Physical and Chemical Performance Testing of Ontario Asphalt Pavements

Thermal and fatigue cracking are the two of the major pavement distress phenomena that contribute significantly towards increased premature pavement failures in Ontario. This in turn puts a massive burden on the provincial budgets as the government spends huge sums of money on the repair and rehabilitation of roads every year. Governments therefore need to rethink and re-evaluate their current measures in order to prevent it in future. The main objectives of this study include: the investigation of fatigue distress of 11 contract samples at 10oC, 15oC, 20oC and 25oC and the use of crack-tip-opening-displacement (CTOD) requirements at temperatures other than 15oC; investigation of thermal and fatigue distress of the comparative analysis of 8 Ministry of Transportation (MTO) recovered and straight asphalt samples through double-edge-notched-tension test (DENT) and extended bending beam rheometry (EBBR); chemical testing of all samples though X-ray Fluorescence (XRF) and Fourier transform infrared analysis (FTIR); Dynamic Shear Rheometer (DSR) higher and intermediate temperature grading; and the case study of a local Kingston road. Majority of 11 contract samples showed satisfactory performance at all temperatures except one sample. Study of CTOD at various temperatures found a strong correlation between the two variables. All recovered samples showed poor performance in terms of their ability to resist thermal and fatigue distress relative to their corresponding straight asphalt as evident in DENT test and EBBR results. XRF and FTIR testing of all samples showed the addition of waste engine oil (WEO) to be the root cause of pavement failures. DSR high temperature grading showed superior performance of recovered binders relative to straight asphalt. The local Kingston road showed extensive signs of damage due to thermal and fatigue distress as evident from DENT test, EBBR results and pictures taken in the field. In the light of these facts, the use of waste engine oil and recycled asphalt in pavements should be avoided as these have been shown to cause premature failure in pavements. The DENT test existing CTOD requirements should be implemented at other temperatures in order to prevent the occurrences of premature pavement failures in future.

Performance and Assessment of Rehabilitated Steel Culverts

This thesis explores the effects of rehabilitation on the structural performance of corrugated steel culverts. A full-scale laboratory experiment investigated the effects of grouted slip-liners on the performance of two buried circular corrugated steel culverts. One culvert was slip-lined and grouted using low strength grout, while the other was slip-lined and grouted using high strength grout. The performances of the culverts were measured before and after rehabilitation under service loads using single wheel pair loading at 0.45m of cover. Then, the rehabilitated culverts were loaded to their ultimate limit states. Results showed that the low and high strength grouted slip-liners provided strength well beyond requirements, with the low strength specimen failing at a load 2.4 times the fully factored service load, while the high strength specimen did not reach an ultimate limit state before bearing failure of the soil stopped testing. Results also showed that the low strength specimen behaved rigidly under service loads and flexibly under higher loads, while the high strength specimen behaved rigidly under all loads. A second full-scale experiment investigated the effect of a paved invert rehabilitation procedure on the performance of a deteriorated horizontal ellipse culvert. The performance of the culvert before and after rehabilitation was examined under service loads using tandem axle loading at 0.45m of cover. The rehabilitated culvert was then loaded up to its ultimate limit state. The culvert failed due to the formation of a plastic hinge at the West shoulder, while the paved invert cracked at the invert. Results showed that the rehabilitation increased the structural performance of the culvert, increasing the system stiffness and reducing average strains and local bending at critical locations in the culvert under service loads. A sustainability rating tool specifically for the evaluation of deteriorated culvert replacement or rehabilitation projects was also developed. A module for an existing tool, called GoldSET, was created and tested using two case studies, each comparing the replacement of a culvert using a traditional open-cut method with two trenchless rehabilitation techniques. In each case, the analyses showed that the trenchless techniques were the better alternatives in terms of sustainability.