Modelling the effect of temperature on product reliability

Reliability of electronic parts is a major concern for many manufacturers, since early failures in the field can cost an enormous amount to repair - in many cases far more than the original cost of the product. A great deal of effort is expended by manufacturers to determine the failure rates for a process or the fraction of parts that will fail in a period of time. It is widely recognized that the traditional approach to reliability predictions for electronic systems are not suitable for today's products. This approach, based on statistical methods only, does not address the physics governing the failure mechanisms in electronic systems. This paper discusses virtual prototyping technologies which can predict the physics taking place and relate this to appropriate failure mechanisms. Simulation results illustrate the effect of temperature on the assembly process of an electronic package and the lifetime of a flip-chip package.

Wire bond reliability for power electronic modules - effect of bonding temperature

In this paper, thermal cycling reliability along with ANSYS analysis of the residual stress generated in heavy-gauge Al bond wires at different bonding temperatures is reported. 99.999% pure Al wires of 375 mum in diameter, were ultrasonically bonded to silicon dies coated with a 5mum thick Al metallisation at 25degC (room temperature), 100degC and 200degC, respectively (with the same bonding parameters). The wire bonded samples were then subjected to thermal cycling in air from -60degC to +150degC. The degradation rate of the wire bonds was assessed by means of bond shear test and via microstructural characterisation. Prior to thermal cycling, the shear strength of all of the wire bonds was approximately equal to the shear strength of pure aluminum and independent of bonding temperature. During thermal cycling, however, the shear strength of room temperature bonded samples was observed to decrease more rapidly (as compared to bonds formed at 100degC and 200degC) as a result of a high crack propagation rate across the bonding area. In addition, modification of the grain structure at the bonding interface was also observed with bonding temperature, leading to changes in the mechanical properties of the wire. The heat and pressure induced by the high temperature bonding is believed to promote grain recovery and recrystallisation, softening the wires through removal of the dislocations and plastic strain energy. Coarse grains formed at the bonding interface after bonding at elevated temperatures may also contribute to greater resistance for crack propagation, thus lowering the wire bond degradation rate

Effect of temperature on slumping behaviour of lead-free solder paste and its rheological simulation

Variation in temperature can have a significant impact on the rheological characterisation of solder pastes used in the electronic assembly of surface mount devices. This paper concerns the study of the effect of temperature on slumping characteristics of lead-free solder pastes. The identification of the slumping characteristics can help in the correlation of the pastes characteristics to its printing performance. Further issues, which aid in justifying the undertaking of such a study, include the temperature differences identified both at the squeegee during the print, and during reflow. Due to these temperature variations, it is imperative to understand how slump differs with a temperature gradient