Computer modelling of the reliability of flip chips with metal column bumping

Recently, research has been carried out to test a novel bumping method which omits the under bump metallurgy forming process by bonding copper columns directly onto the Al pads of the silicon dies. This bumping method could be adopted to simplify the flip chip manufacturing process, increase the productivity and achieve a higher I/O count. This paper describes an investigation of the solder joint reliability of flip-chips based on this new bumping process. Computer modelling methods are used to predict the shape of solder joints and response of flip chips to thermal cyclic loading. The accumulated plastic strain energy at the comer solder joints is used as the damage indicator. Models with a range of design parameters have been compared for their reliability. The parameters that have been investigated are the copper column height, radius and solder volume. The ranking of the relative importance of these parameters is given. For most of the results presented in the paper, the solder material has been assumed to be the lead-free 96.5Sn3.5Ag alloy but some results for 60Sn40Pb solder joints have also been presented.

Predicting the relationship between reliability and geometric parameters of cu column bumped flip-chips

Cu column bumping is a novel flip chip packaging technique that allows Cu columns to be bonded directly with the dies. It has eliminated the under-bump-metallurgy (UBM) fonnation step of the traditional flip chip manufacturing process. This bumping technique has the potential benefits of simplifying the flip chip manufacturing process, increasing productivity and the UO counts. In this paper, a study of reliability of Cu column bumped flip chips will be presented. Computer modelling methods have been used to predict the shape of solder joints and the response of flip chips to cyclic thermal-mechanical loading. The accumulated plastic strain energy at the corner solder joints has been used as an indicator of the solder joint reliability. Models with a wide range of design parameters have been compared for their reliability. The design parameters that have been investigated are the copper column height and radius, PCB pad radius, solder volume and Cu column wetting height. The relative importance ranking of these parameters has been obtained. The Lead-free solder material 96.5Sn3.5Ag has been used in this modelling work.

Macro-Micro Modelling Analysis for High Density Packaged Flip Chips

A wide range of flip chip technologies with solder or adhesives have become dominant solutions for high density packaging applications due to the excellent electrical performance, high I/O density and good thermal performance. This paper discusses the use of modeling technique to predict the reliability of high density packaged flip chips in the humid environment. Reliability assessment is discussed for flip chip package at ultra-fine pitch with anisotropic conductive film (ACF). The purpose of this modeling work is to understand the role that moisture plays in the failure of ACF flip chips. A macro-micro 3D finite element modeling technique was used in order to make the multi-length-scale modeling of the ACF flip chip possible. Modeling results are consistent with the findings in the experimental work

Material properties, geometry and their effect on the fatigue life of two flip-chip models

This paper describes how modeling technology has been used in providing fatigue life time data of two flip-chip models. Full-scale three-dimensional modeling of flip-chips under cyclic thermal loading has been combined with solder joint stand-off height prediction to analyze the stress and strain conditions in the two models. The Coffin-Manson empirical relationship is employed to predict the fatigue life times of the solder interconnects. In order to help designers in selecting the underfill material and the printed circuit board, the Young's modulus and the coefficient of thermal expansion of the underfill, as well as the thickness of the printed circuit boards are treated as variable parameters. Fatigue life times are therefore calculated over a range of these material and geometry parameters. In this paper we will also describe how the use of micro-via technology may affect fatigue life

Reliability analysis of flip chip designs via computer simulation

A flip chip component is a silicon chip mounted to a substrate with the active area facing the substrate. This paper presents the results of an investigation into the relationship between a number of important material properties and geometric parameters on the thermal-mechanical fatigue reliability of a standard flip chip design and a flip chip design with the use of microvias. Computer modeling has been used to analyze the mechanical conditions of flip chips under cyclic thermal loading where the Coffin-Manson empirical relationship has been used to predict the life time of the solder interconnects. The material properties and geometry parameters that have been investigated are the Young's modulus, the coefficient of thermal expansion (CTE) of the underfill, the out-of-plane CTE (CTEz) of the substrate, the thickness of the substrate, and the standoff height. When these parameters vary, the predicted life-times are calculated and some of the features of the results are explained. By comparing the predicted lifetimes of the two designs and the strain conditions under thermal loading, the local CTE mismatch has been found to be one of most important factors in defining the reliability of flip chips with microvias.

Modelling the performance of lead-Free solder interconnects for copper bumped flip-chip devices

Traditionally, before flip chips can be assembled the dies have to be attached with solder bumps. This process involves the deposition of metal layers on the Al pads on the dies and this is called the under bump metallurgy (UBM). In an alternative process, however, Copper (Cu) columns can be used to replace solder bumps and the UBM process may be omitted altogether. After the bumping process, the bumped dies can be assembled on to the printed circuit board (PCB) by using either solder or conductive adhesives. In this work, the reliability issues of flip chips with Cu column bumped dies have been studied. The flip chip lifetime associated with the solder fatigue failure has been modeled for a range of geometric parameters. The relative importance of these parameters is given and solder volume has been identified as the most important design parameter for long-term reliability. Another important problem that has been studied in this work is the dissolution of protection metals on the pad and Cu column in the reflow process. For small solder joints the amount of Cu which dissolves into the molten solder after the protection layers have worn out may significantly affect solder joint properties.

Modelling the metal arc weldpool

Traditionally, before flip chips can be assembled the dies have to be attached with solder bumps. This process involves the deposition of metal layers on the Al pads on the dies and this is called the under bump metallurgy (UBM). In an alternative process, however, Copper (Cu) columns can be used to replace solder bumps and the UBM process may be omitted altogether. After the bumping process, the bumped dies can be assembled on to the printed circuit board (PCB) by using either solder or conductive adhesives. In this work, the reliability issues of flip chips with Cu column bumped dies have been studied. The flip chip lifetime associated with the solder fatigue failure has been modeled for a range of geometric parameters. The relative importance of these parameters is given and solder volume has been identified as the most important design parameter for long-term reliability. Another important problem that has been studied in this work is the dissolution of protection metals on the pad and Cu column in the reflow process. For small solder joints the amount of Cu which dissolves into the molten solder after the protection layers have worn out may significantly affect solder joint properties.

No-flow underfill flip chip assembly–an experimental and modeling analysis

In the flip-chip assembly process, no-flow underfill materials have a particular advantage over traditional underfill: the application and curing of the former can be undertaken before and during the reflow process. This advantage can be exploited to increase the flip-chip manufacturing throughput. However, adopting a no-flow underfill process may introduce reliability issues such as underfill entrapment, delamination at interfaces between underfill and other materials, and lower solder joint fatigue life. This paper presents an analysis on the assembly and the reliability of flip-chips with no-flow underfill. The methodology adopted in the work is a combination of experimental and computer-modeling methods. Two types of no-flow underfill materials have been used for the flip chips. The samples have been inspected with X-ray and scanning acoustic microscope inspection systems to find voids and other defects. Eleven samples for each type of underfill material have been subjected to thermal shock test and the number of cycles to failure for these flip chips have been found. In the computer modeling part of the work, a comprehensive parametric study has provided details on the relationship between the material properties and reliability, and on how underfill entrapment may affect the thermal–mechanical fatigue life of flip chips with no-flow underfill.

Dynamic analysis of Flip-Chip Self-Alignment

Self-alignment of soldered electronic components such as flip-chips (FC), ball grid arrays (BGA) and optoelectronic devices during solder reflow is important as it ensures good alignment between components and substrates. Two uncoupled analytical models are presented which provide estimates of the dynamic time scales of both the chip and the solder in the self-alignment process. These predicted time scales can be used to decide whether a coupled dynamic analysis is required for the analysis of the chip motion. In this paper, we will show that for flip-chips, the alignment dynamics can be described accurately only when the chip motion is coupled with the solder motion because the two have similar time-scale values. To study this coupled phenomenon, a dynamic modeling method has been developed. The modeling results show that the uncoupled and coupled calculations result in significantly different predictions. The calculations based on the coupled model predict much faster rates of alignment than those predicted using the uncoupled approach.

The effect of curing on the performance of ACF bonded chip-on-flex assemblies after thermal ageing

Purpose – Anisotropic conductive film (ACF) is now an attractive technology for direct mounting of chips onto the substrate as an alternative to lead-free solders. However, despite its various advantages over other technologies, it also has many unresolved reliability issues. For instance, the performance of ACF assembly in high temperature applications is questionable. The purpose of this paper is to study the effect of bonding temperatures on the curing of ACFs, and their mechanical and electrical performance after high temperature ageing. Design/methodology/approach – In the work presented in this paper, the curing degree of an ACF at different bonding temperatures was measured using a differential scanning calorimeter. The adhesion strength and the contact resistance of ACF bonded chip-on-flex assembly were measured before and after thermal ageing and the results were correlated with the curing degree of ACF. The ACF was an epoxy-based adhesive in which Au-Ni coated polymer particles were randomly dispersed. Findings – The results showed that higher bonding temperatures had resulted in better ACF curing and stronger adhesion. After ageing, the adhesion strength increased for the samples bonded at lower temperatures and decreased for the samples bonded at higher temperatures. ACF assemblies with higher degrees of curing showed smaller increases in contact resistance after ageing. Conduction gaps at the bump-particle and/or particle-pad interfaces were found with the help of scanning electron microscopy and are thought to be the root cause of the increase in contact resistance. Originality/value – The present study focuses on the effect of bonding temperatures on the curing of ACFs, and their adhesion strength and electrical performances after high temperature ageing. The results of this study may help the development of ACFs with higher heat resistance, so that ACFs can be considered as an alternative to lead-free solders.

Moisture Effects on the Reliability of Anisotropic Conductive Films

Anisotropic conductive film (ACF) which consists of an adhesive epoxy matrix and randomly distributed conductive particles are widely used as the connection material for electronic devices with high I/O counts. However, for the semiconductor industry the reliability of the ACF is still a major concern due to a lack of experimental reliability data. This paper reports an investigation into the moisture effects on the reliability of ACF interconnections in the flip-chip-on-flex (FCOF) applications. A macro-micro 3D finite element modeling technique was used in order to make the multi-length-scale modeling of the ACF flip chip possible. The purposes of this modeling work was to understand the role that moisture plays in the failure of ACF flip chips, and to look into the influence of physical properties and geometric characteristics, such as the coefficient of the moisture expansion (CME), Young's modulus of the adhesive matrix and the bump height on the reliability of the ACF interconnections in a humid environment. Simulation results suggest that moisture-induced swelling of the adhesive matrix is the major cause of the ACF joint opening. Modeling results are consistent with the findings in the experimental work.

Macro-micro modelling of moisture induced stresses in an ACF flip chip assembly

Purpose – This paper discusses the use of modelling techniques to predict the reliability of an anisotropic conductive film (ACF) flip chip in a humid environment. The purpose of this modelling work is to understand the role that moisture plays in the failure of ACF flip chips. Design/methodology/approach – A 3D macro-micro finite element modelling technique was used to determine the moisture diffusion and moisture-induced stresses inside the ACF flip chip. Findings – The results show that the ACF layer in the flip chip can be expected to be fully saturated with moisture after 3?h at 121°C, 100%RH, 2?atm test conditions. The swelling effect of the adhesive due to this moisture absorption causes predominately tensile stress at the interface between the adhesive and the metallization, which could cause a decrease in the contact area, and therefore an increase in the contact resistance. Originality/value – This paper introduces a macro-micro modelling technique which enables more detailed 3D modelling analysis of an ACF flip chip than previously.

Thermal analysis of LEDS for liquid crystal display's backlighting

This paper investigated the thermal design of the light emitting diode (LED)onto the board and its packaging. The LED was a 6-lead MultiLED with three chips designed for LCD backlighting and other lighting purposes. A 3D finite element model of this LED was built up and thermal analysis was carried out using the multi physics software package PHYSICA. The modeling results were presented as temperature distributions in each LED, and the predicted junction temperature was used for thermal resistance calculation. The results for the board structure indicated that (1) removing the foil attach decreased the thermal resistance, (2) Increasing the copper foil thickness reduced the thermal resistance. package design indicated that the SMT designed LED with integrated slug gave lower thermal resistance. Pb-free solder material gave lower thermal resistance and junction temperature when compared with conductive adhesive

Effect of fluid dynamics and device mechanism on biofluid behaviour in microchannel systems: modelling biofluids in a microchannel biochip separator

Biofluid behaviour in microchannel systems is investigated in this paper through the modelling of a microfluidic biochip developed for the separation of blood plasma. Based on particular assumptions, the effects of some mechanical features of the microchannels on behaviour of the biofluid are explored. These include microchannel, constriction, bending channel, bifurcation as well as channel length ratio between the main and side channels. The key characteristics and effects of the microfluidic dynamics are discussed in terms of separation efficiency of the red blood cells with respect to the rest of the medium. The effects include the Fahraeus and Fahraeus-Lindqvist effects, the Zweifach-Fung bifurcation law, the cell-free layer phenomenon. The characteristics of the microfluid dynamics include the properties of the laminar flow as well as particle lateral or spinning trajectories. In this paper the fluid is modelled as a single-phase flow assuming either Newtonian or Non-Newtonian behaviours to investigate the effect of the viscosity on flow and separation efficiency. It is found that, for a flow rate controlled Newtonian flow system, viscosity and outlet pressure have little effect on velocity distribution. When the fluid is assumed to be Non-Newtonian more fluid is separated than observed in the Newtonian case, leading to reduction of the flow rate ratio between the main and side channels as well as the system pressure as a whole.