Reliability study of the electroless Ni–P layer against solder alloy

Copper (Cu) has been widely used in the under bump metallurgy of chip and substrate metallization for chip packaging. However, due to the rapid formation of Cu–Sn intermetallic compound (IMC) at the tin-based solder/Cu interface during solder reaction, the reliability of this type of solder joint is a serious concern. In this work, electroless nickel–phosphorous (Ni–P) layer was deposited on the Cu pad of the flexible substrate as a diffusion barrier between Cu and the solder materials. The deposition was carried out in a commercial acidic sodium hypophosphite bath at 85 °C for different pH values. It was found that for the same deposition time period, higher pH bath composition (mild acidic) yields thicker Ni–P layer with lower phosphorous content. Solder balls having composition 62%Sn–36%Pb–2%Ag were reflowed at 240 °C for 1 to 180 min on three types of electroless Ni–P layers deposited at the pH value of 4, 4.8 and 6, respectively. Thermal stability of the electroless Ni–P barrier layer against the Sn–36%Pb–2%Ag solder reflowed for different time periods was examined by scanning electron microscopy equipped with energy dispersed X-ray. Solder ball shear test was performed in order to find out the relationship between the mechanical strength of solder joints and the characteristics of the electroless Ni–P layer deposited. The layer deposited in the pH 4 acidic bath showed the weak barrier against reflow soldering whereas layer deposited in pH 6 acidic bath showed better barrier against reflow soldering. Mechanical strength of the joints were deteriorated quickly in the layer deposited at pH 4 acidic bath, which was found to be thin and has a high phosphorous content. From the cross-sectional studies and fracture surface analyses, it was found that the appearance of the dark crystalline phosphorous-rich Ni layer weakened the interface and hence lower solder ball shear strength. Ni–Sn IMC formed at the interfaces was found to be more stable at the low phosphorous content (∼14 at.%) layer. Electroless Ni–P deposited at mild acidic bath resulting phosphorous content of around 14 at.% is suggested as the best barrier layer for Sn–36%Pb–2%Ag solder.

The application of electrostatic dry powder deposition technology to coat drug-eluting stents

Purpose: A novel methodology has been introduced to effectively coat intravascular stents with sirolimus-loaded polymeric microparticles. Methods: Dry powders of the microparticulate formulation, consisting of non-erodible polymers, were produced by a supercritical, aerosol, solvent extraction system (ASES). A design of experiment (DOE) approach was conducted on the independent variables, such as organic/CO2 phase volume ratio, polymer weight and stirring-rate, while regression analysis was utilized to interpret the influence of all operational parameters on the dependent variable of particle size. The dry powders, so formed, entered an electric field created by corona charging and were sprayed on the earthed metal stent. Furthermore, the thermal stability of sirolimus was investigated to define the optimum conditions for fusion to the metal surfaces. Results: The electrostatic dry powder deposition technology (EDPDT) was used on the metal strut followed by fusion to produce uniform, reproducible and accurate coatings. The coated stents exhibited sustained release profiles over 25 days, similar to commercial products. EDPDT-coated stents displayed significant reduced platelet adhesion. Conclusions: EDPDT appeared to be a robust accurate and reproducible technology to coat eluting stents.

Assessment of the degradation of Aspirin by Differential Scanning Calorimetry (DSC)

Purpose. To study thermal stability of Aspirin and define thermal events that are associated with the thermal degradation of aspirin. Methods. Experiments were performed using a DSC 823e (Mettler Toledo, Swiss). Aspirin is prone to thermal degradation upon exposure to high temperatures. The melting point of aspirin is 140.1±0.4ºC (DSC). Aspirin has been examined by heating samples to 120ºC, 155ºC and 185ºC with subsequent cooling to -55ºC and a final heating to 155ºC. Although different heating and cooling ranges have been used, only results obtained at a rate of 10ºC/min will be presented. All runs where conducted in hermetically sealed pans. Results. Upon heating the sample to 120ºC no significant thermal event can be detected. After cooling the sample and reheating a glass transition can be observed at ~-8ºC, followed by the melting of aspirin at ~139ºC. By heating the sample to 155ºC melting of aspirin has been detected at ~139ºC. On cooling and subsequent heating a glass transition occurs at ~-32ºC, together with a broad crystallisation (onset at ~38ºC and peak maximum at ~57ºC) followed by a broad melting with an onset at 94ºC and peak maximum at ~112ºC. Finally, by heating the sample to 185ºC melting at ~ 139ºC was observed, and upon cooling and reheating a glass transition was detected at ~-26ºC and no further events could be recorded. Conclusions. This research demonstrates that the degradation steps of Aspirin depend on the thermal treatment. The main degradation products of different thermal treatments are currently unknown it is clear that acetic acid, which is one of the degradation products, acts as an antiplasticiser by lowering the glass transition temperature. In addition, due to the presence of the degradation products in liquid form (observed by hot stage microscopy), Aspirin is still present in the sample and recrystallises during the second heating step and melts at much lower temperatures.