Polymer waveguide and VCSEL array multi-physics modelling for OECB based optical backplanes [opto-electrical circuit boards]

The deployment of OECBs (opto-electrical circuit boards) is expected to make a significant impact in the telecomm switches arena within the next five years. This will create optical backplanes with high speed point-to-point optical interconnects. The crucial aspect in the manufacturing process of the optical backplane is the successful coupling between VCSEL (vertical cavity surface emitting laser) device and embedded waveguide in the OECB. The results from a thermo-mechanical analysis are being used in a purely optical model, which solves optical energy and attenuation from the VCSEL aperture into, and then through, the waveguide. Results from the modelling are being investigated using DOE analysis to identify packaging parameters that minimise misalignment. This is achieved via a specialist optimisation software package. Results from the thermomechanical and optical models are discussed as are experimental results from the DOE.

Comparative wetting behavior of Sn-0.7Cu and Sn-0.7Cu-0.3Ni solders on Cu and Ni substrates

Electronic packaging industries are now in great challenge to find a suitable lead-free solder as an interconnection material to replace the conventional SnPb solders. Many solders such as SnCu, SnAg, SnAgCu, SnZn, SnBi have already been proposed as the replacement but none of them has reached the physical and metallurgical properties similar to the SnPb solder. However, wetting is one of the basic problems that make the lead-free solder inferior as compared to the SnPb solder. Therefore, alloying with the help of third, fourth or fifth element is the researchers' interest to improve the wetting behavior of lead-free solders. This paper describes the comparative wetting behavior of Sn-0.7Cu and Sn-0.7Cu-0.3Ni solders on Cu and Ni substrates. Wetting balance tests were performed to assess the wetting behaviors. Three different commercial fluxes namely no-clean (NC), non-activated (R) and water soluble organic acid (WS)fluxes were used to assess the wettability for three solder bath temperatures. It was found that Sn0.7Cu-03Ni solder exhibits better wettability on Cu substrate for NC and WS fluxes whereas reverse results were found for R-type flux. In the case of Ni substrate, Sn-0.7Cu-0.3Ni solder showed better wetting behavior compared to the well-known Sn-0.7Cu solder. Among the three fluxes, R-type flux showed the worst performance. Very large contact angles were documented for both solders with this flux. Higher solder bath temperature lowered the contact angles, increased the wetting forces and enhanced the wettability. Computer modeling of wetting balance test revealed that both the wetting force and meniscus height are inversely proportional to the contact angles. Modeling results also reveal that increase in solder bath depths and radiuses do not affect significantly on the wetting behavior.