Kinetics of the photocatalysed oxidation of NO in the ISO 22197 reactor

The photocatalytic reactor described in the NOx removal ISO 22197-1:2007 is used to study the kinetics of the process, using a film of P25 TiO2 which has either been conventionally pre-irradiated in a stream of air, or unconventionally in a stream of NO (1 ppmv). In the former case it is shown that the system does not achieve steady state exit levels of NO, probably due to the gradual accumulation of HNO3 on the surface of the photocatalyst. The NO-preconditioned TiO2 film demonstrated excellent steady-state levels when monitored as a function of NO concentration, [NO] and UV irradiance, ρ. However, in this case the photocatalytic reaction under study is NOT NOx removal, but the conversion of NO to NO2. It is shown that the kinetics of this steady state process fit very well to a kinetic expression based on a disrupted adsorption reaction mechanism, which has also been used by others to fit their observed (non-steady state) kinetics for NOx removal on conventionally-(air) preconditioned films of P25. The appropriateness of this model for either system is questioned, since in both systems the kinetics appear to have a significant mass transport element. These findings suggest that mass transport and non-steady-state kinetics are likely to be significant features for most active photocatalytic samples, where the %NO conversion is >7%, and so limits the usefulness of the NOx removal ISO 22197-1:2007.

Corrosion Fatigue Behaviour of Laser-welded Shape Memory NiTi Wires in a Simulated Body Fluid

Corrosion fatigue is a fracture process as a consequence of synergistic interactions between the material structure, corrosive environment and cyclic loads/strains. It is difficult to be detected and can cause unexpected failure of engineering components in use. This study reveals a comparison of corrosion fatigue behaviour of laser-welded and bare NiTi wires using bending rotation fatigue (BRF) test coupled with a specifically-designed corrosion cell. The testing medium was Hanks’ solution (simulated body fluid) at 37.5 oC. Electrochemical impedance spectroscopic (EIS) measurement was carried out to monitor the change of corrosion resistance of sample during the BRF test at different periods of time. Experiments indicate that the laser-welded NiTi wire would be more susceptible to the corrosion fatigue attack than the bare NiTi wire. This study can serve as a benchmark for the product designers and engineers to understand the corrosion fatigue behaviour of the NiTi laser weld joint and determine the fatigue life safety factor for NiTi medical devices/implants involving laser welding in the fabrication process.