Effect of 0.5 wt % Cu addition in Sn–3.5% Ag solder on the dissolution rate of Cu metallization

The dissolution of thin film under-bump-metallization (UBM) by molten solder has been one of the most serious processing problems in electronic packaging technology. Due to a higher melting temperature and a greater Sn content, a molten lead-free solder such as eutectic SnAg has a faster dissolution rate of thin film UBM than the eutectic SnPb. The work presented in this paper focuses on the role of 0.5 wt % Cu in the base Sn–3.5%Ag solder to reduce the dissolution of the Cu bond pad in ball grid array applications. We found that after 0.5 wt % Cu addition, the rate of dissolution of Cu in the molten Sn–3.5%Ag solder slows down dramatically. Systematic experimental work was carried out to understand the dissolution behavior of Cu by the molten Sn–3.5%Ag and Sn–3.5%Ag–0.5%Cu solders at 230–250 °C, for different time periods ranging from 1 to 10 min. From the curves of consumed Cu thickness, it was concluded that 0.5 wt % Cu addition actually reduces the concentration gradient at the Cu metallization/molten solder interface which reduces the driving force of dissolution. During the dissolution, excess Cu was found to precipitate out due to heterogeneous nucleation and growth of Cu6Sn5 at the solder melt/oxide interface. In turn, more Cu can be dissolved again. This process continues with time and leads to more dissolution of Cu from the bond pad than the amount expected from the solubility limit, but it occurs at a slower rate for the molten Sn–3.5%Ag–0.5%Cu solder. © 2003 American Institute of Physics.

Rheological characterisation and printing performance of Sn/Ag/Cu solder pastes

Lead-free solder paste printing process accounts for majority of the assembly defects in the electronic manufacturing industry. The study investigates rheological behaviour and stencil printing performance of the lead-free solder pastes (Sn/Ag/Cu). Oscillatory stress sweep test was carried out to study the visco-elastic behaviour of the lead-free solder pastes. The visco-elastic behaviour of the paste encompasses solid and liquid characteristic of the paste, which could be used to study the flow behaviour experienced by the pastes during the stencil printing process. From this study, it was found that the solid characteristics (G0) is higher than the liquid characteristic (G0 0) for the pastes material. In addition, the results from the study showed that the solder paste with a large G0 = G0 0 has a higher cohesiveness resulting in poor withdrawal of the paste during the stencil printing process. The phase angles (d) was used to correlate the quality of the dense suspensions to the formulation of solder paste materials. This study has revealed the value of having a rheological measurement for explaining and characterising solder pastes for stencil printing. As the demand for lead free pastes increases rheological measurements can assist with the formulation or development of new pastes.

Study of the rheological behaviour of Sn-Ag-Cu solder pastes and their correlation with printing performance

Solder paste plays an important role in the electronic assembly process by providing electrical, mechanical and thermal bonding between the components and the substrate. The rheological characterisation of pastes is an important step in the design and development of new paste formulations. With the ever increasing trend of miniaturisation of electronic products, the study of the rheological properties of solder pastes is becoming an integral part in the R&D of new paste formulations and in the quality monitoring and control during paste manufacture and electronic assembly process. This research work outlines some of the novel techniques which can be successfully used to investigate the rheology of leadfree solder pastes. The report also presents the results of the correlation of rheological properties with solder paste printing performance. Four different solder paste samples (namely paste P1, P2, P3 and P4) with different flux vehicle systems and particle size distributions were investigated in the study. As expected, all the paste samples showed shear thinning behaviour. Although the samples displayed similar flow behaviour at high shear rates, differences were observed at low shear rates. In the stencil printing trials, round deposits showed better results than rectangular deposits in terms of paste heights and aperture filling. Our results demonstrate a good correlation between higher paste viscosity and good printing performance. The results of the oscillatory and thixotropy tests were also successfully correlated to the printing behaviour of solder paste.