106 resultados para Cerium alloys
Resumo:
Thermochemical surface gas nitriding of ß21s, Timetal 205 and a Ti–Al alloy was conducted using differential scanning calorimeter equipment, in nominally pure nitrogen at 850 °C and 950 °C (ß21s), 730 °C and 830 °C (Timetal 205), and 950 °C and 1050 °C (Ti–Al) for 1 h, 3 h and 5 h. X-ray diffraction analyses showed new phases formed in the nitrided layer, depending on the alloy and the time and the temperature of nitriding. Microstructures were analyzed using optical microscopy. Cross-sectional microhardness profiles of cross-sectional samples after nitriding were obtained using a Knoop indenter.
Resumo:
Ceria (CeO2) is a technologically important rare earth material because of its unique properties and various engineering and biological applications. A facile and rapid method has been developed to prepare ceria nanoparticles using microwave with the average size 7 nm in the presence of a set of ionic liquids based on the bis (trifluoromethylsulfonyl) imide anion and different cations of 1-alkyl-3-methyl-imidazolium. The structural features and optical properties of the nanoparticles were determined in depth with X-ray powder diffraction, transmission electron microscope, N-2 adsorption-desorption technique, dynamic light scattering (DLS) analysis, FTIR spectroscopy, Raman spectroscopy, UV-vis absorption spectroscopy, and Diffuse reflectance spectroscopy. The energy band gap measurements of nanoparticles of ceria have been carried out by UV-visible absorption spectroscopy and diffuse reflectance spectroscopy. The surface charge properties of colloidal ceria dispersions in ethylene glycol have been also studied. To the best of our knowledge, this is the first report on using this type of ionic liquids in ceria nanoparticle synthesis. (C) 2011 Elsevier Inc. All rights reserved.
Resumo:
The activity of a 5-wt% Cu/CeO2-x catalyst during preferential CO oxidation in hydrogen-rich gas mixtures was studied in a microchannel reactor. The CO concentration dropped from 1 vol.% to 10 ppm at a selectivity of 60%, at a temperature of 190 degrees C, and a weight hour space velocity (WHSV) of 55,000 cm(3) g(-1) h(-1). Both the CO concentration and the temperature increased when the WHSV was increased from 50,000 to 500,000 cm(3) g(-1) h(-1). An increase of the O-2 concentration from a 1.2 to 3 fold excess reduced the CO concentration to 10 ppm in a broad temperature interval of 50 degrees C at WHSVs up to 275,000 cm(3) g(-1) h(-1). The preferential CO oxidation could be carried out at higher flow rates and at higher selectivities in the microchannel reactor compared to a fixed-bed flow reactor. (C) 2008 Elsevier B.V. All rights reserved.