3MnO3 (LSMO) submicron structures using atomic force microscopy. The submicron LSMO-dot structures underneath the ferroelectric PTO film allow exploring gradual changes in material properties. The LSMO interfacial layer influences significantly both electrical and ferroelectric properties of the upper PTO layer. The obtained results show that the as-grown polarization state of an epitaxial ferroelectric layer is strongly influenced by the properties of the layer on top of which it is deposited. (C) 2013 AIP Publishing LLC.

Mask assisted fabrication of nanoislands of BiFeO3 by ion beam milling

We report on a low-damage method for direct and rapid fabrication of arrays of epitaxial BiFeO3(BFO) nanoislands. An array of aluminium dots is evaporated through a stencil mask on top of an epitaxial BiFeO3 thin film. Low energy focused ion beam milling of an area several microns wide containing the array-covered film leads to removal of the bismuth ferrite in between the aluminium-masked dots. By chemical etching of the remaining aluminium, nanoscale epitaxial bismuth ferrite islands with diameter ∼250 nm were obtained. Piezoresponse force microscopy showed that as-fabricated structures exhibited good piezoelectric and ferroelectric properties, with polarization state retention of several days.

Multiferroic PbZrxTi1-xO3/Fe3O4 epitaxial sub-micron sized structures

Large range well ordered epitaxial ferrimagnetic nominally Fe3O4 structures were fabricated by pulsed-laser deposition and embedded in ferroelectric PbZrxTi1-xO3 (x = 0.2, 0.52) epitaxial films. Magnetite dots were investigated by magnetic force microscopy and exhibited magnetic domain contrast at room temperature (RT). Embedding ferroelectric PbZrxTi1-xO3 layers exhibit remnant polarization values close to the values of single epitaxial layers. Transmission electron microscopy demonstrated the epitaxial growth of the composites and the formation of the ferrimagnetic and ferroelectric phases. Physical and structural properties of these composites recommend them for investigations of stress mediated magneto-electric coupling at room temperature. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.3692583]

Epitaxial BiFeO3 nanostructures fabricated by differential etching of BiFeO3 films

We report on differential etching behavior of the different orientations of the polarization in BiFeO3 (BFO), similar to other ferroelectrics, such as LiNbO3. We show how this effect can be used to fabricate epitaxial BiFeO3 nanostructures. By means of piezoresponse force microscopy (PFM) domains of arbitrary shape and size can be poled in an epitaxial BiFeO3 film, which are then reproduced in the film morphology by differential etching. Structures with a lateral size smaller than 200 nm were fabricated and very good retention properties as well as a highly increased piezoelectric response were detected by PFM. (C) 2011 American Institute of Physics. [doi:10.1063/1.3630027]

Ferroelectric nanostructures fabricated by focused-ion-beam milling in epitaxial BiFeO3 thin films

We studied a suitable route to fabricate ferroelectric islands by focused-ion-beam milling in bismuth ferrite epitaxial thin films. Piezoresponse force microscopy shows that the damage induced by the milling process is extended to 1 mu m away from the edge of the focused-ion-beam patterned islands. After a combined vacuum and oxygen atmosphere annealing procedure, ferroelectricity is fully recovered in structures with sizes down to 500 nm, while for 250 nm islands the defects at the interfaces induce polarization direction pinning.

Monodomain strained ferroelectric PbTiO(3) thin films: Phase transition and critical thickness study

This work demonstrates that instead of paraelectric PbTiO(3), completely c-oriented ferroelectric PbTiO(3) thin films were directly grown on (001)-SrTiO(3) substrates by pulsed-laser deposition with thickness up to 340 nm at a temperature well above the Curie temperature of bulk PbTiO(3). The influence of laser-pulse frequency, substrate-surface termination on growth, and functional properties were studied using x-ray diffraction, transmission electron microscopy, and piezoresponse force microscopy. At low growth rates (frequency 8 Hz) a domains were formed for film thickness above 20-100 nm. Due to coherency strains the Curie temperature (T(c)) of the monodomain films was increased approximately by 350 degrees C with respect to the T(c) of bulk PbTiO(3) even for 280-nm-thick films. Nonetheless, up to now this type of growth mode has been considered unlikely to occur since the Matthews-Blakeslee (MB) model already predicts strain relaxation for films having a thickness of only similar to 10 nm. However, the present work disputes the applicability of the MB model. It clarifies the physical reasons for the large increase in T(c) for thick films, and it is shown that the experimental results are in good agreement with the predictions based on the monodomain model of Pertsev et al. [Phys. Rev. Lett. 80, 1988 (1998)].