Condition assessment of a 63-year old reinforced concrete structure exposed to the North Sea

This paper describes the condition of a reinforced concrete balustrade consisting of some 1000 individual beam elements all exposed similarly to the hostile marine environment of the North Sea at Arbroath, Scotland since 1943. A comparison is made of the condition of the original construction with the condition of repairs carried out in 1968 and in 1993. It is shown that the 1943 construction shows very little corrosion-induced cracking and little rust staining even though it does not appear to be of high construction quality. Only a very low percentage of the balustrade beams have been replaced. In contrast the beam installed in 1968 and later in 1993 show very considerable and large concrete cracks directly attributable to the corrosion of the longitudinal reinforcement, even though the concrete is of a higher quality and density. A detailed condition survey and statistics of crack sizes are presented in the paper. It is found that the higher corrosion resistance of the 1943 concrete is generally consistent with the concrete electrical resistivity measurements but the degree of corrosion of the reinforcing bars is inconsistent with chloride penetration measurements. The results are compared with the very few observations available in the literature for ageing concrete structures in marine environments. The results cast doubt on the conventional wisdom that chloride content at the reinforcement correlates well with reinforcement corrosion.

Prediction of reinforcement corrosion in concrete and its effects on concrete cracking and strength reduction

Based on extensive research on reinforcing steel corrosion in concrete in the past decades, it is now possible to estimate the effect of the progression of reinforcement corrosion in concrete infrastructure on its structural performance. There are still areas of considerable uncertainty in the models and in the data available, however This paper uses a recently developed model for reinforcement corrosion in concrete to improve the estimation process and to indicate the practical implications. In particular stochastic models are used to estimate the time likely to elapse for each phase of the whole corrosion process: initiation, corrosion-induced concrete cracking, and structural strength reduction. It was found that, for practical flexural structures subject to chloride attacks, corrosion initiation may start quite early in their service life. It was also found that, once the structure is considered to be unserviceable due to corrosion-induced cracking, there is considerable remaining service life before the structure can be considered to have become unsafe. The procedure proposed in the paper has the potential to serve as a rational tool for practitioners, operators, and asset managers to make decisions about the optimal timing of repairs, strengthening, and/or rehabilitation of corrosion-affected concrete infrastructure. Timely intervention has the potential to prolong the service life of infrastructure.