A modelling and experimental analysis of the no-flow underfill process for flip-chip assembly

In the flip-chip assembly process, no-flow underfill materials have a particular advantage over traditional underfills as the application and curing of this type of underfill can be undertaken before and during the reflow process - adding high volume throughput. Adopting a no-flow underfill process may result in underfill entrapment between solder and fluid, voiding in the underfill, a possible delamination between underfill and surrounding surfaces. The magnitude of these phenomena may adversely affect the reliability of the assembly in terms of solder joint thermal fatigue. This paper presents both an experimental and mdeling analysis investigating the reliabity of a flip-chip component and how the magnitude of underfill entrapment may affect thermal-mechanical fatigue life.

Lifetime assessment of electronic components for high reliability aerospace applications

This paper details a modelling approach for assessing the in-service (field) reliability and thermal fatigue life-time of electronic package interconnects for components used in the assembly of an aerospace system. The Finite Element slice model of a Plastic Ball Grid Array (PBGA) package and suitable energy based damage models for crack length predictions are used in this study. Thermal fatigue damage induced in tin-lead solder joints are investigated by simulating the crack growth process under a set of prescribed field temperature profiles that cover the period of operational life. The overall crack length in the solder joint for all different thermal profiles and number of cycles for each profile is predicted using a superposition technique. The effect of using an underfill is also presented. A procedure for verifying the field lifetime predictions for the electronic package by using reliability assessment under Accelerated Thermal Cycle (ATC) testing is also briefly outlined.

Decision support systems for eco-friendly electronic products

This paper discusses an optimisation based decision support system and methodology for electronic packaging and product design and development which is capable of addressing in efficient manner specified environmental, reliability and cost requirements. A study which focuses on the design of a flip-chip package is presented. Different alternatives for the design of the flip-chip package are considered based on existing options for the applied underfill and volume of solder material used to form the interconnects. Variations in these design input parameters have simultaneous effect on package aspects such as cost, environmental impact and reliability. A decision system for the design of the flip-chip that uses numerical optimisation approach is used to identify the package optimal specification which satisfies the imposed requirements. The reliability aspect of interest is the fatigue of solder joints under thermal cycling. Transient nonlinear finite element analysis (FEA) is used to simulate the thermal fatigue damage in solder joints subject to thermal cycling. Simulation results are manipulated within design of experiments and response surface modelling framework to provide numerical model for reliability which can be used to quantify the package reliability. Assessment of the environmental impact of the package materials is performed by using so called Toxic Index (TI). In this paper we demonstrate the evaluation of the environmental impact only for underfill and lead-free solder materials. This evaluation is based on the amount of material per flip-chip package. Cost is the dominant factor in contemporary flip-chip packaging industry. In the optimisation based decision support system for the design of the flip-chip package, cost of materials which varies as a result of variations in the design parameters is considered.

Assessing the performance of crack detection tests for solder joints

This paper presents both modelling and experimental test data to characterise the performance of four non-destructive tests. The focus is on determining the presence and rough magnitude of thermal fatigue cracks within the solder joints for a surface mount resistor on a strip of FR4 PCB. The tests all operate by applying mechanical loads to the PCB and monitoring the strain response at the top of the resistor. The modelling results show that of the four tests investigated, three are sensitive to the presence of a crack in the joint and its magnitude. Hence these tests show promise in being able to detect cracking caused by accelerated testing. The experimental data supports these results although more validation is required.

Material properties, geometry and their effect on the fatigue life of two flip-chip models

This paper describes how modeling technology has been used in providing fatigue life time data of two flip-chip models. Full-scale three-dimensional modeling of flip-chips under cyclic thermal loading has been combined with solder joint stand-off height prediction to analyze the stress and strain conditions in the two models. The Coffin-Manson empirical relationship is employed to predict the fatigue life times of the solder interconnects. In order to help designers in selecting the underfill material and the printed circuit board, the Young's modulus and the coefficient of thermal expansion of the underfill, as well as the thickness of the printed circuit boards are treated as variable parameters. Fatigue life times are therefore calculated over a range of these material and geometry parameters. In this paper we will also describe how the use of micro-via technology may affect fatigue life

Modeling and experiments on an isothermal fatigue test for solder joints

This paper investigates an isothermal fatigue test for solder joints developed at the NPL. The test specimen is a lap joint between two copper arms. During the test the displacement at the ends of the copper are controlled and the force measured. The modeling results in the paper show that the displacement across the solder joint is not equal to the displacement applied at the end of the specimen. This is due to deformation within the copper arms. A method is described to compensate for this difference. The strain distribution in the solder was determined by finite element analysis and compared to the distribution generated by a theoretical 'ideal' test which generates an almost pure shear mode in the solder. By using a damage-based constitutive law the shape of the crack generated in the specimen has been predicted for both the actual test and the ideal pure shear test. Results from the simulations are also compared with experimental data using SnAgCu solder.