Experimental and Modelling Analysis on the Moisture Induced Failures in Flip Chip on Flex Interconnections with Anisotropic Conductive Film

This paper reports the investigations into the moisture induced failures in flip-chip-on-flex interconnections with anisotropic conductive films (ACF). Both experimental and modeling methods were applied. In the experiments, the contact resistance was used as a quality indicator and was measured continuously during the accelerated tests (autoclave tests). The temperature, relative humidity and the pressure were set at 121°C, 100%RH, 1atm respectively. The contact resistance of the ACF joints increased during the tests and nearly 25% of the joints were found to be open after 168 hours' testing time. Visible conduction gaps between the adhesive and substrate pads were observed. Cracks at the adhesive/flex interface were also found. It is believed that the swelling effect of the adhesive and the water penetration along the adhesive/flex interface are the main causes of this contact degradation. Another finding from the experimental work was that the ACF interconnections that had undergone the reflow treatment were more sensitive to the moisture and showed worse reliability during the tests. For a better understanding of the experimental results, 3D finite element (FE) models were built and a macro-micro modeling method was used to determine the moisture diffusion and moisture-induced stresses inside the ACF joints. Modeling results are consistent with the findings in the experimental work.

Experimental and numerical study of the cold crucible melting process

The cold crucible, or induction skull melting process as is otherwise known, has the potential to produce high purity melts of a range of difficult to melt materials, including Ti–Al and Ti6Al4V alloys for Aerospace, Ti–Ta and other biocompatible materials for surgical implants, silicon for photovoltaic and electronic applications, etc. A water cooled AC coil surrounds the crucible causing induction currents to melt the alloy and partially suspend it against gravity away from water-cooled surfaces. Strong stirring takes place in the melt due to the induced electromagnetic Lorentz forces and very high temperatures are attainable under the right conditions (i.e., provided contact with water cooled walls is minimised). In a joint numerical and experimental research programme, various aspects of the design and operation of this process are investigated to increase our understanding of the physical mechanisms involved and to maximise process efficiency. A combination of FV and Spectral CFD techniques are used at Greenwich to tackle this problem numerically, with the experimental work taking place at Birmingham University. Results of this study, presented here, highlight the influence of turbulence and free surface behaviour on attained superheat and also discuss coil design variations and dual frequency options that may lead to winning crucible designs.

Experimental and numerical study of the cold crucible melting process

The cold crucible, or induction skull melting process as is otherwise known, has the potential to produce high purity melts of a range of difficult to melt materials, including Ti–Al and Ti6Al4V alloys for Aerospace, Ti–Ta and other biocompatible materials for surgical implants, silicon for photovoltaic and electronic applications, etc. A water cooled AC coil surrounds the crucible causing induction currents to melt the alloy and partially suspend it against gravity away from water-cooled surfaces. Strong stirring takes place in the melt due to the induced electromagnetic Lorentz forces and very high temperatures are attainable under the right conditions (i.e., provided contact with water cooled walls is minimised). In a joint numerical and experimental research programme, various aspects of the design and operation of this process are investigated to increase our understanding of the physical mechanisms involved and to maximise process efficiency. A combination of FV and Spectral CFD techniques are used at Greenwich to tackle this problem numerically, with the experimental work taking place at Birmingham University. Results of this study, presented here, highlight the influence of turbulence and free surface behaviour on attained superheat and also discuss coil design variations and dual frequency options that may lead to winning crucible designs.

Surface-enhanced Raman scattering studies of rhodanines: Evidence for substrate surface-induced dimerization

The surface-enhanced Raman scattering (SERS) spectra of rhodanine adsorbed on silver nanoparticles have been examined using 514.5 and 632.8 nm excitation. There is evidence that, under the experimental conditions used, rhodanine undergoes a nanoparticle surface-induced reaction resulting in the formation of a dimeric species via the active methylene group in a process which is analogous to the Knoevenagel reaction. The experimental observations are supported by DFT calculations at the B3-LYP/cc-pVDZ level. Calculated energies for the interaction of the E and Z isomers of the dimers of rhodanine with silver nanoparticles support a model in which the (intra-molecular hydrogen bonded) E isomer dimer is of lower energy than the Z isomer. A strong band, at 1566 cm(-1), in the SERS spectrum of rhodanine is assigned to the nu(C=C) mode of the dimer species.