Tissue-specific bioscaffolds for adipose-derived stem/stromal cell expansion and delivery

Decellularized adipose tissue (DAT) is a promising biomaterial for soft tissue regeneration, and it provides a highly conducive microenvironment for human adipose-derived stem/stromal cell (ASC) attachment, proliferation, and adipogenesis. This thesis focused on developing techniques to fabricate 3-D bioscaffolds from enzymatically-digested DAT as platforms for ASC culture and delivery in adipose tissue engineering and large-scale ASC expansion. Initial work investigated chemically crosslinked microcarriers fabricated from pepsin-digested DAT as injectable adipo-inductive substrates for ASCs. DAT microcarriers highly supported ASC adipogenesis compared to gelatin microcarriers in a CELLSPIN system, as confirmed by glycerol-3-phosphate dehydrogenase (GPDH) enzyme activity, lipid accumulation, and endpoint RT-PCR. ASCs cultured on DAT microcarriers in proliferation medium also had elevated PPARγ, C/EBPα, and LPL expression which suggested adipo-inductive properties. In vivo testing of the DAT microcarriers exhibited stable volume retention and enhanced cellular infiltration, tissue remodeling, and angiogenesis. Building from this work, non-chemically crosslinked porous foams and bead foams were fabricated from α-amylase-digested DAT for soft tissue regeneration. Foams were stable and strongly supported ASC adipogenesis based on GPDH activity and endpoint RT-PCR. PPARγ, C/EBPα, and LPL expression in ASCs cultured on the foams in proliferation media indicated adipo-inductive properties. Foams with Young’s moduli similar to human fat also influenced ASC adipogenesis by enhanced GPDH activity. In vivo adipogenesis accompanied by a potent angiogenic response and rapid resorption showed their potential use in wound healing applications. Finally, non-chemically crosslinked porous microcarriers synthesized from α-amylase-digested DAT were investigated for ASC expansion. DAT microcarriers remained stable in culture and supported significantly higher ASC proliferation compared to Cultispher-S microcarriers in a CELLSPIN system. ASC immunophenotype was preserved for all expanded groups, with reduced adhesion marker expression under dynamic conditions. DAT microcarrier expansion upregulated ASC expression of early adipogenic (PPARγ, LPL) and chondrogenic (COMP) markers without inducing a mature phenotype. DAT microcarrier expanded ASCs also showed similar levels of adipogenesis and osteogenesis compared to Cultispher-S despite a significantly higher population fold-change, and had the highest level of chondrogenesis among all groups. This study demonstrates the promising use of DAT microcarriers as a clinically relevant strategy for ASC expansion while maintaining multilineage differentiation capacity.

BLOCK COPOLYMERS CONTAINING A LOW-SURFACE-ENERGY BLOCK AND THEIR APPLICATIONS

This thesis reports the synthesis and/or applications of three types of block copolymers that each bear a low-surface-energy block. First, poly(dimethylsiloxane)-block-poly(2-cinnamoyloxyethyl acrylate) (PDMS-b-PCEA) was synthesized and characterized. Cotton coating using a micellar solution of this block copolymer yielded superhydrophobic cotton fabrics. X-ray photoelectron spectroscopy (XPS) and surface property analyses indicated that the PDMS block topped the polymer coating. Photocuring the cotton swatches crosslinked the underlying PCEA layer and yielded permanent coatings. More interestingly, hydrophilically patterned superhydrophobic cotton fabrics were produced using photolithography that allowed the crosslinking of the coating around irradiated fibers but the removal, by solvent extraction, of the coating on fibers that were not irradiated. Since water-based ink only permeated the uncoated regions, such patterned fabric was further used to print ink patterns onto substrates such as fabrics, cardboard, paper, wood, and aluminum foil. Then, another PDMS-based diblock copolymer poly(dimethylsiloxane)-block-poly(glycidyl methacrylate) (PDMS-b-PGMA) was prepared. Different from PCEA that photocrosslinked around cotton fibers, PGMA reacted with hydroxyl groups on cotton fiber surfaces to get covalently attached. Further, different PGMA chains crosslinked with each other. PDMS-b-PGMA-coated cotton fabrics have been used for oil-water separations. In addition, polymeric nanoparticles were grafted onto cotton fiber surface before PDMS-b-PGMA was used to cover the surfaces of the grafted spheres and the residual surfaces of the cotton fibers. These two types of fabrics, coated by the block copolymer alone or by the polymer nanospheres and then the copolymer, were characterized by scanning electron microscope (SEM), Fourier transform infrared spectroscopy (FT-IR), and water repellency analyses. A comprehensive comparative study was made of their performances in oil-water separation. Finally, a fluorinated ABC triblock copolymer poly(acrylic acid)-block-poly(2-cinnamoyloxyethyl methacrylate)-block-poly(2-perfluorooctylethyl methacrylate) (PAA-b-PCEMA-b-PFOEMA) was used to iii encapsulate air nanobubbles. The produced air nanobubbles were thermodynamically stable in water and were some 100 times more stable than commercially available perfluorocarbon-filled microbubbles under ultrasound. These nanobubbles, due to their small sizes and thus ability to permeate the capillary networks of organs and to reach tumors, may expand the applications of microbubbles in diagnostic ultrasonography and find new applications in ultrasound-regulated drug delivery.

Reversibly Photo-Crosslinkable Polycarbonate-Based Polymersomes for Drug Encapsulation and Delivery

This thesis describes the preparation of polymersomes from poly(ethylene glycol)-block-polycarbonate (PEG-PC) copolymers functionalized with pendant coumarin groups. Coumarin groups undergo photo-reversible dimerization when irradiated with specific ultraviolet wavelengths, so they can be used to prepare polymers with photo-responsive properties. In this case, the pendant coumarin groups enable stabilization of the polymersome membrane through photo-crosslinking of the hydrophobic block. Initially, several novel cinnamoyl and coumarin functionalized cyclic carbonate monomers were synthesized using ester, ether, or amide linkages. While the homopolymerization of these functionalized monomers proved challenging due to their high melting points, both cinnamoyl and coumarin functionalized monomers were successfully copolymerized with trimethylene carbonate (TMC) at 100 ℃ using a catalyst-free melt polymerization process where the TMC doubled as a solvent for the higher melting point monomer. Using this system, polycarbonate copolymers with up to 33% incorporation of the functionalized monomers were prepared. In addition, an investigation of some anomalous polymerization results identified previously unreported triethylamine-based catalysts for the melt polymerization of carbonate monomers. These studies also demonstrated that the catalyst-free polymerization of TMC occurs faster and at lower temperatures than previously reported. Subsequently, the photo-crosslinking of cinnamoyl and coumarin functionalized polycarbonates was compared and coumarin was identified as the more effective crosslinking agent when using 300-400 nm UV. An investigation of the photo-reversibility of the coumarin dimerization revealed no discernible change in the properties of crosslinked networks, but rapid photo-reversion in dilute solutions. The photo-crosslinking and photo-reversion kinetics of the coumarin functionalized polycarbonates were determined to be second-order in both cases. Finally, the self-assembly of PEG-PC diblock copolymers functionalized with coumarin was examined and both reverse solvent evaporation and solvent displacement were found to induce self-assembly, with hydrophilic mass fractions (f-factors) of 12-28% resulting in the formation of solid microparticles and nanoparticles and f-factors of 33-43% resulting in the formation of polymersomes. The stabilization of these polymersome membranes through photo-initiator-free photo-crosslinking was demonstrated with the crosslinking allowing polymersomes to withstand centrifugation at 12,000 x g. In addition, the encapsulation of calcein, as a model small molecule drug, in the stabilized polymersomes was successfully demonstrated using confocal microscopy.