The Relationship Between Cadwaladerite Al(OH)2Cl∙4H2O and Lesukite Al2(OH)5Cl∙2H2O as Investigated by SEM, PXRD, FTIR and Raman Spectroscopy

Cadwaladerite (Al(OH)2Cl∙4H2O) collected from Cerro Pintados, Chile described by Gordon in 1941 is designated as “doubtful” by the IMA. Material collected from the same locality in 2015 resembling the description of cadwaladerite gave a powder XRD pattern similar to lesukite (Al2(OH)5Cl∙2H2O). However, Gordon provided no X-ray data for his material from Cerro Pintados. In order to determine whether cadwaladerite and lesukite are the same mineral species, measurements were made on a suite of samples from various localities. A portion of the material collected by Gordon in 1941 was also obtained from the Mineralogical Museum of Harvard University. Type material of lesukite from a fumarolic environment at the Tolbachik Fissure in Kamchatka, Russia was obtained as well as lesukite from the Maria Mine, Chile (Arica Province) and a previously undescribed locality for lesukite (Barranaca del Sulfato, Mejillones Peninsula, Antofagasta Province). All samples are yellow to yellow-orange in colour and all exhibit small cubic crystals (up to 50µm), even Gordon’s cadwaladerite which was thought to be amorphous. The Chilean samples are all associated with halite and sometimes with anhydrite. These five samples were studied by SEM, FTIR, powder XRD, and Raman spectroscopy. A ratio of Al:Cl less than or equal to 1.3:1 was observed for all the samples, including measurements made on lesukite from the Russian locality Vergasova et al. studied in 1997, and determined to have a 2:1 ratio. SEM-EDS analyses also show all samples to have minor iron substitution, as well as copper substitution in two samples. FTIR spectra are very similar for all samples. Raman spectroscopy done on both samples collected in Cerro Pintados and the Russian lesukite gave similar spectra. Powder XRD analyses on all samples showed spectra identified to be lesukite, including Gordon’s cadwaladerite. Crystal cell parameters calculated from powder XRD ranged from 19.778Å to 19.878Å. Results using modern instrumental techniques confirm Gordon’s cadwaladerite, collected in 1939 and described in 1941, and lesukite are the same mineral species.

BLOCK COPOLYMERS CONTAINING A LOW-SURFACE-ENERGY BLOCK AND THEIR APPLICATIONS

This thesis reports the synthesis and/or applications of three types of block copolymers that each bear a low-surface-energy block. First, poly(dimethylsiloxane)-block-poly(2-cinnamoyloxyethyl acrylate) (PDMS-b-PCEA) was synthesized and characterized. Cotton coating using a micellar solution of this block copolymer yielded superhydrophobic cotton fabrics. X-ray photoelectron spectroscopy (XPS) and surface property analyses indicated that the PDMS block topped the polymer coating. Photocuring the cotton swatches crosslinked the underlying PCEA layer and yielded permanent coatings. More interestingly, hydrophilically patterned superhydrophobic cotton fabrics were produced using photolithography that allowed the crosslinking of the coating around irradiated fibers but the removal, by solvent extraction, of the coating on fibers that were not irradiated. Since water-based ink only permeated the uncoated regions, such patterned fabric was further used to print ink patterns onto substrates such as fabrics, cardboard, paper, wood, and aluminum foil. Then, another PDMS-based diblock copolymer poly(dimethylsiloxane)-block-poly(glycidyl methacrylate) (PDMS-b-PGMA) was prepared. Different from PCEA that photocrosslinked around cotton fibers, PGMA reacted with hydroxyl groups on cotton fiber surfaces to get covalently attached. Further, different PGMA chains crosslinked with each other. PDMS-b-PGMA-coated cotton fabrics have been used for oil-water separations. In addition, polymeric nanoparticles were grafted onto cotton fiber surface before PDMS-b-PGMA was used to cover the surfaces of the grafted spheres and the residual surfaces of the cotton fibers. These two types of fabrics, coated by the block copolymer alone or by the polymer nanospheres and then the copolymer, were characterized by scanning electron microscope (SEM), Fourier transform infrared spectroscopy (FT-IR), and water repellency analyses. A comprehensive comparative study was made of their performances in oil-water separation. Finally, a fluorinated ABC triblock copolymer poly(acrylic acid)-block-poly(2-cinnamoyloxyethyl methacrylate)-block-poly(2-perfluorooctylethyl methacrylate) (PAA-b-PCEMA-b-PFOEMA) was used to iii encapsulate air nanobubbles. The produced air nanobubbles were thermodynamically stable in water and were some 100 times more stable than commercially available perfluorocarbon-filled microbubbles under ultrasound. These nanobubbles, due to their small sizes and thus ability to permeate the capillary networks of organs and to reach tumors, may expand the applications of microbubbles in diagnostic ultrasonography and find new applications in ultrasound-regulated drug delivery.