Fabrication and evaluation of NiO/Y2O3-stabilized-ZrO2 hollow fibers for anode-supported micro-tubular solid oxide fuel cells

In this work NiO/3mol% Y₂O₃-ZrO₂ (3YSZ) and NiO/8mol% Y₂O₃-ZrO₂ (8YSZ) hollow fibers were prepared by phase-inversion. The effect of different kinds of YSZ (3YSZ and 8YSZ) on the porosity, electrical conductivity, shrinkage and flexural strength of the hollow fibers were systematically evaluated. When compared with Ni-8YSZ the porosity and shrinkage of Ni-3YSZ hollow fibers increases while the electrical conductivity decreases, while at the same time also exhibiting enhanced flexural strength. Single cells with Ni-3YSZ and Ni-8YSZ hollow fibers as the supported anode were successfully fabricated showing maximum power densities of 0.53 and 0.67Wcm^-2 at 800°C, respectively. Furthermore, in order to improve the cell performance, a Ni-8YSZ anode functional layer was added between the electrolyte and Ni-YSZ hollow fiber. Here enhanced peak power densities of 0.79 and 0.73Wcm^-2 were achieved at 800°C for single cells with Ni-3YSZ and Ni-8YSZ hollow fibers, respectively.

High performance cobalt-free Cu1.4Mn1.6O4 spinel oxide as an intermediate temperature solid oxide fuel cell cathode

In this work Cu_1.4Mn_1.6O₄ (CMO) spinel oxide is prepared and evaluated as a novel cobalt-free cathode for intermediate temperature solid oxide fuel cells (IT-SOFCs). Single phase CMO powder with cubic structure is identified using XRD. XPS results confirm that mixed Cu⁺/Cu²⁺ and Mn³⁺/Mn⁴⁺ couples exist in the CMO sample, and a maximum conductivity of 78 S cm⁻¹ is achieved at 800 °C. Meanwhile, CMO oxide shows good thermal and chemical compatibility with a 10 mol% Sc₂O₃ stabilized ZrO₂ (ScSZ) electrolyte material. Impedance spectroscopy measurements reveals that CMO exhibits a low polarization resistance of 0.143 Ω cm² at 800 °C. Furthermore, a Ni-ScSZ/ScSZ/CMO single cell demonstrates a maximum power density of 1076 mW cm⁻² at 800 °C under H₂ (3% H₂O) as the fuel and ambient air as the oxidant. These results indicate that Cu_1.4Mn_1.6O₄ is a superior and promising cathode material for IT-SOFCs.

Preparation and characterization of Pr0.6Sr0.4FeO3-δ-Ce0.9Pr0.1O2-δ nanofiber structured composite cathode for IT-SOFCs

In this work, Pr_0.6Sr_0.4FeO_3-δ -Ce_0.9Pr_0.1O_2-δ (PSFO-CPO) nanofibers were synthesized by a one-step electrospin technique for use in intermediate-temperature solid oxide fuel cell (IT-SOFC) applications. PSFO-CPO nanofibers were produced with a diameter of about 100nm and lengths exceeding tens of microns. The thermal expansion coefficient (TEC) matches with standard GDC electrolytes and the resulting conductivity also satisfies the needs of IT-SOFCs cathodes. EIS analysis of the nanofiber structured electrode gives a polarization resistance of 0.072Ωcm² at 800°C, smaller than that from the powdered cathode with the same composition. The excellent electrochemical performance can be attributed to the well-constructed microstructure of the nanofiber structured cathode, which promotes surface oxygen diffusion and charge transfer processes. All the results imply that the one-step electrospin method is a facile and practical way of improving the cathode properties and that PSFO-CPO is a promising cathode material for IT-SOFCs.

Facile synthesis of copper-manganese spinel anodes with high capacity and cycling performance for lithium-ion batteries

Copper-manganese spinel containing anodes were synthesized by a facile sol-gel method and evaluated in lithium-ion battery applications for the first time. The synergistic effects between copper-manganese and the aqueous binder (sodium carboxymethyl cellulose) provided a high specific capacity and excellent cycling performance. It was found that the specific capacity of the copper-manganese spinel remained at 608 mAh g⁻¹ after 100 cycles at a current density of 200 mA g⁻¹. Furthermore, a relatively high reversible capacity of 278 mAh g⁻¹ could be obtained at a current density of 2000 mA g⁻¹, indicating a good rate capability. These studies suggest that copper-manganese spinel is a promising material for lithium-ion battery applications due to a combination of good electrochemical performance and low cost.

An effective three-dimensional ordered mesoporous CuCo2O4 as electrocatalyst for Li-O2 batteries

Three-dimensional ordered mesoporous (3DOM) CuCo₂O₄ materials have been synthesized via a hard template and used as bifunctional electrocatalysts for rechargeable Li-O₂ batteries. The characterization of the catalyst by X-ray diffractometry and transmission electron microscopy confirms the formation of a single-phase, 3-dimensional, ordered mesoporous CuCo₂O₄ structure. The as-prepared CuCo₂O₄ nanoparticles possess a high specific surface area of 97.1 m² g^{- 1} and a spinel crystalline structure. Cyclic voltammetry demonstrates that mesoporous CuCo₂O₄ catalyst enhances the kinetics for either oxygen reduction reaction (ORR) or oxygen evolution reaction (OER). The Li-O₂ battery utilizing 3DOM CuCo₂O₄ shows a higher specific capacity of 7456 mAh g^{- 1} than that with pure Ketjen black (KB). Moreover, the CuCo₂O₄-based electrode enables much enhanced cyclability with a 610 mV smaller discharge-recharge voltage gap than that of the carbon-only cathode at a current rate of 100 mA g^{- 1}. Such excellent catalytic performance of CuCo₂O₄ could be associated with its larger surface area and 3D ordered mesoporous structure. The excellent electrochemical performances coupled with its facile and cost-effective way will render the 3D mesoporous CuCo₂O₄ nanostructures as attractive electrode materials for promising application in Li-O₂ batteries.

Fabrication and characterization of SSZ tape cast electrolyte-supported solid oxide fuel cells

A 10 mol%Sc₂O₃, 1 mol%CeO₂ stabilized-ZrO₂ (SSZ) powder was successfully prepared using the sol-gel method. Subsequent SSZ electrolyte pellets were prepared by tape casting technique and sintered at 1400 °C, 1450 °C, 1500 °C, 1550 °C and 1600 °C. These were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical impedance spectroscopy (EIS). SSZ showed a pure cubic phase after sintering, the grain size of SSZ increased with the increase of sintering temperature. The SSZ sintered at 1550 °C showed the highest ion conductivity. The maximum power densities of Ni-SSZ/SSZ/La_0.8Sr_0.2MnO_3-δ (LSM)-SSZ single cells sintered at 1550 °C were 0.18, 0.36, 0.51 and 0.72 W cm^-2 at 650, 700, 750 and 800 °C, respectively. The polarization resistance (R_p) of the single cell attained 0.201 Ω cm² at 800 °C.

Improved electrochemical performance of Sr2Fe1.5Mo0.4Nb0.1O6-δ -Sm0.2Ce0.8O2-δ composite cathodes by a one-pot method for intermediate temperature solid oxide fuel cells

In this paper, Sr₂Fe_1.5Mo_0.4Nb_0.1O_6-δ (SFMNb)-xSm_0.2Ce_0.8O_2-δ (SDC) (x = 0, 20, 30, 40, 50 wt%) composite cathode materials were synthesized by a one-pot combustion method to improve the electrochemical performance of SFMNb cathode for intermediate temperature solid oxide fuel cells (IT-SOFCs). The fabrication of composite cathodes by adding SDC to SFMNb is conducive to providing extended electrochemical reaction zones for oxygen reduction reactions (ORR). X-ray diffraction (XRD) demonstrates that SFMNb is chemically compatible with SDC electrolytes at temperature up to 1100 °C. Scanning electron microscope (SEM) indicates that the SFMNb-SDC composite cathodes have a porous network nanostructure as well as the single phase SFMNb. The conductivity and thermal expansion coefficient of the composite cathodes decrease with the increased content of SDC, while the electrochemical impedance spectra (EIS) exhibits that SFMNb-40SDC composite cathode has optimal electrochemical performance with low polarization resistance (R_p) on the La_0.9Sr_0.1Ga_0.8Mg_0.2O₃ electrolyte. The R_p of the SFMNb-40SDC composite cathode is about 0.047 Ω cm² at 800 °C in air. A single cell with SFMNb-40SDC cathode also displays favorable discharge performance, whose maximum power density is 1.22 W cm^-2 at 800 °C. All results indicate that SFMNb-40SDC composite material is a promising cathode candidate for IT-SOFCs.

Synthesis of Pr0.6Sr0.4FeO 3-δ -xCe0.9Pr0.1O 2-δ cobalt-free composite cathodes by a one-pot method for intermediate-temperature solid oxide fuel cells

Cobalt-free composite cathodes consisting of Pr_0.6Sr_0.4FeO _3-δ -xCe_0.9Pr_0.1O _2-δ (PSFO-xCPO, x = 0-50 wt%) have been synthesized using a one-pot method. X-ray diffraction, scanning electron microscopy, thermal expansion coefficient, conductivity, and polarization resistance (R _P ) have been used to characterize the PSFO-xCPO cathodes. Furthermore the discharge performance of the Ni-SSZ/SSZ/GDC/PSFO-xCPO cells has been measured. The experimental results indicate that the PSFO-xCPO composite materials fully consist of PSFO and CPO phases and posses a porous microstructure. The conductivity of PSFO-xCPO decreases with the increase of CPO content, but R _P of PSFO-40CPO shows the smallest value amongst all the samples. The power density of single cells with a PSFO-40CPO composite cathode is significantly improved compared with that of the PSFO cathode, exhibiting 0.43, 0.75, 1.08 and 1.30 W cm^-2 at 650, 700, 750 and 800 °C, respectively. In addition, single cells with the PSFO-40CPO composite cathode show a stable performance with no obvious degradation over 100 h when operating at 750 °C.