Coagent Modified Polypropylene Prepared by Reactive Extrusion: A New Look Into the Structure-Property Relations of Injection Molded Parts

Peroxide-mediated reactive extrusion of linear isotactic polypropylene (L-PP) was conducted in the presence of trimethylolpropane trimethacrylate (TMPTMA) and triallyl trimesate (TAM) coagents, using a twin screw extruder. The resulting coagent-modified polypropylenes (CM-PP) had higher viscosities and elasticities, as well as increased crystallization temperature compared to PP reacted only with peroxide (DCP-PP). Additionally, deviations from terminal flow, and strain hardening were observed in PP modified with TAM, signifying the presence of long chain branching (LCB). The CM-PP formulations retained the modulus and tensile strength of the parent L-PP, in spite of their lower molar mass and viscosities, whereas their elongation at break and the impact strength were better. This was attributed to the finer spherulitic structure of these materials, and to the disappearance of the skin-core layer in the injection molded specimens.

Method to Improve the Linearity of Active Commutating Mixers Using Dynamic Current Injection

A double balanced (DBM) CMOS mixer providing high linearity is presented in this paper. A cross-coupled pair used in the IF stage of the mixer to dynamically inject current into the to mixer provide a high linearity. The proposed DBM was fabricated using a standard 130-nm CMOS process and was tested on-wafer. The double balanced mixer delivers 10 dB conversion gain, 9.5 dBm IIP3, and input P1dB of -2.4 dBm. RF bandwidth of the proposed mixer is 6 GHz, covering 0.5 GHz to 6.5 GHz with IF bandwidth of 300 MHz. RF to IF and LO to IF isolation are also better than 59 dB in the whole frequency band. The circuit uses an area of 0.015 mm2 excluding bonding pads and draw 4.5mW from a 1.2V supply.