Structural and magnetic properties of Ni1-xZnxFe2O4 (x=0, 0.5 and 1) nanopowders prepared by sol-gel method

A series of nanostructured Ni-Zn ferrites Ni1-xZnxFe2O4 (x=0, 0.5 and 1) with a grain size from 24 to 65 nm have been prepared with a sol-gel method. The effect of composition and sintering temperature on morphology, magnetic properties, Curie temperature, specific heating rate at 295 kHz and hysteresis loss have been studied. The highest coercivity of 50 and 40 Oe, were obtained for NiFe2O4 and Ni0.5Zn0.5Fe2O4 samples with the grain size of 35 and 29 nm, respectively. The coercivity of Ni and Ni-Zn mixed ferrites decreased with temperature. The Bloch exponent was 1.5 for all samples. As the grain size increased, the Curie temperature of NiFe2O4 increased from 849 to 859 K. The highest saturation magnetization of 70 emu/g at 298 K and the highest specific heating rate of 1.6 K/s under radiofrequency heating at 295 kHz were observed over NiFe2O4 calcined at 1073 K. Both the magnitude of the hysteresis loss and the temperature dependence of the loss are influenced by the sintering temperature and composition.

Quantum yield measurements for the photocatalytic oxidation of Acid Orange 7 (AO7) and reduction of 2,6-dichloroindophenol (DCIP) on transparent TiO2 films of various thickness

This work comprises the photoactivity assessment of transparent sol–gel TiO2 coatings of various thickness using two test systems. The initial rates of both photocatalytic reactions, namely the oxidative bleaching of Acid Orange 7 (AO7) and the reductive bleaching of 2,6-dichlorindophenol (DCIP) increase linearly with increasing titania film thickness as well as with increasing absorbed light flux. The latter work revealed quantum yields (QY) of 0.19% and 92% for the AO7 and DCIP test system, respectively. The low QY for the AO7 oxidation is due to the combination of a slow irreversible reduction of oxygen and also for the oxidation of AO7, thus favouring the high efficiency for electron–hole recombination that is typical for aqueous organic pollutants. In contrast, the very high QY for the photocatalysed reduction of DCIP is due to the presence of a vast excess of glycerol which traps the photogenerated holes efficiently and so allow time for the slower reduction of dye to take place. Furthermore, the oxidation of glycerol results in the generation of highly reducing R-hydroxyalkyl radicals that are able to also reduce DCIP. As a consequence of this ‘current doubling’ effect, the observed QY (92%) is much higher than the apparent theoretical value of 50%.

Novel titania sol-gel derived film for luminescence-based oxygen sensing.

A novel method for the preparation of titania sol–gel derived oxygen sensors based on the ruthenium(II) dye, [Ru(bpy)3]2+, is described. A titania sol–gel paste film was cast onto microscope slides, and the dye ion-paired to the deprotonated, hydroxylated groups on the film's surface from an aqueous solution of the dye at pH 11. The resulting sensor film is extremely oxygen sensitive, with a PO2 (S = 1/2) value (i.e. the partial pressure of oxygen required in order to reduce the original, oxygen free, luminescence intensity by 50%) of 0.011 atm. The sensor undergoes 95% response to oxygen in 4 s, and shows 95% recovery of its luminescence in argon within 7 s.

Photocatalytic activity indicator inks for the probing a wide range of surfaces

Three photocatalyst inks based on the redox dyes, Resazurin (Rz), Basic Blue 66 (BB66) and Acid Violet 7 (AV7), are used to assess the photocatalytic activities of a variety of different materials, such as commercial paint, tiles and glass and laboratory made samples of sol–gel coated glass and paint, which collectively exhibit a wide range of activities that cannot currently be probed by any one of the existing ISO tests. Unlike the ISO tests, the ink tests are fast (typically <10 min), simple to employ and inexpensive. Previous work indicates that the Rz ink test at least correlates linearly with other photocatalytic tests such as the photomineralisation of stearic acid. The average time to bleach 90% of the key RGB colour component of the ink, red for Rz and BB66 inks and green for AV7 ink, is determined, ttb(90), for eight samples of each of the different materials tested. Five laboratories conducted the tests and the results revealed an average repeatability and reproducibility of: ca. 11% and ca 21%, respectively, which compare well with those reported for the current ISO tests. Additional work on commercial self-cleaning glass using an Rz ink showed that the change in the red component of the RGB image of the ink correlated linearly with that of the change of absorbance at 608 nm, as measured using UV/vis spectroscopy, and the change in the a* component of the Lab colour analysis of the ink, as measured using diffuse reflectance spectroscopy. As a consequence, all three methods generate the same ttb(90). The advantages of the RGB digital image analysis method are discussed briefly.