Investigation of the cold crucible melting process: experimental and numerical study

The dynamic process of melting different materials in a cold crucible is being studied experimentally with parallel numerical modelling work. The numerical simulation uses a variety of complementing models: finite volume, integral equation and pseudo-spectral methods combined to achieve the accurate description of the dynamic melting process. Results show the temperature history of the melting process with a comparison of the experimental and computed heat losses in the various parts of the equipment. The free surface visual observations are compared to the numerically predicted surface shapes.

Experimental and modeling analysis of the reliability of the anisotropic conductive films

Experiments as well as computer modeling methods have been used to investigate the effect of the solder reflow process on the electrical characteristics and reliability of anisotropic conductive film (ACF) interconnections. In the experiments, the contact resistance of the ACF interconnections was found to increase after a subsequent reflow and the magnitude of this increase was strongly correlated to the peak temperature of the reflow profile. In fact, nearly 40 percent of the joints were opened (i.e. lifted away from the pad) after the reflow with a peak temperature of 260 OC while no openings was observed when the peak temperature was 210 "C. It is believed that the CTE mismatch between the polymer particle and the adhesive matrix is the main cause of this contact degradation. To understand this phenomenon better, a 3-D model of an ACF joint structure was built and Finite Element Analysis was used to predict the stress distrihution in the conductive particles, adhesive matrix and metal pads during the reflow process. The effects of the peak temperature, the CTE of the adhesive matrix and the bump height on the reliability of the ACF interconnections were discussed.

No-flow underfill flip chip assembly–an experimental and modeling analysis

In the flip-chip assembly process, no-flow underfill materials have a particular advantage over traditional underfill: the application and curing of the former can be undertaken before and during the reflow process. This advantage can be exploited to increase the flip-chip manufacturing throughput. However, adopting a no-flow underfill process may introduce reliability issues such as underfill entrapment, delamination at interfaces between underfill and other materials, and lower solder joint fatigue life. This paper presents an analysis on the assembly and the reliability of flip-chips with no-flow underfill. The methodology adopted in the work is a combination of experimental and computer-modeling methods. Two types of no-flow underfill materials have been used for the flip chips. The samples have been inspected with X-ray and scanning acoustic microscope inspection systems to find voids and other defects. Eleven samples for each type of underfill material have been subjected to thermal shock test and the number of cycles to failure for these flip chips have been found. In the computer modeling part of the work, a comprehensive parametric study has provided details on the relationship between the material properties and reliability, and on how underfill entrapment may affect the thermal–mechanical fatigue life of flip chips with no-flow underfill.

Experimental and Modelling Analysis on the Moisture Induced Failures in Flip Chip on Flex Interconnections with Anisotropic Conductive Film

This paper reports the investigations into the moisture induced failures in flip-chip-on-flex interconnections with anisotropic conductive films (ACF). Both experimental and modeling methods were applied. In the experiments, the contact resistance was used as a quality indicator and was measured continuously during the accelerated tests (autoclave tests). The temperature, relative humidity and the pressure were set at 121°C, 100%RH, 1atm respectively. The contact resistance of the ACF joints increased during the tests and nearly 25% of the joints were found to be open after 168 hours' testing time. Visible conduction gaps between the adhesive and substrate pads were observed. Cracks at the adhesive/flex interface were also found. It is believed that the swelling effect of the adhesive and the water penetration along the adhesive/flex interface are the main causes of this contact degradation. Another finding from the experimental work was that the ACF interconnections that had undergone the reflow treatment were more sensitive to the moisture and showed worse reliability during the tests. For a better understanding of the experimental results, 3D finite element (FE) models were built and a macro-micro modeling method was used to determine the moisture diffusion and moisture-induced stresses inside the ACF joints. Modeling results are consistent with the findings in the experimental work.

Review of methods to predict solder joint reliability under thermo-mechanical cycling

Solder joints are often the cause of failure in electronic devices, failing due to cyclic creep induced ductile fatigue. This paper will review the modelling methods available to predict the lifetime of SnPb and SnAgCu solder joints under thermo-mechanical cycling conditions such as power cycling, accelerated thermal cycling and isothermal testing, the methods do not apply to other damage mechanisms such as vibration or drop-testing. Analytical methods such as recommended by the IPC are covered, which are simple to use but limited in capability. Finite element modelling methods are reviewed, along with the necessary constitutive laws and fatigue laws for solder, these offer the most accurate predictions at the current time. Research on state-of-the-art damage mechanics methods is also presented, although these have not undergone enough experimental validation to be recommended at present