THE DESIGN AND SYNTHESIS OF SILOXANE PRECURSORS FOR CHIRAL PERIODIC MESOPOROUS ORGANOSILICA MATERIALS

The development of cost-effective and reliable methods for the synthesis and separation of asymmetric compounds is paramount in helping to meet society’s ever-growing demand for chiral small molecules. Of these methods, chiral heterogeneous supports are particularly appealing as they allow for the reuse of the chiral source. One such support, based on the synergy between chiral organic units and structurally stable inorganic silicon scaffolds are periodic mesoporous organosilicas (PMOs). In the work described herein, I examine some of the factors governing the transmission of chirality between chiral dopants and prochiral bulk phases in chiral PMO materials. In particular, the exploration of 1,1’-binaphthalene-bridged chiral dopants with a focus on the point of attachment into the materials. Moreover, the effects of ordering in the materials are examined and reveal that chirality transfer is more facile in materials with molecular-scale order then those containing amorphous walls. Secondly, the issues surrounding the synthesis and purification of aryl-triethoxysilanes as siloxane precursors are addressed. Both the introduction of a two-carbon linker and the direct attachment of allyl and mixed allyldiethoxysilane species are explored. This work demonstrates that allyldiethoxysilanes are ideal, in that they are stable enough to permit facile synthesis, while still being able to hydrolyze completely to produce well-ordered materials. Lastly, the production of new bulk phases for chiral PMO materials is examined by introducing new prochiral nitrogen-containing siloxane precursors. Biphenyldiamine and bipyridine-bridged siloxane precursors are readily synthesized on reasonable scales. Their use as the bulk siloxane precursor in the production of PMO materials however, is precluded by insufficient gelation and additional siloxane precursors are necessary for the production of ordered materials. In addition to the research detailed above that forms the body of this thesis, two short works are appended. The first details the production of polythiophene assemblies mediated through coordination nanospaces, while the second explores the production of N-heterocyclic carbene functionalized gold nanoparticles through ligand exchange.

MEDIUM-CHAIN-LENGTH POLY(3-HYDROXYALKANOATE) NANOPARTICLE SUSPENSIONS

The main goal of this thesis was to prepare medium-chain-length poly-3-hydroxyalkanoate (mcl-PHA) nanoparticle suspensions at high solids content (≥ 10 % w/v). A two-stage emulsification-solvent evaporation process was employed to produce poly-3-hydroxydecanoate (PHD) suspensions. The formulation and processing conditions including ultrasonication time and amplitude, selection of solvent, and selection of surfactants and their concentrations were investigated to make concentrated suspensions (10 and 30 % (w/v)) of PHD with particles less than 300 nm. Among the ionic surfactants tested to stabilize the suspension, the anionic, sodium dodecyl sulphate (SDS), and the cationic, dodecyltrimethylammonium bromide (DTAB) surfactants produced the smallest particle sizes (~100 nm). However, more stabilized nanoparticles were obtained when the ionic surfactant, SDS, was combined with any of the non-ionic surfactants tested, with polyoxyethylene octyl phenyl ether (Triton X-100) or polyoxyethylene (20) sorbitan monooleate (Tween 80) resulting in a slight increase in zeta potential over 30 days while the zeta potential with other non-ionic surfactants decreased. Mcl-PHA containing 11 and 18 % of carboxyl groups was synthesized via free radical addition reaction of 11-mercaptoundecanoic acid to the pendant double bonds of unsaturated poly-3-hydroxynonanoate (PHNU). Colloidal suspensions prepared by ultrasonication needed a surfactant to maintain stability, even at 0.4 % solids of mcl-PHA containing 11 % carboxylation (PHNC-1) unlike the stable suspensions prepared without surfactants by the titration method. Similar particle sizes (155.6 ± 8.4 to 163.4 ± 11.3 nm) and polydispersity indices (0.42 ± 0.03 to 0.49 ± 0.04) were obtained when several non-ionic surfactants were tested to minimize particle agglomeration, with the smallest particles obtained with Triton X-100. When Triton X-100 was combined with a variety of ionic surfactants, smaller nanoparticles (97.1 ± 1.1 to 121.7 ± 5.7 nm) with a narrower particle size distribution (0.21 ± 0.001 to 0.25 ± 0.003) were produced. The SDS and Triton X-100 combination was chosen to evaluate other mcl-PHAs at 10 % (w/v) solids content. Slightly smaller nanoparticles were formed with carboxylated mcl-PHAs compared to mcl-PHAs having aliphatic pendant side chains. Mcl-PHA consisting of 18 % carboxylation (PHNC-2) formed a much smaller nanoparticles and higher zeta potential.