Optimization strategy for minimizing damage in postbuckling stiffened panels

Composite materials are finding increasing use on primary aerostructures to meet demanding performance targets while reducing environmental impact. This paper presents a finite-element-based preliminary optimization methodology for postbuckling stiffened panels, which takes into account damage mechanisms that lead to delamination and subsequent failure by stiffener debonding. A global-local modeling approach is adopted in which the boundary conditions on the local model are extracted directly from the global model. The optimization procedure is based on a genetic algorithm that maximizes damage resistance within the postbuckling regime. This routine is linked to a finite element package and the iterative procedure automated. For a given loading condition, the procedure optimized the stacking sequence of several areas of the panel, leading to an evolved panel that displayed superior damage resistance in comparison with nonoptimized designs.

Numerical analysis of stiffener runout sections

The recent trend of incorporating more composite material in primary aircraft structures has highlighted the vulnerability of stiffened aerostructures to through-thickness stresses, which may lead to delamination and debonding at the skin-stiffener interface, leading to collapse. Stiffener runout regions are particularly susceptible to this problem and cannot be avoided due to the necessity to terminate stiffeners at rib intersections or at cutouts, interrupting the stiffener load path. In this paper, experimental tests relating to two different stiffener runout specimens are presented and the failure modes of both specimens are discussed in detail. A thinner-skinned specimen showed sudden and unstable crack propagation, while a thicker-skinned specimen showed initially unstable but subsequent stable crack growth. Detailed finite element models of the two specimens are developed, and it is shown how such models can explain and predict the behaviour and failure mode of stiffener runouts. The models contain continuum shell elements to model the skin and stiffener, while cohesive elements using a traction-separation law are placed at the skin-stiffener interface to effectively model the debonding which promotes structural failure.

The Behavior of compressively loaded stiffener runout specimens - Part II: Finite element analysis

The termination of stiffeners in composite aircraft structures give rise to regions of high interlaminar shear and peel stresses as the load in the stiffener is diffused into the skin. This is of particular concern in co-cured composite stiffened structures where there is a relatively low resistance to through-thickness stress components at the skin-stiffener interface. In Part I, experimental results of tested specimens highlighted the influence of local design parameters on their structural response. Indeed some of the observed behavior was unexpected. There is a need to be able to analyse a range of changes in geometry rapidly to allow the analysis to form an integral part of the structural design process.

This work presents the development of a finite element methodology for modelling the failure process of these critical regions. An efficient thick shell element formulation is presented and this element is used in conjuction with the Virtual Crack Closure Technique (VCCT) to predict the crack growth characteristics of the modelled specimens. Three specimens were modelled and the qualitative aspects of crack growth were captured successfully. The shortcomings in the quantitative correlation between the predicted and observed failure loads are discussed. There was evidence to suggest that high through-thickness compressive stresses enhanced the fracture toughness in these critical regions.

The Behavior of compressively loaded stiffener runout specimens - Part I: Experiments

The development of the next generation of civil and military transport aircraft will inevitably see an increased use of advanced carbon fibre composite material in the primary structure if performance targets are to be met. One concern in this development is the vulnerability of co-cured and co-bonded stiffened structures to through-thickness stresses at the skin-stiffener interfaces, particularly in stiffener runout regions. These regions are a consequence of the requirement to terminate stiffeners at cutouts, rib intersections, or other structural features which interrupt the stiffener load path.

This work presents the results of an experimental programme investigating the failure of thick-sectioned stiffener runout specimens loaded in uniaxial compression. For all tests, failure initiated at the edge of the runout and propagated across the skin-stiffener interface. It was found that the failure load of each specimen was greatly influenced by intentional changes in the geometric features of these specimens. High frictional forces at the edge of the runout were also deduced from a fractographic analysis, indicating a predominantly Mode II initial failure mode.

An investigation of Mode I and Mode II fracture toughness enhancement using aligned carbon nanotubes forests at the crack interface

A novel approach for introducing aligned multi-walled carbon nanotubes (MWCNTs) in a carbon-fibre composite pre-impregnated (prepreg) laminate, to improve the through-thickness fracture toughness, is presented. Carbon nanotube (CNT) 'forests' were grown on a silicon substrate with a thermal oxide layer, using a chemical vapour deposition (CVD) process. The forests were then transferred to a pre-cured laminate interface, using a combination of pressure and heat, while maintaining through-thickness CNT alignment. Standard Mode I and four-point bend end-notched flexure Mode II tests were undertaken on a set of specimens and compared with pristine specimens. Mode I fracture toughness for T700/M21 laminates was improved by an average of 31% while for T700/SE84LV specimens, an improvement of 61% was observed. Only T700/M21 specimens were tested in Mode II which yielded an average fracture toughness improvement of 161%. Scanning Electron Microscopy (SEM) showed good wetting of the CNT forest as well as evidence of penetration of the forest into the adjacent plies. © 2013 Elsevier Ltd.

Experimental investigation of thermoforming carbon fibre-reinforced polyphenylene sulphide composites

Pre-consolidated carbon fibre-reinforced polyphenylene sulphide (CF/PPS) laminates were
thermoformed into V-shaped parts via designed out of autoclave thermoforming experiments.
The different processing conditions tested in the experiment have resulted in final
part angles whose differences ranged from 2.087 to 3.431 from the original mould angle.
The test results show that processing conditions influenced finished part dimensions as the
final sample angles were found to decrease relative to the tooling dimensions, as mould
temperature increases. Higher mould temperature conditions produce thinner parts due
to the thermal expansion of mould tools. The mould temperature of 170C, which can
produce parts with high degree of crystallinity as well as small size of crystal, has been
established as the optimal thermoforming condition for CF/PPS composites.

Finite Element Analysis of Drilling of Carbon Fibre Reinforced Composites

Despite the increased applications of the composite materials in aerospace due to their exceptional physical and mechanical properties, the machining of composites remains a challenge. Fibre reinforced laminated composites are prone to different damages during machining process such as delamination, fibre pull-out, microcracks, thermal damages. Optimization of the drilling process parameters can reduces the probability of these damages. In the current research, a 3D finite element (FE) model is developed of the process of drilling in the carbon fibre reinforced composite (CFC). The FE model is used to investigate the effects of cutting speed and feed rate on thrust force, torque and delamination in the drilling of carbon fiber reinforced laminated composite. A mesoscale FE model taking into account of the different oriented plies and interfaces has been proposed to predict different damage modes in the plies and delamination. For validation purposes, experimental drilling tests have been performed and compared to the results of the finite element analysis. Using Matlab a digital image analysis code has been developed to assess the delamination factor produced in CFC as a result of drilling. © Springer Science+Business Media B.V. 2011.