Wire bond reliability for power electronic modules - effect of bonding temperature

In this paper, thermal cycling reliability along with ANSYS analysis of the residual stress generated in heavy-gauge Al bond wires at different bonding temperatures is reported. 99.999% pure Al wires of 375 mum in diameter, were ultrasonically bonded to silicon dies coated with a 5mum thick Al metallisation at 25degC (room temperature), 100degC and 200degC, respectively (with the same bonding parameters). The wire bonded samples were then subjected to thermal cycling in air from -60degC to +150degC. The degradation rate of the wire bonds was assessed by means of bond shear test and via microstructural characterisation. Prior to thermal cycling, the shear strength of all of the wire bonds was approximately equal to the shear strength of pure aluminum and independent of bonding temperature. During thermal cycling, however, the shear strength of room temperature bonded samples was observed to decrease more rapidly (as compared to bonds formed at 100degC and 200degC) as a result of a high crack propagation rate across the bonding area. In addition, modification of the grain structure at the bonding interface was also observed with bonding temperature, leading to changes in the mechanical properties of the wire. The heat and pressure induced by the high temperature bonding is believed to promote grain recovery and recrystallisation, softening the wires through removal of the dislocations and plastic strain energy. Coarse grains formed at the bonding interface after bonding at elevated temperatures may also contribute to greater resistance for crack propagation, thus lowering the wire bond degradation rate

Reliability analysis for power electronics modules

This paper discusses the reliability of power electronics modules. The approach taken combines numerical modeling techniques with experimentation and accelerated testing to identify failure modes and mechanisms for the power module structure and most importantly the root cause of a potential failure. The paper details results for two types of failure (i) wire bond fatigue and (ii) substrate delamination. Finite element method modeling techniques have been used to predict the stress distribution within the module structures. A response surface optimisation approach has been employed to enable the optimal design and parameter sensitivity to be determined. The response surface is used by a Monte Carlo method to determine the effects of uncertainty in the design.

Computer modelling analysis of the globtop's effects on aluminium wirebond reliability

In power electronics modules, heavy aluminium wires, i.e. wire diameters greater than 100 microns, are bonded to the active semiconductor devices and conductor metallization to form electric circuits of the power electronic module. Due to the high currents that may flow through these wires, a single connection usually contains several wires and thus, a large number of wires are used in a power electronics module. Under normal operation or test condition, a significant amount of stresses and strains induced in the wire and bonding interfaces, resulting in failure over time. In this paper, computer modelling techniques are used to analyse the effect of globtop design on the reliability of aluminium wirebonds under cyclic thermal-mechanical loading conditions. The results will show the sensitivity of the reliability of the wirebonds to the changes in the geometry and the material properties of the wirebond globtop.