Dual template synthesis of a highly mesoporous SSZ-13 zeolite with improved stability in the methanol-to-olefins reaction

The dual template synthesis of zeolite SSZ-13 by use of trimethyl-adamantanammonium hydroxide and a diquaternary-ammonium mesoporogen induces considerable mesoporosity without impeding zeolite microporosity. The strongly improved accessibility of Bronsted sites in mesoporous SSZ-13 increases its stability during application as an acid catalyst in the methanol-to-olefins reaction.

Dry gel conversion of organosilane templated mesoporous silica: from amorphous to crystalline catalysts for benzene oxidation

Mesoporous silica grown using [3-(trimethoxysilyl)propyl]octadecyldimethylammonium chloride as the mesoporogen in the presence of Fe and Al is X-ray amorphous, but contains very small domains with features of MFI zeolite as evidenced by IR and Raman spectroscopy. When applied as a catalyst, this amorphous sample shows good performance in the selective oxidation of benzene using nitrous oxide. Addition of tetrapropylammonium as structure directing agent to the as-synthesized mesoporous silica and subsequent dry gel conversion results in the formation of hierarchical Fe/ZSM-5 zeolite. During dry gel conversion the wormhole mesostructure of the initial material is completely lost. A dominant feature of the texture after crystallization is the high interconnectivity of micropores and mesopores. Substantial redistribution of low-dispersed Fe takes place during dry gel conversion towards highly dispersed isolated Fe species outside the zeolite framework. The catalytic performance in the oxidation of benzene to phenol of these highly mesoporous zeolites is appreciably higher than that of the parent material.

Rapid, simple method for determining the porosity of mesoporous TiO2 films using a quartz crystal microbalance (QCM)

Two different mesoporous films of TiO2 were coated onto a QCM disc and fired at 450o C for 30 min. The first film was derived from a sol-gel paste that was popular in the early days of dye-sensitised solar cell, i.e. dssc, research, a TiO2(sg) film. The other was a commercial colloidal paste used to make examples of the current dssc cell; a TiO2(ds) film. A QCM was used to determine the mass of the TiO2 film deposited on each disc and the increase in the mass of the film when immersed in water/glycerol solutions with wt% values spanning the range 0-70%. The results of this work reveal that with both TiO2 mesoporous films the solution fills the film's pores and acts as a rigid mass, thereby allowing the porosity of each film to be calculated as: 59.1% and 71.6% for the TiO2(sg) and TiO2(ds) films, respectively. These results, coupled with surface area data, allowed the pore radii of the two films to be calculated as: 9.6 and 17.8 nm, respectively. This method is then simplified further, to just a few frequency measurements in water and only air to reveal the same porosity values. The value of the latter ‘one point’ method for making porosity measurements is discussed briefly.

An effective three-dimensional ordered mesoporous ZnCo2O4 as electrocatalyst for Li-O2 batteries

Three-dimensional ordered mesoporous (3DOM) ZnCo₂O₄ materials have been synthesized via a hard template and used as bifunctional electrocatalysts for rechargeable Li-O₂ batteries. The as-prepared ZnCo₂O₄ nanoparticles possess a high specific surface area of 127.2 m² g^-1 and a spinel crystalline structure. The Li-O₂ battery utilizing 3DOM ZnCo₂O₄ shows a higher specific capacity of 6024 mAh g^-1 than that with pure Ketjen black (KB). Moreover, the ZnCo₂O₄-based electrode enables much enhanced cyclability with a smaller discharge-recharge voltage gap than that of the carbon-only cathode. Such excellent catalytic performance of ZnCo₂O₄ could be associated with its larger surface area and 3D ordered mesoporous structure

An effective three-dimensional ordered mesoporous CuCo2O4 as electrocatalyst for Li-O2 batteries

Three-dimensional ordered mesoporous (3DOM) CuCo₂O₄ materials have been synthesized via a hard template and used as bifunctional electrocatalysts for rechargeable Li-O₂ batteries. The characterization of the catalyst by X-ray diffractometry and transmission electron microscopy confirms the formation of a single-phase, 3-dimensional, ordered mesoporous CuCo₂O₄ structure. The as-prepared CuCo₂O₄ nanoparticles possess a high specific surface area of 97.1 m² g^{- 1} and a spinel crystalline structure. Cyclic voltammetry demonstrates that mesoporous CuCo₂O₄ catalyst enhances the kinetics for either oxygen reduction reaction (ORR) or oxygen evolution reaction (OER). The Li-O₂ battery utilizing 3DOM CuCo₂O₄ shows a higher specific capacity of 7456 mAh g^{- 1} than that with pure Ketjen black (KB). Moreover, the CuCo₂O₄-based electrode enables much enhanced cyclability with a 610 mV smaller discharge-recharge voltage gap than that of the carbon-only cathode at a current rate of 100 mA g^{- 1}. Such excellent catalytic performance of CuCo₂O₄ could be associated with its larger surface area and 3D ordered mesoporous structure. The excellent electrochemical performances coupled with its facile and cost-effective way will render the 3D mesoporous CuCo₂O₄ nanostructures as attractive electrode materials for promising application in Li-O₂ batteries.