Effect of fretting on fatigue performance of Ti-1023 titanium alloy

The plain fatigue and fretting fatigue tests of Ti-1023 titanium alloy were performed using a high-frequency push-pull fatigue testing machine. Both σmax versus number of cycles to failure curves were obtained for comparative analysis of the fretting effect on fatigue performance of the titanium alloy. Meanwhile, by analyzing the fracture of plain fatigue and fretting fatigue, the fretting scar and the fretting debris observed by scanning electron microscopy (SEM), the mechanism of fretting fatigue failure of Ti-1023 titanium alloy is discussed. The fretting fatigue strength of Ti-1023 titanium alloy is 175 MPa under 10 MPa contact pressure, which is 21% of plain fatigue strength (836 MPa). Under fretting condition, the Ti-1023 titanium alloy fatigue fracture failure occurs in a shorter fatigue life. When it comes to σmax versus number of cycles to failure curves, data points in the range of 106–107 cycles under plain fatigue condition moved to the range of 105–106 under fretting fatigue condition. The integrity of the fatigue specimen surface was seriously damaged under the effect of fretting. With the alternating stress loaded on specimen, the stress concentrated on the surface of fretting area, which brought earlier the initiation and propagation of crack.

Microstructure evolution in CLAM steel under low cycle fatigue

In the process of room-temperature low cycle fatigue, the China Low Activation Martensitic steel exhibits at the beginning cyclic hardening and then continuous cyclic softening. The grain size decreased and the martensitic lath transformed to cells/subgrains after the tests. The subgrains increase in size with increasing strain amplitude.

Low cycle fatigue properties of CLAM steel at 823 K

China Low Activation Martensitic (CLAM) steel is considered to be the main candidate material for the first wall components of future fusion reactors in China. In this paper, the low cycle fatigue (LCF) behavior of CLAM steel is studied under fully reversed tension–compression loading at 823 K in air. Total strain amplitude was controlled from 0.14% to 1.8% with a constant strain rate of 2.4×10−3 s−1. The corresponding plastic strain amplitude ranged from 0.023% to 1.613%. The CLAM steel displayed continuous softening to failure at 823 K. The relationship between strain, stress and fatigue life was obtained using the parameters obtained from fatigue tests. The LCF properties of CLAM steel at 823 K followed Coffin–Manson relationship. Furthermore, irregular serration was observed on the stress–strain hysteresis loops of CLAM steel tested with the total strain amplitude of 0.45–1.8%, which was attributed to the dynamic strain aging (DSA) effect. During continuous cyclic deformation, the microstructure and precipitate distribution of CLAM steel changed gradually. Many tempered martensitic laths were decomposed into subgrains, and the size and number of M23C6 carbide and MX carbonitride precipitates decreased with the increase of total strain amplitude. The response cyclic stress promoted the recovery of martensitic lath, while the thermal activation mainly played an important role on the growth of precipitates in CLAM steel at 823 K. In order to have a better understanding of high-temperature LCF behavior, the potential mechanisms controlling stress–strain response, DSA phenomenon and microstructure changes have also been evaluated.

A study to evaluate the introduction of simulation as a teaching strategy for the mental health and learning disability fields of nursing, in an undergraduate nursing curriculum within one higher education institution

High Fidelity Simulation or Human Patient Simulation is an educational strategy embedded within nursing curricula throughout many healthcare educational institutions. This paper reports on an evaluative study that investigated the views of a group of Year 2 undergraduate nursing students from the mental health and the learning disability fields of nursing (n = 75) in relation to simulation as a teaching pedagogy. The study took place in the simulation suite within a School of Nursing and Midwifery in the UK. Two patient scenarios were used for the session and participants completed a 22-item questionnaire consisting of three biographical information questions and a 19-item Likert scale. Descriptive statistics were employed to illustrate the data and non-parametric testing (Mann-Whitney U test) was employed to test a number of hypotheses. Overall students were positive about the introduction of patient scenarios using the human patient simulator into the undergraduate nursing curriculum. This study used a small, convenience sample in one institution and therefore the results obtained cannot be generalised to nursing education before further research can be conducted with larger samples and a mixed-method research approach. However these results provide encouraging evidence to support the use of simulation within the mental health and the learning disability fields of nursing, and the development and implementation of further simulations to complement the students’ practicum.

Does vicarious traumatisation affect oncology nurses?:A literature review

It is widely documented that nurses experience work-related stress [Quine, L., 1998. Effects of stress in an NHS trust: a study. Nursing Standard 13 (3), 36-41; Charnley, E., 1999. Occupational stress in the newly qualified staff nurse. Nursing Standard 13 (29), 32-37; McGrath, A., Reid, N., Boore, J., 2003. Occupational stress in nursing. International Journal of Nursing Studies 40, 555-565; McVicar, A., 2003. Workplace stress in nursing: a literature review. Journal of Advanced Nursing 44 (6), 633-642; Bruneau, B., Ellison, G., 2004. Palliative care stress in a UK community hospital: evaluation of a stress-reduction programme. International Journal of Palliative Nursing 10 (6), 296-304; Jenkins, R., Elliott, P., 2004. Stressors, burnout and social support: nurses in acute mental health settings. Journal of Advanced Nursing 48 (6), 622-631], with cancer nursing being identified as a particularly stressful occupation [Hinds, P.S., Sanders, C.B., Srivastava, D.K., Hickey, S., Jayawardene, D., Milligan, M., Olsen, M.S., Puckett, P., Quargnenti, A., Randall, E.A., Tyc, V., 1998. Testing the stress-response sequence model in paediatric oncology nursing. Journal of Advanced Nursing 28 (5), 1146-1157; Barnard, D., Street, A., Love, A.W., 2006. Relationships between stressors, work supports and burnout among cancer nurses. Cancer Nursing 29 (4), 338-345]. Terminologies used to capture this stress are burnout [Pines, A.M., and Aronson, E., 1988. Career Burnout: Causes and Cures. Free Press, New York], compassion stress [Figley, C.R., 1995. Compassion Fatigue. Brunner/Mazel, New York], emotional contagion [Miller, K.I., Stiff, J.B., Ellis, B.H., 1988. Communication and empathy as precursors to burnout among human service workers. Communication Monographs 55 (9), 336-341] or simply the cost of caring (Figley, 1995). However, in the mental health field such as psychology and counselling, there is terminology used to captivate this impact, vicarious traumatisation. Vicarious traumatisation is a process through which the therapist's inner experience is negatively transformed through empathic engagement with client's traumatic material [Pearlman, L.A., Saakvitne, K.W., 1995a. Treating therapists with vicarious traumatization and secondary traumatic stress disorders. In: Figley, C.R. (Ed.), Compassion Fatigue: Coping with Secondary Traumatic Stress Disorder in Those Who Treat the Traumatized. Brunner/Mazel, New York, pp. 150-177]. Trauma not only affects individuals who are primarily present, but also those with whom they discuss their experience. If an individual has been traumatised as a result of a cancer diagnosis and shares this impact with oncology nurses, there could be a risk of vicarious traumatisation in this population. However, although Thompson [2003. Vicarious traumatisation: do we adequately support traumatised staff? The Journal of Cognitive Rehabilitation 24-25] suggests that vicarious traumatisation is a broad term used for workers from any profession, it has not yet been empirically determined if oncology nurses experience vicarious traumatisation. This purpose of this paper is to introduce the concept of vicarious traumatisation and argue that it should be explored in oncology nursing. The review will highlight that empirical research in vicarious traumatisation is largely limited to the mental health professions, with a strong recommendation for the need to empirically determine whether this concept exists in oncology nursing.

Up close and personal: A qualitative study exploring the lived experience of older carers. Mental Health and Learning Disabilities Research. 8 (1). Pp.15-29.

This study explored the experiences of informal carers who were aged 65 years and over. It has been estimated that 15 per cent of those aged 65 or over provide some form of informal care in England. Despite a growing literature on the involvement of older people in research, there is a paucity of literature on the involvement of older carers. In this study, older carers were identified via a General Practice (GP) register in one urban medical practice. Data was collected through a series of focus groups, which were transcribed and analysed using
thematic analysis. Every carer aged 55 or over and registered with the medical practice was invited to take part in the study. Four female carers and one male carer took part in the study (age range 65-83). Themes that emerged during data analysis included, 1) managing things in an emergency, 2) feeling valued because they took part in the research and 3) the day-to-day reality of living with social exclusion. GP registers provide a valuable tool for identifying older
carers who may otherwise be difficult to engage in research. However, persuading GPs to engage with qualitative research may be a challenge.

Cyclic nanoindentation and nano-impact fatigue characterisation of functionally graded TiN/TiNi shape memory film

This paper investigates the mechanism of nanoscale fatigue of functionally graded TiN/TiNi films using nano-impact and multiple-loading-cycle nanoindentation tests. The functionally graded films were deposited on silicon substrate, in which TiNi films maintain shape memory and pseudo elastic behavior, while a modified TiN surface layer provides tribological and anti-corrosion properties. Nanomechanical tests were performed to comprehend the localized film performance and failure modes of the functionally graded film using NanoTestTM equipped with Berkovich and conical indenter between 100 μN to 500 mN loads. The loading mechanism and load history are critical to define film failure modes (i.e. backward depth deviation) including the shape memory effect of the functionally graded layer. The results are sensitive to the applied load, loading type (e.g. semi-static, dynamic) and probe geometry. Based on indentation force-depth profiles, depth-time data and post-test surface observations of films, it is concluded that the shape of the nanoindenter is critical in inducing the localized indentation stress and film failure, including shape recovery at the lower load range. Elastic-plastic finite element (FE) simulation during nanoindentation loading indicated that the location of subsurface maximum stress near the interface influences the backward depth deviation type of film failure. A standalone, molecular dynamics simulation was performed with the help of a long range potential energy function to simulate the tensile test of TiN nanowire with two different aspect ratios to investigate the theory of its failure mechanism.

An international comparison of legal frameworks for supported and substitute decision-making in mental health services

There have been important recent developments in law, research, policy and practice relating to supporting people with decision-making impairments, in particular when a person’s wishes and preferences are unclear or inaccessible. A driver in this respect is the United Nations Convention on the Rights of Persons with Disabilities (CRPD); the implications of the CRPD for policy and professional practices are currently debated. This article reviews and compares four legal frameworks for supported and substitute decision-making for people whose decision-making ability is impaired. In particular, it explores how these frameworks may apply to people with mental health problems. The four jurisdictions are: Ontario, Canada; Victoria, Australia; England and Wales, United Kingdom (UK); and Northern Ireland, UK. Comparisons and contrasts are made in the key areas of: the legal framework for supported and substitute decision-making; the criteria for intervention; the assessment process; the safeguards; and issues in practice. Thus Ontario has developed a relatively comprehensive, progressive and influential legal framework over the past thirty years but there remain concerns about the standardisation of decision-making ability assessments and how the laws work together. In Australia, the Victorian Law Reform Commission (2012) has recommended that the six different types of substitute decision-making under the three laws in that jurisdiction, need to be simplified, and integrated into a spectrum that includes supported decision-making. In England and Wales the Mental Capacity Act 2005 has a complex interface with mental health law. In Northern Ireland it is proposed to introduce a new Mental Capacity (Health, Welfare and Finance) Bill that will provide a unified structure for all substitute decision-making. The discussion will consider the key strengths and limitations of the approaches in each jurisdiction and identify possible ways that further progress can be made in law, policy and practice.

In situ diagnostics and prognostics of solder fatigue in IGBT modules for electric vehicle drives

This paper proposes an in situ diagnostic and prognostic (D&P) technology to monitor the health condition of insulated gate bipolar transistors (IGBTs) used in EVs with a focus on the IGBTs' solder layer fatigue. IGBTs' thermal impedance and the junction temperature can be used as health indicators for through-life condition monitoring (CM) where the terminal characteristics are measured and the devices' internal temperature-sensitive parameters are employed as temperature sensors to estimate the junction temperature. An auxiliary power supply unit, which can be converted from the battery's 12-V dc supply, provides power to the in situ test circuits and CM data can be stored in the on-board data-logger for further offline analysis. The proposed method is experimentally validated on the developed test circuitry and also compared with finite-element thermoelectrical simulation. The test results from thermal cycling are also compared with acoustic microscope and thermal images. The developed circuitry is proved to be effective to detect solder fatigue while each IGBT in the converter can be examined sequentially during red-light stopping or services. The D&P circuitry can utilize existing on-board hardware and be embedded in the IGBT's gate drive unit.