Thermal-mechanical modelling of power electronic module packaging

In this paper the reliability of the isolation substrate and chip mountdown solder interconnect of power modules under thermal-mechanical loading has been analysed using a numerical modelling approach. The damage indicators such as the peel stress and the accumulated plastic work density in solder interconnect are calculated for a range of geometrical design parameters, and the effects of these parameters on the reliability are studied by using a combination of the finite element analysis (FEA) method and optimisation techniques. The sensitivities of the reliability of the isolation substrate and solder interconnect to the changes of the design parameters are obtained and optimal designs are studied using response surface approximation and gradient optimization method

Predicting the relationship between reliability and geometric parameters of cu column bumped flip-chips

Cu column bumping is a novel flip chip packaging technique that allows Cu columns to be bonded directly with the dies. It has eliminated the under-bump-metallurgy (UBM) fonnation step of the traditional flip chip manufacturing process. This bumping technique has the potential benefits of simplifying the flip chip manufacturing process, increasing productivity and the UO counts. In this paper, a study of reliability of Cu column bumped flip chips will be presented. Computer modelling methods have been used to predict the shape of solder joints and the response of flip chips to cyclic thermal-mechanical loading. The accumulated plastic strain energy at the corner solder joints has been used as an indicator of the solder joint reliability. Models with a wide range of design parameters have been compared for their reliability. The design parameters that have been investigated are the copper column height and radius, PCB pad radius, solder volume and Cu column wetting height. The relative importance ranking of these parameters has been obtained. The Lead-free solder material 96.5Sn3.5Ag has been used in this modelling work.

Study of Anisotropic Conductive Adhesive Joint Behaviour under 3-Point Bending

Flip chip interconnections using anisotropic conductive film (ACF) are now a very attractive technique for electronic packaging assembly. Although ACF is environmentally friendly, many factors may influence the reliability of the final ACF joint. External mechanical loading is one of these factors. Finite element analysis (FEA) was carried out to understand the effect of mechanical loading on the ACF joint. A 3-dimensional model of adhesively bonded flip chip assembly was built and simulations were performed for the 3-point bending test. The results show that the stress at its highest value at the corners, where the chip and ACF were connected together. The ACF thickness was increased at these corner regions. It was found that higher mechanical loading results in higher stress that causes a greater gap between the chip and the substrate at the corner position. Experimental work was also carried out to study the electrical reliability of the ACF joint with the applied bending load. As per the prediction from FEA, it was found that at first the corner joint failed. Successive open joints from the corner towards the middle were also noticed with the increase of the applied load.

Lifetime prediction for power electronics module substrate mount-down solder interconnect

A numerical modeling method for the prediction of the lifetime of solder joints of relatively large solder area under cyclic thermal-mechanical loading conditions has been developed. The method is based on the Miner's linear damage accumulation rule and the properties of the accumulated plastic strain in front of the crack in large area solder joint. The nonlinear distribution of the damage indicator in the solder joints have been taken into account. The method has been used to calculate the lifetime of the solder interconnect in a power module under mixed cyclic loading conditions found in railway traction control applications. The results show that the solder thickness is a parameter that has a strong influence on the damage and therefore the lifetime of the solder joint while the substrate width and the thickness of the baseplate are much less important for the lifetime

Computer modelling analysis of the globtop's effects on aluminium wirebond reliability

In power electronics modules, heavy aluminium wires, i.e. wire diameters greater than 100 microns, are bonded to the active semiconductor devices and conductor metallization to form electric circuits of the power electronic module. Due to the high currents that may flow through these wires, a single connection usually contains several wires and thus, a large number of wires are used in a power electronics module. Under normal operation or test condition, a significant amount of stresses and strains induced in the wire and bonding interfaces, resulting in failure over time. In this paper, computer modelling techniques are used to analyse the effect of globtop design on the reliability of aluminium wirebonds under cyclic thermal-mechanical loading conditions. The results will show the sensitivity of the reliability of the wirebonds to the changes in the geometry and the material properties of the wirebond globtop.

Computer simulation of crack propagation in power electronics module solder joints

A numerical modelling method for the analysis of solder joint damage and crack propagation has been described in this paper. The method is based on the disturbed state concept. Under cyclic thermal-mechanical loading conditions, the level of damage that occurs in solder joints is assumed to be a simple monotonic scalar function of the accumulated equivalent plastic strain. The increase of damage leads to crack initiation and propagation. By tracking the evolution of the damage level in solder joints, crack propagation path and rate can be simulated using Finite Element Analysis method. The discussions are focused on issues in the implementation of the method. The technique of speeding up the simulation and the mesh dependency issues are analysed. As an example of the application of this method, crack propagation in solder joints of power electronics modules under cyclic thermal-mechanical loading conditions has been analyzed and the predicted cracked area size after 3000 loading cycles is consistent with experimental results.

Computer simulation of aluminium wirebonds with globtop in power electronics modules

In this paper, computer modelling techniques are used to analyse the effects of globtops on the reliability of aluminium wirebonds in power electronics modules under cyclic thermal-mechanical loading conditions. The sensitivity of the wirehond reliability to the changes of the geometric and the material property parameters of wirebond globtop are evaluated and the optimal combination of the Young's modulus and the coefficient of thermal expansion have been predicted.

The use of acoustic emission monitoring to rank paper materials with respect to their fracture toughness

In this study, a simplified Acoustic Emission (AE) equipment, in essence an AE signal conditioner and a USB (Universal Serial Bus) data acquisition system, is used to study what happens in paper structures during mechanical loading. By the use of such equipment, some parameters that can be extracted are e.g. the stress and strain at onset of AE, the stress and strain at the onset of rapid AE defined as some numerical factor (larger then one) times the initial emission rate, the emission rate at the first stage of loading and the stress and strain at final failure i.e. when the specimen loses its load carrying ability.In this study however, the interest is focused on one particular parameter i.e. the elastic strain energy density W c at onset of AE. This is a parameter with a clear physical meaning and in this study, the correlation between this parameter and a fracture toughness measure, is investigated.The conclusion is that when nine different paper materials (with a large span regarding properties) are considered, there is a correlation (however not linear) between these two parameters.