Thermal study of selectively plated nickel sulfamate coatings

Nickel sulfamate solution was applied to mild steel substrates by the process of selective plating. The coated samples were heated to temperatures in the range of 50–1000 °C. Thermal analysis, X-ray diffraction and microscopy techniques were used to investigate the effect of secondary heating on the microstructure, mechanical properties and the composition of the surface coatings.

The microscopy analysis showed that the secondary heating caused diffusion within the coating itself and diffusion between the coating and the substrate as concentrations of iron increased in the coating and nickel appeared in the substrate. This diffusion redistribution also caused a phase transformation in the coating as NiO formed on the surface when the coating was heated in a furnace fitted with a nitrogen flow. However this transformation was found not to occur when the coating was heated in a sealed helium environment. Layer and grain growth occurred as temperature increased with the grains taking their preferred orientation as they were heated.

The surface hardness was found to initially rise up from 565 HV to 600 HV when heated to 200 °C. After 200 °C the surface hardness decreased in two stages before falling to 110 HV by 1000 °C. During tensile testing the coated samples performed marginally better in tension than the uncoated samples, however the temperatures used were not elevated high enough to show any real degradation during the tensile testing of the nickel coating that was shown during hardness testing and the microscopy analysis

The Effect of Antinotches on Domain Wall Mobility in Single Crystal Ferroelectric Nanowires

Changes in domain wall mobility, caused by the presence of antinotches in single crystal BaTiO3 nanowires, have been investigated. While antinotches appeared to cause a slight broadening in the distribution of switching events, observed as a function of applied electric field (inferred from capacitance-voltage measurements), the effect was often subtle. Greater clarity of information was obtained from Rayleigh analysis of the capacitance variation with ac field amplitude. Here the magnitude of the domain wall mobility parameter (R) associated with irreversible wall movements was found to be reduced by the presence of antinotches - an effect which became more noticeable on heating toward the Curie temperature. The reduction in this domain wall mobility was contrasted with the noticeable enhancement found previously in ferroelectric wires with notches. Finite element modeling of the electric field, developed in the nanowires during switching, revealed regions of increased and decreased local field at the center of the notch and antinotch structures, respectively; the absolute magnitude of field enhancement in the notch centers was considerably greater than the field reduction in the center of the antinotches and this was commensurate with the manner in, and degree to, which domain wall mobility appeared to be affected. We therefore conclude that the main mechanism by which morphology alters the irreversible component of the domain wall mobility in ferroelectric wire structures is via the manner in which morphological variations alter the spatial distribution of the electric field.

Comparison of the cidal activity of tea tree oil and terpinen-4-ol against clinical bacterial skin isolates and human fibroblast cells

Aim: The aim of this study was to compare both the antimicrobial activity of terpinen-4-ol and tea tree oil (TTO) against clinical skin isolates of meticillin-resistant Staphylococcus aureus (MRSA) and coagulase-negative staphylococci (CoNS) and their toxicity against human fibroblast cells.

Marketing secondhand goods in late medieval England

Purpose – The purpose of this paper is to identify the main practitioners, goods, customers and locations of secondhand marketing activities in late medieval England. It questions how important was the economic role played by such markets and what was the interaction with more formal market structures?

Design/methodology/approach – A broad range of evidence was examined, covering the period from 1200 to 1500: regulations, court rolls, wills, manorial accounts, literature, and even archaeology. Such material often provided mere scraps of information about marginal marketing activity and it was important to recognise the severe limitations of the evidence. Nevertheless, a wide survey of the available sources can give us an insight into medieval attitudes towards such trade, as well as reminding us that much marketing activity occurred beyond the reach of the surviving documentation.

Findings – Late medieval England had numerous outlets for secondhand items, from sellers of used clothes and furs who wandered the marketplaces to craftsmen who recycled and mended old materials. Secondhand marketing was an important part of the medieval makeshift economy, serving not only the needs of the lower sectors of society but also those aspiring to a higher status. However, it is unlikely that such trade generated much profit and the traders were often viewed as marginal, suspicious and even fraudulent.

Originality/value – There is a distinct lack of research into the extent of and significance of medieval secondhand marketing, which existed in the shadowy margins of formal markets and is thus poorly represented in the primary sources. A broad-based approach to the evidence can highlight a variety of important issues, which impact upon the understanding of the medieval English economy.

High Reactivity of Metal-Organic Frameworks under Grinding Conditions: Parallels with Organic Molecular Materials

Interconversion made easy: Metal–organic frameworks (MOFs) are surprisingly reactive under grinding conditions and can perform various rearrangements (see picture). In this respect, the results reveal clear parallels between MOFs and organic molecular materials.

A metal complex that imitates a micelle

A metal complex with a micelle-like, core-shell structure adopts higher nuclearity in water than in organic solvents, thereby imitating also the growth of a micelle, but through covalent rather than non-covalent aggregation.

Ionic liquid S-alkylthiouronium salts

The prepn. and characterization of a series of ionic liqs. based on S-alkylthiouronium cations prepd. from thiourea, 1,3-dimethylthiourea, 1,3-diethylthiourea and 1,3-tetramethylthiourea coupled with bis{(trifluoromethane)sulfonyl}imide, bromide, methylsulfate or ethylsulfate anions are reported. All are liqs. at room temp. or solids with m.ps. close to room temp., except for the bromide salts, which have m.ps. below 92 °C. Systematic variation in the N- and S-alkyl substituents demonstrates how the phys. properties of these ionic liqs. can be readily controlled. The mutual miscibility limits of representative examples with octane, dodecane and toluene have been detd. as a function of temp., and the extn. of dibenzothiophene from dodecane as a model for desulfurisation of diesel has been investigated.

Domain Bundle Boundaries in Single Crystal BaTiO3 Lamellae: Searching for Naturally Forming Dipole Flux-Closure / Quadrupole Chains

Naturally occurring boundaries between bundles of 90o stripe domains, which form in BaTiO3 lamellae on cooling through the Curie Temperature, have been characterised using both piezoresponse force microscopy (PFM) and scanning transmission electron microscopy (STEM). Detailed interpretation of the dipole configurations present at these boundaries (using data taken from PFM) shows that, in the vast majority of cases, they are composed of simple zigzag 180° domain walls. Topological information from STEM shows that, occasionally, domain bundle boundaries can support chains of dipole flux closure and quadrupole nanostructures, but these kinds of boundaries are comparatively rare; when such chains do exist, it is notable that singularities at the cores of the dipole structures are avoided. The symmetry of the boundary shows that diads and centres of inversion exist at positions where core singularities should have been expected.

The application of colloidal gas aphrons in the recovery of fine cellulose fibres from paper mill wastewater

Colloidal gas aphrons (CGAs) are micron-sized gas bubbles of 25–30 µm in diameter produced by a high-speed stirrer in a vessel containing dilute surfactant solution. These bubbles, because of their small size, exhibit some colloidal properties. In this work, CGAs were used to separate fine fibres from a lean slurry of cellulosic pulp in a flotation column. The pulp fibres were recovered as foamate from the top. Sodium dodecyl sulphate at a concentration of 2.0 kg/m3 was used as a surfactant to generate the CGAs in a spinning disc apparatus. The results indicated that up to 70% flotation efficiency could be obtained within a short column height of 0.3–0.35 m. This technique can be applied to recover fine cellulosic pulp from paper-machine backwater.

Adsorption of Ni(SO4) on Malaysian rubber-wood ash

The possible use of wood ash as an adsorbent of nickel sulphate from dilute solutions and the effect of operating parameters were investigated in this study. The rate constants of adsorption were determined at different concentrations and temperatures. The applicability of the first-order reversible equation and an empirical kinetic model were tested to understand the kinetics of nickel sulphate removal at different concentrations. Pore diffusion was found as the rate-controlling step. The Langmuir and Freundlich isotherms were applied to find out the adsorption parameters. The activation energy of adsorption was -11.54 kJ mol-1. The value of the enthalpy change was ?H=-10.35 kcal mol-1.

Mass transfer correlation in flotation of palm oil by colloidal gas aphrons

Colloidal gas aphrons (CGAs) are micron-sized bubbles, which are produced by stirring a dilute surfactant solution at a high speed. In this work, CGAs have been used to clarify oily wastewater by flotation technique. The CGAs sparging rate was a critical factor that governed the efficiency of the process. A model for the determination of the mass transfer coefficient is also developed for the purpose of process design.

A stereocontrolled method for the synthesis of D- and L-2-deoxy-C-nucleosides using an intramolecular Sakurai-type cyclisation reaction

A novel synthetic procedure has been developed that provides access to D/L-2-deoxy-C-nucleosides from 3,4-epoxytetrahydrofuran in seven steps and in moderate to good yields. The key chemical transformation was the Lewis acid catalysed intramolecular cyclisation reaction of an acetal for which the stereochemical outcome was dependent of the reagents' ratio.