Experimental and modeling analysis of the reliability of the anisotropic conductive films

Experiments as well as computer modeling methods have been used to investigate the effect of the solder reflow process on the electrical characteristics and reliability of anisotropic conductive film (ACF) interconnections. In the experiments, the contact resistance of the ACF interconnections was found to increase after a subsequent reflow and the magnitude of this increase was strongly correlated to the peak temperature of the reflow profile. In fact, nearly 40 percent of the joints were opened (i.e. lifted away from the pad) after the reflow with a peak temperature of 260 OC while no openings was observed when the peak temperature was 210 "C. It is believed that the CTE mismatch between the polymer particle and the adhesive matrix is the main cause of this contact degradation. To understand this phenomenon better, a 3-D model of an ACF joint structure was built and Finite Element Analysis was used to predict the stress distrihution in the conductive particles, adhesive matrix and metal pads during the reflow process. The effects of the peak temperature, the CTE of the adhesive matrix and the bump height on the reliability of the ACF interconnections were discussed.

Experimental and Modelling Analysis on the Moisture Induced Failures in Flip Chip on Flex Interconnections with Anisotropic Conductive Film

This paper reports the investigations into the moisture induced failures in flip-chip-on-flex interconnections with anisotropic conductive films (ACF). Both experimental and modeling methods were applied. In the experiments, the contact resistance was used as a quality indicator and was measured continuously during the accelerated tests (autoclave tests). The temperature, relative humidity and the pressure were set at 121°C, 100%RH, 1atm respectively. The contact resistance of the ACF joints increased during the tests and nearly 25% of the joints were found to be open after 168 hours' testing time. Visible conduction gaps between the adhesive and substrate pads were observed. Cracks at the adhesive/flex interface were also found. It is believed that the swelling effect of the adhesive and the water penetration along the adhesive/flex interface are the main causes of this contact degradation. Another finding from the experimental work was that the ACF interconnections that had undergone the reflow treatment were more sensitive to the moisture and showed worse reliability during the tests. For a better understanding of the experimental results, 3D finite element (FE) models were built and a macro-micro modeling method was used to determine the moisture diffusion and moisture-induced stresses inside the ACF joints. Modeling results are consistent with the findings in the experimental work.

Moisture Effects on the Reliability of Anisotropic Conductive Films

Anisotropic conductive film (ACF) which consists of an adhesive epoxy matrix and randomly distributed conductive particles are widely used as the connection material for electronic devices with high I/O counts. However, for the semiconductor industry the reliability of the ACF is still a major concern due to a lack of experimental reliability data. This paper reports an investigation into the moisture effects on the reliability of ACF interconnections in the flip-chip-on-flex (FCOF) applications. A macro-micro 3D finite element modeling technique was used in order to make the multi-length-scale modeling of the ACF flip chip possible. The purposes of this modeling work was to understand the role that moisture plays in the failure of ACF flip chips, and to look into the influence of physical properties and geometric characteristics, such as the coefficient of the moisture expansion (CME), Young's modulus of the adhesive matrix and the bump height on the reliability of the ACF interconnections in a humid environment. Simulation results suggest that moisture-induced swelling of the adhesive matrix is the major cause of the ACF joint opening. Modeling results are consistent with the findings in the experimental work.

Effects of thermal cycling profiles on the performance of chip-on-flex assembly using anisotropic conductive films

Anisotropic conductive films (ACFs) are widely used in the electronic packaging industries because of their fine pitch potential and the assembly process is simpler compared to the soldering process. However, there are still unsolved issues in the volume productions using ACFs. The main reason is that the effects of many factors on the interconnects are not well understood. This work focuses on the performance of ACF-bonded chip-on-flex assemblies subjected to a range of thermal cycling test conditions. Both experimental and three-dimensional finite element computer modelling methods are used. It has been revealed that greater temperature ranges and longer dwell-times give rise to higher stresses in the ACF interconnects. Higher stresses are concentrated along the edges of the chip-ACF interfaces. In the experiments, the results show that higher temperature ranges and prolonged dwell times increase contact resistance values. Close examination of the microstructures along the bond-line through the scanning electron microscope (SEM) indicates that cyclic thermal loads disjoint the conductive particles from the bump of the chip and/or pad of the substrate and this is thought to be related to the increase of the contact resistance value and the failure of the ACF joints.