Novel low-temperature photocatalytic titania films produced by plasma-assisted reactive dc magnetron sputtering

Robust, active, anatase titania films, 250 nm thick, are deposited onto glass at low temperatures, i.e., 2.0 for the photocatalytic mineralization of stearic acid. These films are typically 6.9 times more active than a sample of commercial self-cleaning glass, comprising a 15 nm layer of fitania deposited by CVD, mainly because they are much thicker and, therefore, absorb more of the incident UV light. The most active of the films tested comprised particles of P25, but lacked any significant physical robustness. Similar results, but much more quickly obtained, were generated using a photocatalyst- sensitive ink, based on the redox dye, resazurin, Rz. All fitania films tested, including those produced by magnetrom sputtering exhibited photo-induced superhydrophilicity. The possible future application of PAR-DG-MS for producing very active photocatalytic films on substrates not renowned for their high temperature stabilities, such as plastics, is noted. (c) 2006 Elsevier B.V All rights reserved.

Investigation of the effect of the preparation method on the activity and stability of Au/CeZrO4 catalysts for the low temperature water gas shift reaction

The impact of the preparation method on the activity and stability of gold supported on ceria-zirconia low temperature water-gas shift (WGS) catalysts have been investigated. The influence of the gold deposition method, nature of the gold precursor, nature of the washing solution, drying method, Ce: Zr ratio of the support and sulfation of the support have been evaluated. The highest activity catalysts were obtained using a support with a Ce: Zr mole ratio 1: 1, HAuCl4 as the gold precursor deposited via deposition precipitation using sodium carbonate as the precipitation agent and the catalyst washed with water or 0.1 M NH4OH solution. In addition, the drying used was found to be critical with drying under vacuum at room temperature found to be most effective.

Two-dimensional imaging of low temperature laser produced plasmas

Laser induced fluorescence images of a low temperature laser-produced plasma expanding into vacuum are presented and compared to a computer simulation. The complex nature of a plume expanding into background gas is highlighted, along with a potential means of simplifying the study of such systems.

The Langmuir probe as a diagnostic of the electron component within low temperature laser ablated plasma plumes

A Langmuir probe has been used as a diagnostic of the temporally evolving electron component within a laser ablated Cu plasma expanding into vacuum, for an incident laser power density on target similar to that used for the pulsed laser deposition of thin films. Electron temperature data were obtained from the retarding region of the probe current/voltage (I/V) characteristic, which was also used to calculate an associated electron number density. Additionally, electron number density data were obtained from the saturation electron current region of the probe (I/V) characteristic. Electron number density data, extracted by the two different techniques, were observed to show the same temporal form, with measured absolute values agreeing to within a factor of 2. The Langmuir probe, in the saturation current region, has been shown for the first time to be a convenient diagnostic of the electron component within relatively low temperature laser ablated plasma plumes. (C) 1999 American Institute of Physics. [S0034-6748(99)01503-8].

Low temperature conditions in building sandstone: the role of extreme events in temperate environments

Data on rock temperatures has previously been collected to characterise typical diurnal regimes, and more recently to describe short-term variability in extreme locations. However, there is also the case that little is understood concerning the impact of extreme events in otherwise temperate environments. Internal stone temperatures (5?cm) collected during the atypical cold extreme experienced, throughout the UK, in December 2010 show a difference between ambient air temperatures and aspect-related thermal differences, particularly concerning temperature lows and the influence of radiative heating. In this case, debris release was not visible; however, laboratory simulations have shown that under such conditions, surface loss does not necessarily negate the occurrence of internal stone modifications. This preparatory sequence of change demonstrates that surface loss is not the result of one process, but rather many operating over time to sufficiently decrease stone strength to facilitate obvious damage.

Low-Temperature Selective Catalytic Reduction (SCR) of NOx with n-Octane Using Solvent-Free Mechanochemically Prepared Ag/Al2O3 Catalysts

Low-temperature (<200 degrees C) hydrocarbon selective catalytic reduction of NOx has been achieved for the first time in the absence of hydrogen using a solvent-free mechanochemically prepared Ag/Al2O3 catalyst. Catalysts prepared by this ball-milling method show a remarkable increase in activity for the reduction of nitrogen oxides with octane by lowering the light-off temperature by up to 150 degrees C compared with a state-of-the-art 2 wt %Ag/Al2O3 catalyst prepared by wet impregnation. The best catalyst prepared from silver oxide showed 50% NOx conversion at 240 degrees C and 99%, at 302 degrees C. The increased activity is not due to an increased surface area of the support, but may be associated with a change in.the'defeet structure of the alumina surface, leading to the formation of the small silver clusters necessary for the activation of the octane without leading to total combustion. On the other hand, since one possible role of hydrogen is to remove inhibiting species from the silver, we cannot exclude some change in the chemical properties of the silver as a result of the ball-milling treatment.

Deactivation mechanism of a Au/CeZrO4 catalyst during a low-temperature water gas shift reaction

On-stream deactivation during a water gas shift (WGS) reaction over gold supported on a ceria-zirconia catalyst was examined. Although the fresh catalyst has very high low temperature (<200 degrees C) for WGS activity, a significant loss of CO conversion is found under steady-state operations over hours. This has been shown to be directly related to the concentration of water in the gas phase. The same catalyst also undergoes thermal deactivation above 250 degrees C, and using a combined experimental and theoretical approach, a common deactivation mechanism is proposed. In both cases, the gold nanoparticles, which are found under reaction conditions, are thought to detach from the oxide support either through hydrolysis, <200 degrees C, or thermally, > 200 degrees C. This process reduces the metal-support interaction, which is considered to be critical in determining the high activity of the catalyst.

Low-temperature oxidation reactions of ethane over a Pt/Al2O3 catalyst

Oxidative dehydrogenation of ethane was performed under conventional microreactor and TAP reactor conditions over a Pt/Al2O3 catalyst between 100 and 600 degreesC. During TAP studies, no ethene was produced whereas under flow conditions small but significant ethene formation was observed. This is consistent with a mechanism involving the gas-phase production of ethene rather than via a surface reaction. In comparison, both hydrogen and methane formation were found under TAP conditions and the trends with temperature and surface oxide composition are interpreted in terms of successive dehydrogenation steps on the catalyst surface. It is further observed that periodic introduction of the reactants can minimize deactivation processes. (C) 2003 Elsevier Inc. All rights reserved.

A method for studying the structure of low-temperature ionic liquids by XAFS

An in situ method of studying the structure of reactive ionic materials in the solid and liquid states by XAFS is described. These salts have novel catalytic and solvent properties, and the results show that their structure may be studied using transmission XAFS by utilizing pressed disks of BN, graphite, and LiF and is not affected by the sample matrix used.

The water-gas shift reaction over CeO/CuO:Operando SSITKA-DRIFTS-mass spectrometry study of low temperature mechanism

An inverse CeO2/CuO catalyst has been investigated by operando steady-state isotopic transient kinetic analysis (SSITKA) in combination with diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) under 3% CO +3% H2O reactant mixture at 473 K with the aim of determining intermediates involved in the water gas shift reaction at relatively low temperatures. Among the various species detected in the infrared spectra which may be involved in the reaction, i.e. formates, copper carbonyls and carbonates, a particular type of carbonate species is identified as a reaction intermediate on the basis of detailed analysis of the spectra during isotopic exchange in comparison with the change in the corresponding isotopically labelled CO2 product. 

Tubular cathode prepared by a dip-coating method for low temperature DMFC

A novel tubular cathode for the direct methanol fuel cell (DMFC) is proposed, based on a tubular titanium mesh. A dip-coating method has been developed for its fabrication. The tubular cathode is composed of titanium mesh, a cathode diffusion layer, a catalyst layer, and a recast Nafion® film. The titanium mesh is present at the inner circumference of the diffusion layer, while the recast Nafion® film is at the outer circumference of the catalyst layer. A DMFC single cell with a 3.5 mgPt cm tubular cathode was able to perform as well, in terms of power density, as a conventional planar DMFC. A peak power density of 9 mW cm was reached under atmospheric air at 25 °C. © 2006 WILEY-VCH Verlag GmbH & Co. KGaA.