基于局部损伤混凝土模型的FRP-混凝土界面有限元分析研究

A meso-scale finite element model is presented for investigating the FRP-concrete bond behaviour under static and dynamic loadings. It adopts a local concrete damage model. A large number of single shear tests under static pull-off loading were modeled. It is demonstrated that the developed model can satisfactorily simulate the static debonding behaviour, in terms of the load-carrying capacity and the local bond-slip behaviour. A preliminary study of the effect of the dynamic loading rate on the debonding behaviour was also conducted by considering a dynamic increase factor for the concrete strength as a function of strain rate. It is shown that a higher loading rate leads to a higher load-carrying capacity, a longer effective bond length, and a larger damaged area of concrete in the single shear loading scenario.

抗剪加固FRP与混凝土界面粘结性能的试验研究

In this study, 21 small beam specimens with a pre-set through-crack were tested with FRP strips bonded to the sides to study the bond behavior between shear-strengthening FRP and concrete (referred to as "the interface" for simplicity hereafter). The test parameters included the bond length, width, thickness of FRP strip and the angle between fiber orientation and crack opening direction (referred to as "fiber tensile angle" θ hereafter) on the bond behavior of the interface. Test results showed that: 1) the small beam test setup with a pre-set crack is suitable for studying the bond behavior between FRP and concrete; 2) the bond length, width, and thickness of the FRP as well as the fiber angle have significant effects on the bond strength; 3) the distribution of FRP strains along the direction perpendicular to the fiber orientation (FRP width direction) is non-uniform; this is mainly attributed to the progressive debonding of the FRP strips in the width direction, with the FRP at the location of larger crack width debonding earlier.

A technique for reducing strain concentrations in FRP wrapped concrete columns

Existing studies have shown conclusively that the measured fibre reinforced polymer (FRP) rupture strain in FRP wrapped concrete columns is usually significantly smaller than the rupture strain obtained from flat coupon tests. One of the main causes for this phenomenon is the existence of geometrical discontinuities at both ends of the FRP sheets. This study proposes a new strengthening method in which continuous FRP spiral wrapping is used to eliminate strain concentrations due to the geometrical discontinuities and thus increase the FRP rupture strain at column failure. The effect of the spiral angle of FRP on the FRP rupture strain in FRP wrapped specimens was experimentally investigated. The test results indicate that the spiral wrapping with a small angle with respect to the column circumference can significantly increase the strain efficiency of FRP and thus enhance the axial compression capacity of the strengthened cylinders.

Bond behavior of NSM FRP strips between two adjacent cracks in concrete beams: A numerical study

Strengthening RC structures with near-surface mounted (NSM) fibre reinforced polymer (FRP) composites has a number of advantages compared with that with externally bonded (EB) FRP sheets/plates. As with EB FRP, the performance of the bond between NSM FRP and concrete is one of the key factors affecting the behaviour of the strengthened structure. This paper presents a numerical investigation into the behaviour of NSM FRP loaded at its both ends to simulate the NSM FRP-toconcrete bond between two adjacent cracks in RC members. The main objective of this study is to quantitatively clarify the effect of the bondline damage during slip reversal on the ultimate load (bond strength). The results show that the bondline damage has a significant effect on the load-carrying capacity of the NSM FRP-to-concrete bonded interface and should be considered in FE modeling of the interface.

Interpretation of flat FRP coupon test results

The tensile strength obtained from existing testing methods such as ASTM D3039, based on flat coupons, usually has a large scatter for fibre reinforced polymer (FRP) composites. This means that the measured strength may not represent the actual strength of the material, leading to under or over design. This paper develops a new interpretation method which requires fewer tests, saving money and time. Moreover the results are more consistent and more closely represent the actual strength which can lead to a safer and more economical design.

Mitigation of concrete cover separation in frpstrengthened RC beams using FRP U-jackets

Concrete cover separation is a common failure mode of reinforced concrete (RC) beams strengthened with a fibre-reinforced polymer (FRP) plate bonded to the tension face (FRP-plated RC beams). Plate-end FRP U-jackets have previously been explored as a mitigation measure to delay or suppress concrete cover separation, although its effectiveness needs further clarification. The paper presents the first systemic experimental study on the use of FRP U-jackets of different forms for mitigating the concrete cover separation failure. A total of ten full-scale FRP-plated RC beams were tested. The test results show that both the ultimate load and the ductility of the beams were enhanced by the U-jackets. Among the forms of U-jackets explored, those inclined at 45o are the most effective.