Finite element modelling of the formation of pre-load damage in cement mantles of orthopaedic joint replacements

Finite element modeling of the formation of pre-loaded damage in cement mantles of orthopaedic joint replacements was presented. The existence of cracking suggested a high level of residual stress. The direction of maximum principal stress vectors corresponded well with the observed crack orientation. Results suggested that cracking depends upon a combination of residual stress, porosity and temperature rise during polymerization.

Characterizing wear processes on orthopaedic materials using scanning probe microscopy

The operational lifetime of hip replacement prostheses can be severely limited due to the occurrence of excessive wear at the load-bearing interfaces. The aim of this study was to investigate how the surface topography of articulating counterfaces evolves over the duration of a laboratory wear run. It was observed that modular stainless steel femoral heads wearing against ultrahigh molecular weight polyethylene (UHMWPE) can themselves be subject to wearing. A comparison with retrieved in vivo-aged femoral heads shows many topographical similarities: in a qualitative sense, scratching and pitting are evident on laboratory and in vivo-worn femoral heads; quantitatively, roughness comparisons between the new and worn devices are seen to increase typically by a factor of 4 after laboratory wearing. The observations suggest that a particular wear mode, namely third-body wear, is responsible for the increased roughness. It is conjectured that third bodies might arise through surface fatigue wear on the metal counterface, Wear debris is also observed to have been generated from the polymer surface, creating rounded debris with sizes predominantly in the range 0.4-0.8 microns: dimensions that are comparable to values previously reported for in vivo generated debris.