59 resultados para Nano-cristaux
Resumo:
Ag/gamma-Al2O3 catalysts have been characterized in-depth during different thermo-chemical treatments by in situ diffuse reflectance UV-visible spectroscopy and quasi in situ Transmission Electron Microscopy. The combination of these techniques indicates that sintering and redispersion of silver is clearly observed from the increases and decreases in the absorption band intensity over the range of 250-600 nm due to the presence of silver clusters and silver nanoparticles. These results allow us to study the effect of the reaction feed on the metal dispersion at different operation conditions and discuss the formation of active sites during the selective catalytic reduction of O-2 with excess H-2 in the presence of unsaturated hydrocarbons. In this case high catalytic activity and selectivity toward the oxygen removal was achieved for this catalyst. (C) 2010 Elsevier B.V. All rights reserved.
Resumo:
Organic aerogels were synthesized by sol–gel polymerization of resorcinol (R) with formaldehyde (F) catalyzed by sodium carbonate (C) followed by vacuum drying. The influence of the resorcinol/sodium carbonate ratio (R/C) on the porous structure of the resultant aerogels was investigated. The nitrogen adsorption–desorption measurements show that the aerogels possess a well developed porous structure and mesoporosity was found to increase with increasing the R/C ratio. Carbon aerogels were obtained by carbonization of RF aerogels. The carbonization temperature impacts the microstructure of the aerogels by pore transformations during carbonization probably due to the formation of micropores and shrinkage of the gel structure. The results showed that a temperature of 1073 Kis more effective in the development of the pore structure of the gel. Activated carbon aerogels were obtained from the CO2 activation of carbon aerogels. Activation results in an increase in the number of both micropores and mesopores, indicative of pore creation in the structure of the carbon. Activation at higher temperatures results in a higher degree of burn off and increases the pore volume and the surface area remarkably without change of the basic porous structure, pore size, and pore size distribution.
Resumo:
Two stable nanofluids comprising of mixed valent copper(I,II) oxide clusters (<1 nm) suspended in 1-butyl-3-methylimidazolium acetate, [C(4)mim][OAc], and copper(II) oxide nanoparticles (<50 nm) suspended in trioctyl(dodecyl) phosphonium acetate, [P-88812][OAc], were synthesised in a facile one-pot reaction from solutions of copper(II) acetate hydrate in the corresponding ionic liquids. Formation of the nanostructures was studied using 13C NMR spectroscopy and differential scanning calorimetry (DSC). From a solution of Cu(OAc)2 in 1-ethyl-3-methylimidazolium acetate, [C2mim][OAc], crystals were obtained that revealed the structure of [C2mim][Cu3(OAc)5(OH)2(H2O)]center dot H2O, indicating the formation of copper hydroxo-clusters in the course of the reaction. Synthesised nanostructures were studied using transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). Physical properties of the prepared IL-nanofluids were examined using IR and UV-VIS spectroscopy, thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and densitometry.
Resumo:
This study has demonstrated biorefining steps for ryegrass and silage at a pilot scale to extrude fibre cake for the production of nanofibrillated cellulose (NFC), a potentially green biomaterial for replacing conventional fillers in the manufacture of polymer composites. Further treatments of processed ryegrass fibres with mechanical shearing, microfluidising, hydrochloric acid (HCl)/ sulphuric acid and a four stage {ethylenediaminetetra-acetic acid, sodium hydroxide, sodium hypochlorite and HCl} hydrolysis yielded 43.8, 36.1, 25.6 and 39.8 kg t21 DM of NFCs respectively. The NFCs were characterised using microscopy, X-ray diffraction, dynamic light scattering, spectroscopy and thermogravimetry. The NFC had diameters from 3.0–9.1 nm and length 308 nm– 4.6 mm. NFC-polyvinyl alcohol composites containing NFC (5 wt%) exhibited enhanced Young’s modulus and thermal stability by factors of 2.5 and 2 respectively compared with control. The mass, energy, water and chemical balances of the four process steps were assessed to evaluate technical feasibility and also to provide baseline production data for scaling up. The microfluidised product has been identified as the best NFC product, but production cost needs to be reduced.
Resumo:
The ability of millimetre wave and terahertz systems to penetrate clothing is well known. The fact that the transmission of clothing and the reflectivity of the body vary as a function of frequency is less so. Several instruments have now been developed to exploit this capability. The choice of operating frequency, however, has often been associated with the maturity and the cost of the enabling technology rather than a sound systems engineering approach. Top level user and systems requirements have been derived to inform the development of design concepts. Emerging micro and nano technology concepts have been reviewed and we have demonstrated how these can be evaluated against these requirements by simulation using OpenFx. Openfx is an open source suite of 3D tools for modeling, animation and visualization which has been modified for use at millimeter waves. © 2012 SPIE.