Low temperature crystal structures of two rhodanine derivatives, 3-amino rhodanine and 3-methyl rhodanine: geometry of the rhodanine ring

Rhodanines (2-thio-4-oxothiazolidines) are synthetic small molecular weight organic molecules with diverse applications in biochemistry, medicinal chemistry, photochemistry, coordination chemistry and industry. The X-ray crystal structure determination of two rhodanine derivatives, namely (I), 3-aminorhodanine [3-amino-2-thio-4-oxothiazolidine], C3H4N2OS2, and (II) 3-methylrhodanine [3-methyl-2-thio-4-oxothiazolidine], C4H5NOS2, have been conducted at 100 K. I crystallizes in the monoclinic space group P2(1)/n with unit cell parameters a = 9.662(2), b = 9.234(2), c = 13.384(2) angstrom, beta = 105.425(3)degrees, V = 1151.1(3) angstrom(3), Z = 8 (2 independent molecules per asymmetric unit), density (calculated) = 1.710 mg/m(3), absorption coefficient = 0.815 mm(-1). II crystallizes in the orthorhombic space group Iba2 with unit cell a = 20.117(4), b = 23.449(5), c = 7.852(2) angstrom, V = 3703.9(12) angstrom(3), Z = 24 (three independent molecules per asymmetric unit), density (calculated) = 1.584 mg/m(3), absorption coefficient 0.755 mm(-1). For I in the final refinement cycle the data/restraints/parameter ratios were 2639/0/161, goodness-of-fit on F-2 = 0.934, final R indices [I > 2sigma(I)] were R1 = 0.0299, wR2 = 0.0545 and R indices (all data) R1 = 0.0399, wR2 = 0.0568. The largest difference peak and hole were 0.402 and -0.259 e angstrom(-3). For II in the final refinement cycle the data/restraints/parameter ratios were 3372/1/221, goodness-of-fit on F(2) = 0.950, final R indices [I > 2sigma(I)] were R1 = 0.0407, wR2 = 0.1048 and R indices (all data) R1 = 0.0450, wR2 = 0.1088. The absolute structure parameter = 0.19(9) and largest difference peak and hole 0.934 and -0.301 e angstrom(-3). Details of the geometry of the five molecules (two for I and three for II) and the crystal structures are fully discussed. Corresponding features of the molecular geometry are highly consistent and firmly establish the geometry of the rhodanine

Central nervous system drugs: Low temperature X-ray structures of (I) the base 5-(2,3-dichlorophenyl)-2,4-diamino-6-fluoromethyl-pyrimidine (4030W92) and (II) 5-(2,6-dichlorophenyl)-1-H-2,4-diamino-6-methyl-pyrimidine methanesulphonic acid salt (227C89)

The X-ray crystal structures of (I), the base 4030W92, 5-(2,3-dichlorophenyl)-2,4-diamino-6-fluoromethyl-pyrimidine, C11H9Cl2FN4, and (II) 227C89, the methanesulphonic acid salt of 5-(2,6-dichlorophenyl)-1-H-2,4-diamino-6-methyl-pyrimidine, C11H11Cl2N4 center dot CH3O3S, have been carried out at low temperature. A detailed comparison of the two structures is given. Structure (I) is non-centrosymmetric, crystallizing in space group P2(1) with unit cell a = 10.821(3), b = 8.290(3), c = 13.819(4) angstrom, beta = 105.980(6)degrees, V = 1191.8(6) angstrom(3), Z = 4 (two molecules per asymmetric unit) and density (calculated) = 1.600 mg/m(3). Structure (II) crystallizes in the triclinic space group P (1) over bar with unit cell a = 7.686(2), b = 8.233(2), c = 12.234(2) angstrom, alpha = 78.379(4), beta = 87.195(4), gamma = 86.811(4)degrees, V = 756.6(2) angstrom(3), Z = 2, density (calculated) = 1.603 mg/m(3). Final R indices [I > 2sigma(I)] are R1 = 0.0572, wR2 = 0.1003 for (I) and R1 = 0.0558, wR2 = 0.0982 for (II). R indices (all data) are R1 = 0.0983, wR2 = 0.1116 for (I) and R1 = 0.1009, wR2 = 0.1117 for (II). 5- Phenyl-2,4 diaminopyrimidine and 6-phenyl-1,2,4 triazine derivatives, which include lamotrigine (3,5-diamino-6-(2,3-dichlorophenyl)-1,2,4-triazine), have been investigated for some time for their effects on the central nervous system. The three dimensional structures reported here form part of a newly developed data base for the detailed investigation of members of this structural series and their biological activities.

Low temperature X-ray crystallographic structures of two lamotrigine analogues: (I) 2-methyl,3-amino, 5-imino-6-(2,3-dichlorophenyl)-1,2,4-triazine water solvate and (II) 2-methyl,3,5-diamino-6-(2,3-dichlorophenyl)-1,2,4-triazine isethionate, hemi-hydrate

The X-ray crystal structures of two lamotrigine derivatives (I) 2-methyl, 3-amino, 5-imino-6-(2, 3-dichlorophenyl)-1,2,4-triazine, C10H9Cl2N5, as the hemi hydrate and (II) 2-methyl,3,5-diamino-6-(2,3-dichlorophenyl)-1,2,4-triazine, C10H10Cl2N5, as the isethionate-water solvate, have been carried out at liquid nitrogen temperature. A detailed comparison of the two structures is given. Both are monoclinic and centrosymmetric, with (I) in space group C2/c, and (II) in space group P2(1)/n. For (I) the unit cell dimensions are a = 19.5466(10), b = 7.5483(4), c = 15.7861(8) angstrom, beta = 91.458(3)degrees, volume = 2328.4(2) angstrom(3), Z = 8, density = 1.590 Mg/m(3); for (II). For (II) the unit cell dimensions are a = 6.0566(2), b = 11.0084(4) c = 23.9973(9) angstrom, beta = 92.587(3)degrees, volume = 1598.35(10) angstrom(3), Z = 4, density = 1.597 Mg/m(3). For (I) final R indices [I > 2sigma(I)] are R1 = 0.0356, wR2 = 0.0782 and R indices (all data) are R1 = 0.0424, wR2 = 0.0817. For (II) final R indices [I > 2sigma(I)] are R1 = 0.0380, wR2 = 0.0871 and R indices (all data) R1 = 0.0558, wR2 = 0.0949. Both structures have a molecule of water of crystallization and (II) also includes a solvated CH3SO3. Comparisons are made between the two structures. Structure (I) is very unusual in having a = NH group at position C5' on the triazine ring. No other examples of this particular substitution, which is usually -NH2, have been reported.

Water transport in zinc oxy-chloride cements

The water uptake and water loss behaviour in three different formulations of zinc oxy-chloride cement have been studied in detail. Specimens of each material were subjected to a high humidity atmosphere (93% RH) over saturated aqueous sodium sulfate, and a low humidity desiccating atmosphere over concentrated sulfuric acid. In high humidity, the cement formulated from the nominal 75% ZnCl2 solutions gained mass, eventually becoming too sticky to weigh further. The specimens at 25% and 50% ZnCl2 by contrast lost mass by a diffusion process, though by 1 week the 50% cement had stated to gain mass and was also too sticky to weigh. In low humidity, all three cements lost mass, again by a diffusion process. Both water gain and water loss followed Fick's law for a considerable time. In the case of water loss under desiccating conditions, this corresponded to values of Mt/MĄ well above 0.5. However, plots did not go through the origin, showing that there was an induction period before true diffusion began. Diffusion coefficients varied from 1.56 x 10-5 (75% ZnCl2) to 2.75 x 10-5 cm2/s (50% ZnCl2), and appeared to be influenced not simply by composition. The drying of the 25% and 50% ZnCl2 cements in high humidity conditions occurred at a much lower rate, with a value of D of 2.5 x 10-8 cm2/s for the 25% ZnCl2 cement. This cement was found to equilibrate slowly, but total water loss did not differ significantly from that of the cements stored under desiccating conditions. Equilibration times for water loss in desiccating conditions were of the order of 2-4 hours, depending on ZnCl2 content; equilibrium water losses were respectively 28.8 [25% ZnCl2], 16.2 [50%] and 12.4 [75%] which followed the order of ZnCl2 content. It is concluded that the water transport processes are strongly influenced by the ZnCl2 content of the cement.