Mathematical modelling of the solidification of liquid tin with electromagnetic stirring

It is well known that during alloy solidification, convection currents close to the so-lidification front have an influence on the structure of dendrites, the local solute concentration, the pattern of solid segregation, and eventually the microstructure of the casting and hence its mechanical properties. Controlled stirring of the melt in continuous casting or in ingot solidification is thought to have a beneficial effect. Free convection currents occur naturally due to temperature differences in the melt and for any given configuration, their strength is a function of the degree of superheat present. A more controlled forced convection current can be induced using electro-magnetic stirring. The authors have applied their Control-Volume based MHD method [1, 2] to the problem of tin solidification in an annular crucible with a water-cooled inner wall and a resistance heated outer one, for both free and forced convection situations and for various degrees of superheat. This problem was studied experimentally by Vives and Perry [3] who obtained temperature measurements, front positions and maps of electro-magnetic body force for a range of superheat values. The results of the mathematical model are compared critically against the experimental ones, in order to validate the model and also to demonstrate the usefulness of the coupled solution technique followed, as a predictive tool and a design aid. Figs 6, refs 19.

The effects of thermo-electrically induced convection in alloy solidification

The effects of a constant uniform magnetic field on thermoelectric currents during dendritic solidification were investigated using a 2-dimensional enthalpy based numerical model. Using an approximation of the dendrite growing in free space it was found that the resulting Lorentz force generates a circulating flow influencing the solidification pattern. As the magnetic field strength increases it was found that secondary growth on the clockwise side of the primary arm of the dendrite was encouraged, while the anticlockwise side is suppressed due to a reduction in local free energy. The preferred direction of growth rotated in the clockwise sense under an anti-clockwise flow for both the binary alloy and pure material. The tip velociy is significantly increased compared to growth in stagnant flow. This is due to a small recirculation that follows the tip of the dendrite; bringing in colder liquid and lower concentrations of solute. The recirculation being not normally incident on the tip is most likely the cause for the rotation. Grain growth consisting of multiple seeds with the same anisotropy growing in the same plane, gives a competition to release latent heat resulting in stunted growth. The initial growth for each dendrite is very similar to the single seed cases indicating that dendrites must become before the thermoelectric interactions are significant.