The effect of H-2 and the presence of hot-O-(ads) during the decomposition of N2O on platinum

The decomposition of N2O was studied using a silica-supported Pt catalyst. The catalyst was found to exhibit short-lived activity at low temperatures to yield N-2 and O-(ads), the latter remained adsorbed on the surface and poisoned the active sites. Creation of hot-O-(ads) atoms during N2O decomposition is proposed to allow O-2 desorption at intermediate temperatures. Inclusion of H-2 as a reducing agent greatly enhanced the activity and suppressed low temperature deactivation. Simultaneous and sequential pulsing of N2O and H-2 showed that H-2 inclusion with the N2O gas stream produced the greatest activity. A mechanism involving H-(ads) addition to

Low-temperature catalytic decomposition of N2O on platinum and bismuth-modified platinum: identification of active sites

Classification of the active surface sites of platinum catalysts responsible for low temperature N2O decomposition, in terms of steps, kinks and terraces, has been achieved by controlled addition of bismuth to as-received platinum/graphite catalysts.

Epitaxial Magnetic Oxide Nanocrystals Via Phase Decomposition of Bismuth Perovskite Precursors

The phase instability of bismuth perovskite (BiMO₃), where M is a ferromagnetic cation, is exploited to create self-assembled magnetic oxide nanocrystal arrays on oxide supports. Conditions during pulsed laser deposition are tuned so as to induce complete breakdown of the perovskite precursor into bismuth oxide (Bi₂ O₃ ) and metal oxide (M-O_x ) pockets. Subsequent cooling in vacuum volatizes the Bi₂ O₃ leaving behind an array of monodisperse nanocrystals. In situ reflective high energy electron diffraction beam is exploited to monitor the synthesis in real-time. Analysis of the patterns confi rms the phase separation and volatization process. Successful synthesis of M-O_x, where M = Mn, Fe, Co, and Cr, is shown using this template-free facile approach. Detailed magnetic characterization of nanocrystals is carried out to reveal the functionalities such as magnetic anisotropy as well as larger than bulk moments, as expected in these oxide nanostructures.

DRIFTS/MS/Isotopic Labeling Study on the NO-Moderated Decomposition of a Silica-Supported Nickel Nitrate Catalyst Precursor

In the preparation of silica-supported nickel oxide from nickel nitrate impregnation and drying, the replacement of the traditional air calcination step by a thermal treatment in 1% NO/Ar prevents agglomeration, resulting in highly dispersed NiO. The mechanism by which NO prevents agglomeration was investigated by using combined in situ diffuse reflectance infrared fourier transform (DRIFT) spectroscopy and mass spectrometry (MS). After impregnation and drying, a supported nickel hydroxynitrate phase with composition Ni(3)(NO(3))(2)(OH)(4) had been formed. Comparison of the evolution of the decomposition gases during the thermal decomposition of Ni(3)(NO(3))(2)(OH)(4) in labeled and unlabeled NO and O(2) revealed that NO scavenges oxygen radicals, forming NO(2). The DRIFT spectra revealed that the surface speciation evolved differently in the presence of NO as compared with in O(2) or Ar. It is proposed that oxygen scavenging by NO depletes the Ni(3)(NO(3))(2)(OH)(4) phase of nitrate groups, creating nucleation sites for the formation of NiO, which leads to very small (similar to 4 nm) NiO particles and prevents agglomeration.

Chemisorption and decomposition of pyrrole on Pd{111}

XPS, TPD and HREEL results indicate that molecular pyrrole is a fragile adsorbate on clean Pd{111}. At 200 K and for low coverages, the molecule remains intact and adopts an almost flat-lying geometry. With increasing coverage, pyrrole molecules tilt away from the surface and undergo N-H bond cleavage to form strongly tilted pyrrolyl (C4H4N) species. In addition, a weakly bound, strongly tilted form of molecular pyrrole is observed at coverages approaching saturation. Heating pyrrole monolayers results in desorption of similar to 15% of the overlayer as molecular pyrrole and N-a+ C4H4Na recombination with formation of hat-lying pyrrole molecules. This strongly bound species undergoes decomposition to adsorbed CN, CHx and H, leading ultimately to desorption of HCN and H-2. The implications of these results for the production of pyrrole by a heterogeneously catalysed route are discussed.

The photocatalytic decomposition of microcystin-LR using selected titanium dioxide materials

Microcystins (cyclic heptapeptides) produced by a number of freshwater cyanobacteria are a potential cause for concern in potable water supplies due to their acute and chronic toxicity. TiO₂ photocatalysis is a promising technology for removal of these toxins from drinking water. It is, however, necessary to have a sufficient knowledge of how the catalyst materials cause the degradation of the toxins through the photocatalytic process. The present study reports microcystin degradation products of the photocatalytic oxidation by using a number of commercial TiO₂ powder (P25, PC50, PC500 and UV100) and granular (KO1, KO3, TiCat-C, TiCat-S) materials, so aiding the mechanistic understanding of this process. Liquid chromatography-mass spectrometry analysis demonstrated that the major destruction pathway of microcystin for all the catalysts tested followed almost the same pathway, indicating the physical properties of the catalysts had little effects on the degradation pathway of microcystin-LR.