Investigation into the effect of molybdenum-site substitution on the performance of Sr2Fe1.5Mo0.5O6-δ for intermediate temperature solid oxide fuel cells

In this paper, niobium doping is evaluated as a means of enhancing the electrochemical performance of a Sr₂Fe_1.5Mo_0.5O_6-δ (SFM) perovskite structure cathode material for intermediate temperature solid oxide fuel cells (IT-SOFCs) applications. As the radius of Nb approximates that of Mo and exhibits +4/+5 mixed valences, its substitution is expected to improve material performance. A series of Sr₂Fe_1.5Mo_0.5-xNb_xO_6-δ (x = 0.05, 0.10, 0.15, 0.20) cathode materials are prepared and the phase structure, chemical compatibility, microstructure, electrical conductivity, polarization resistance and power generation are systematically characterized. Among the series of samples, Sr₂Fe_1.5Mo_0.4Nb_0.10O_6-δ (SFMNb_0.10) exhibits the highest conductivity value of 30 S cm^-1 at 550°C, and the lowest area specific resistance of 0.068 Ω cm² at 800°C. Furthermore, an anode-supported single cell incorporating a SFMNb_0.10 cathode presents a maximum power density of 1102 mW cm^-2 at 800°C. Furthermore no obvious performance degradation is observed over 15 h at 750°C with wet H₂(3% H₂O) as fuel and ambient air as the oxidant. These results demonstrate that SFMNb shows great promise as a novel cathode material for IT-SOFCs.

Investigation into the effect of Fe-site substitution on the performance of Sr2Fe1.5Mo0.5O6-δ anodes for SOFCs

Ni-substituted Sr₂Fe_1.5-xNi_xMo_0.5O_6-δ (SFNM) materials have been investigated as anode catalysts for intermediate temperature solid oxide fuel cells. Reduced samples (x = 0.05 and 0.1) maintained the initial perovskite structure after reduction in H₂, while metallic nickel particles were detected on the grain surface for x = 0.2 and 0.3 using transmission electron microscopy. Temperature programmed reduction results indicate that the stable temperature for SFNM samples under reduction conditions decreases with Ni content. In addition, X-ray photoelectron spectroscopy analysis suggests that the incorporation of Ni affects the conductivity of SFNM through changing the ratios of Fe³⁺/Fe²⁺ and Mo⁶⁺/Mo⁵⁺. Sr₂Fe_1.4Ni_0.1Mo_0.5O_6-δ shows the highest electrical conductivity of 20.6 S cm^-1 at 800 °C in H₂. The performance of this anode was further tested with electrolyte-supported cells, giving 380 mW cm^-2 at 750 °C in H₂, hence demonstrating that Ni doping in the B-site is beneficial for Sr₂Fe_1.5Mo_0.5O_6-δ anode performance.