Modelling technology to predict flip-chip assembly

This paper describes modelling technology and its use in providing data governing the assembly of flip-chip components. Details are given on the reflow and curing stages as well as the prediction of solder joint shapes. The reflow process involves the attachment of a die to a board via solder joints. After a reflow process, underfill material is placed between the die and the substrate where it is heated and cured. Upon cooling the thermal mismatch between the die, underfill, solder bumps, and substrate will result in a nonuniform deformation profile across the assembly and hence stress. Shape predictions then thermal solidification and stress prediction are undertaken on solder joints during the reflow process. Both thermal and stress calculations are undertaken to predict phenomena occurring during the curing of the underfill material. These stresses may result in delamination between the underfill and its surrounding materials leading to a subsequent reduction in component performance and lifetime. Comparisons between simulations and experiments for die curvature will be given for the reflow and curing process

No-flow underfill flip chip assembly–an experimental and modeling analysis

In the flip-chip assembly process, no-flow underfill materials have a particular advantage over traditional underfill: the application and curing of the former can be undertaken before and during the reflow process. This advantage can be exploited to increase the flip-chip manufacturing throughput. However, adopting a no-flow underfill process may introduce reliability issues such as underfill entrapment, delamination at interfaces between underfill and other materials, and lower solder joint fatigue life. This paper presents an analysis on the assembly and the reliability of flip-chips with no-flow underfill. The methodology adopted in the work is a combination of experimental and computer-modeling methods. Two types of no-flow underfill materials have been used for the flip chips. The samples have been inspected with X-ray and scanning acoustic microscope inspection systems to find voids and other defects. Eleven samples for each type of underfill material have been subjected to thermal shock test and the number of cycles to failure for these flip chips have been found. In the computer modeling part of the work, a comprehensive parametric study has provided details on the relationship between the material properties and reliability, and on how underfill entrapment may affect the thermal–mechanical fatigue life of flip chips with no-flow underfill.

A modelling and experimental analysis of the no-flow underfill process for flip-chip assembly

In the flip-chip assembly process, no-flow underfill materials have a particular advantage over traditional underfills as the application and curing of this type of underfill can be undertaken before and during the reflow process - adding high volume throughput. Adopting a no-flow underfill process may result in underfill entrapment between solder and fluid, voiding in the underfill, a possible delamination between underfill and surrounding surfaces. The magnitude of these phenomena may adversely affect the reliability of the assembly in terms of solder joint thermal fatigue. This paper presents both an experimental and mdeling analysis investigating the reliabity of a flip-chip component and how the magnitude of underfill entrapment may affect thermal-mechanical fatigue life.

Modelling the Lamination Process for Ruggedised Displays

Active matrix liquid crystal displays (AMLCD) need to be protected in severe environments. This is achieved through a ruggedisation process, where the display is laminated with cover glasses to become a more robust structure. The ruggedisation process can in itself cause stresses in the display and this can lead to delamination failures during the lamination process, during qualification testing or in-service. Controlling the magnitude of stress in a display during the lamination process is of course very important and this depends highly on the materials used. This paper discusses the use of finite element analysis to investigate the use of different materials in the lamination process and how such materials can affect the stress magnitude in the display.

Reliability analysis for power electronics modules

This paper discusses the reliability of power electronics modules. The approach taken combines numerical modeling techniques with experimentation and accelerated testing to identify failure modes and mechanisms for the power module structure and most importantly the root cause of a potential failure. The paper details results for two types of failure (i) wire bond fatigue and (ii) substrate delamination. Finite element method modeling techniques have been used to predict the stress distribution within the module structures. A response surface optimisation approach has been employed to enable the optimal design and parameter sensitivity to be determined. The response surface is used by a Monte Carlo method to determine the effects of uncertainty in the design.