The biocompatibility of resin-modified glass-ionomer cements for dentistry

OBJECTIVES: The biological effects of resin-modified glass-ionomer cements as used in clinical dentistry are described, and the literature reviewed on this topic. METHODS: Information on resin-modified glass-ionomers and on 2-hydroxyethyl methacrylate (HEMA), the most damaging substance released by these materials, has been collected from over 50 published papers. These were mainly identified through Scopus. RESULTS: HEMA is known to be released from these materials and has a variety of damaging biological properties, ranging from pulpal inflammation to allergic contact dermatitis. These are therefore potential hazards from resin-modified glass-ionomers. However, clinical results with these materials that have been reported to date are generally positive. CONCLUSIONS/SIGNIFICANCE: Resin-modified glass-ionomers cannot be considered biocompatible to nearly the same extent as conventional glass-ionomers. Care needs to be taken with regard to their use in dentistry and, in particular, dental personnel may be at risk from adverse effects such as contact dermatitis and other immunological responses.

Water sorption/desorption in polyacid-modified composite resins for dentistry

The water sorption and desorption behaviour of three commercial polyacid-modified composite resins used in clinical dentistry have been studied in detail. Cured specimens of each material were subjected to two successive water uptake cycles in an atmosphere of 93% relative humidity, with one intervening desorption cycle in a desiccating atmosphere over concentrated sulfuric acid. Specimens were found to absorb and desorb water according Fick's law until Mt/M(infinity) values of approximately 0.5. Diffusion rates for uptake varied between cycles, ranging from 2.37-4.53 x 10(-9 )cm(2) s(-1) for 1st cycle to 0.85-2.72 x 10(-8 )cm(2 )s(-1) for 2nd cycle. Desorption rates were similar to those for 2nd cycle sorption, and ranged from 0.86 to 5.47 x 10(-8 )cm(2 )s(-1). Equilibration times for 1st cycle water uptake were greater than for 2nd cycle sorption and for desorption and overall the behaviour of polyacid-modified composites in a high humidity atmosphere was similar to that of conventional composites in water. It is concluded that the hydrophilic components of the former do not bring about an enhanced rate of water transport.

Polyacid-modified composite resins ("compomers") and their use in clinical dentistry

OBJECTIVES: This paper describes the chemistry and properties of polyacid-modified composite resins ("compomers") designed for use in clinical dentistry, and reviews the literature in this area. METHODS: Information has been obtained from over 50 published articles appearing in the dental and biomaterials literature, with studies being principally identified through MedLine. RESULTS: Published work shows that polyacid-modified composite resins constitute a discrete class of polymeric repair material for use in dentistry. Their distinction is that they contain hydrophilic components, and these cause water to be drawn into the material following cure. This triggers an acid-base reaction, and gives the materials certain clinically-desirable properties (fluoride release, buffering capability) that are also associated with glass-ionomer cements. The water uptake leads to a decline in certain, though not all, physical properties. However, clinical studies have shown these materials to perform acceptably in a variety of applications (Class I, Class II and Class V cavities, as fissure sealants and as orthodontic band cements), especially in children's teeth. CONCLUSIONS/SIGNIFICANCE: Polyacid-modified composite resins constitute a versatile class of dental repair material, whose bioactivity confers clinical advantages, and which are particularly useful in children's dentistry.

Collaborating components in mesh-based electronic packaging

From the model geometry creation to the model analysis, the stages in between such as mesh generation are the most manpower intensive phase in a mesh-based computational mechanics simulation process. On the other hand the model analysis is the most computing intensive phase. Advanced computational hardware and software have significantly reduced the computing time - and more importantly the trend is downward. With the kind of models envisaged coming, which are larger, more complex in geometry and modelling, and multiphysics, there is no clear trend that the manpower intensive phase is to decrease significantly in time - in the present way of operation it is more likely to increase with model complexity. In this paper we address this dilemma in collaborating components for models in electronic packaging application.

Zinc polycarboxylate dental cement for the controlled release of an active organic substance: proof of concept

The potential of employing zinc polycarboxylate dental cement as a controlled release material has been studied. Benzalkonium chloride was used as the active ingredient, and incorporated at concentrations of 1, 2 and 3% by mass within the cement. At these levels, there was no observable effect on the speed of setting. Release was followed using an ion-selective electrode to determine changes in chloride ion concentration with time. This technique showed that the additive was released when the cured cement was placed in water, with release occurring by a diffusion mechanism for the first 3 h, but continuing beyond that for up to 1 week. Diffusion coefficients were in the range 5.62 × 10(−6) cm(2) s(−1) (for 1% concentration) to 10.90 × 10(−6) cm(2) s(−1) (for 3% concentration). Up to 3% of the total loading of benzalkonium chloride was released from the zinc polycarboxylate after a week, which is similar to that found in previous studies with glass-ionomer cement. It is concluded that zinc polycarboxylate cement is capable of acting as a useful material for the controlled release of active organic compounds.

A revised classification for direct tooth-colored restorative materials

Composite resins and glass-ionomer cements were introduced to dentistry in the 1960s and 1970s, respectively. Since then, there has been a series of modifications to both materials as well as the development other groups claiming intermediate characteristics between the two. The result is a confusion of materials leading to selection problems. While both materials are tooth-colored, there is a considerable difference in their properties, and it is important that each is used in the appropriate situation. Composite resin materials are esthetic and now show acceptable physical strength and wear resistance. However, they are hydrophobic, and therefore more difficult to handle in the oral environment, and cannot support ion migration. Also, the problems of gaining long-term adhesion to dentin have yet to be overcome. On the other hand, glass ionomers are water-based and therefore have the potential for ion migration, both inward and outward from the restoration, leading to a number of advantages. However, they lack the physical properties required for use in load-bearing areas. A logical classification designed to differentiate the materials was first published by McLean et al in 1994, but in the last 15 years, both types of material have undergone further research and modification. This paper is designed to bring the classification up to date so that the operator can make a suitable, evidence-based, choice when selecting a material for any given situation.

The influence of alkali metal chlorides on the loss of water from glass-ionomer dental cements

The water loss behaviour of a clinical glass-ionomer dental cement has been studied with and without the addition of alkali metal chlorides. Dehydrating conditions were provided by placing specimens in a desiccator over concentrated sulphuric acid. Cements were prepared using either pure water or an aqueous solution of metal chloride (LiCl, NaCl, KCl) at 1.0 mol/dm(3). In addition, NaCl at 0.5 mol/dm(3) was also used to fabricate cements. Disc-shaped specimens of size 6 mm diameter x 2 mm thickness were made, six performulation, and cured at 37 degrees C for 1 hour They were then exposed to desiccating conditions, and the mass measured at regular intervals. All formulations were found to lose water in a diffusion process that equilibrated after approximately 3 weeks. Diffusion coefficients ranged from 2.27 (0.13) x 10(9) with no additive to 1.85 (0.07) x 10(9) m(2)/s with 1.0 mol/dm(3) KCl. For the salts, diffusion coefficients decreased in the order LiCl > NaCl > KCl. There was no statistically significant difference between the diffusion coefficients for 1.0 and 0.5 mol/dm(3) NaCl. For all salts at 1.0 mol/dm(3) and also additive-free cements, equilibrium losses were, with statistical limits, the same, ranging from 6.23 to 6.34%. On the other hand, 0.5 mol/dm(3) NaCl lost significantly more water 7.05%.

Review paper: role of aluminum in glass-ionomer dental cements and its biological effects

The role of aluminum in glass-ionomers and resin-modified glass-ionomers for dentistry is reviewed. Aluminum is included in the glass component of these materials in the form of Al(2)O(3) to confer basicity on the glass and enable the glass to take part in the acid-base setting reactions. Results of studies of these reactions by FTIR and magic-angle spinning (MAS)-NMR spectroscopy are reported and the role of aluminum is discussed in detail. Aluminum has been shown to be present in the glasses in predominantly 4-coordination, as well as 5- and 6-coordination, and during setting a proportion of this is converted to 6-coordinate species within the matrix of the cement. Despite this, mature cements may contain detectable amounts of both 4- and 5-coordinate aluminum. Aluminum has been found to be leached from glass-ionomer cements, with greater amounts being released under acidic conditions. It may be associated with fluoride, with which it is known to complex strongly. Aluminum that enters the body via the gastro-intestinal tract is mainly excreted, and only about 1% ingested aluminum crosses the gut wall. Calculation shows that, if a glass-ionomer filling dissolved completely over 5 years, it would add only an extra 0.5% of the recommended maximum intake of aluminum to an adult patient. This leads to the conclusion that the release of aluminum from either type of glass-ionomer cement in the mouth poses a negligible health hazard.

The interaction of polyacid-modified composite resins ("compomers") with aqueous fluoride solutions

OBJECTIVE: The aim of this study was to investigate how the release of fluoride from two compomers and a fluoridated composite resin was affected by exposure to KF solution. MATERIAL AND METHODS: Two compomers (Dyract AP and Compoglass F) and one fluoridated composite (Wave) were prepared as discs (6 mm diameter and 2 mm thick), curing with a standard dental lamp. They were then stored in either water or 0.5% KF for 1 week, followed by placement in water for periods of 1 week up to 5 weeks total. Fluoride was determined with and without TISAB (to allow complexed and decomplexed fluoride to be determined), and other ion release (Na, Ca, Al, Si, P) was determined by ICP-OES. RESULTS: Specimens were found not to take up fluoride from 100 ppm KF solution in 24 h, but to release additional fluoride when stored for up to five weeks. Compomers released more fluoride cumulatively following exposure to KF solution (p<0.001), all of which was decomplexed, though initial (1 week) values were not statistically significant for Dyract AP. Other ions showed no variations in release over 1 week, regardless of whether the specimens were exposed to KF. Unlike the compomers, Wave showed no change in fluoride release as a result of exposure to KF. CONCLUSIONS: Compomers are affected by KF solution, and release more fluoride (but not other ions) after exposure than if stored in water.

The use of mineral trioxide aggregate in endodontics - status report

Mineral trioxide aggregate (MTA) is a clinical product comprising a mixture of Portland cement and bismuth oxide which is currently used as a root−filling material in dentistry. It has good biological compatibility, is capable of promoting both osteogenesis and cementogensis, and is finding increasing use in endodontic therapy. It is dimensionally stable, and provides an acceptable and durable seal for endodontically treated teeth. This article reviews the chemistry and applications of MTA, and highlights the fact that very little is currently known about the hydration chemistry, phase evolution and stability of this cement in physiological environments. However, biological effects of MTA have been well documented and are considered in detail. The article concludes that this material is a useful addition to the range of materials available for clinical application in endodontics.

Marginal adaptation and performance of bioactive dental restorative materials in deciduous and young permanent teeth

Objective: The aim of this study was to investigate the adaptation of different types of restorations towards deciduous and young permanent teeth. Materials and Methods: Class V cavities were prepared in deciduous and young permanent teeth and filled with different materials (a conventional glass-ionomer, a resin-modified glass-ionomer, a poly-acid-modified composite resin and a conventional composite resin). Specimens were aged in artificial saliva for 1, 6, 12 and 18 months, then examined by SEM. Results: The composite resin and the polyacid-modified composite had better marginal adaptation than the glass-ionomers,though microcracks developed in the enamel of the tooth. The glass-ionomers showed inferior marginal quality and durability, but no microcracking of the enamel. The margins of the resin-modified glass-ionomer were slightly superior to the conventional glass-ionomer. Conditioning improved the adaptation of the composite resin, but the type of tooth made little or no difference to the performance of the restorative material. All materials were associated with the formation of crystals in the gaps between the filling and the tooth; the quantity and shape of these crystals varied with the material. Conclusions: Resin-based materials are generally better at forming sound, durable margins in deciduous and young permanent teeth than cements, but are associated with microcracks in the enamel. All fluoride-releasing materials give rise to crystalline deposits.

Kinetic studies of water uptake and loss in glass-ionomer cements

The water sorption and desorption behaviour of three commercial glass-ionomer cements used in clinical dentistry have been studied in detail. Cured specimens of each material were found to show slight but variable water uptake in high humidity conditions, but steady loss in desiccating ones. This water loss was found to follow Fick's law for the first 4-5 h. Diffusion coefficients at 22 degrees C were: Chemflex 1.34 x 10(-6) cm(2) s(-1), Fuji IX 5.87 x 10(-7) cm(2) s(-1), Aquacem 3.08 x 10(-6) cm(2) s(-1). At 7 degrees C they were: Chemflex 8.90 x 10(-7) cm(2) s(-1), Fuji IX 5.04 x 10(-7) cm(2) s(-1), Aquacem 2.88 x 10(-6) cm(2) s(-1). Activation energies for water loss were determined from the Arrhenius equation and were found to be Chemflex 161.8 J mol(-1), Fuji IX 101.3 J mol(-1), Aquacem 47.1 J mol(-1). Such low values show that water transport requires less energy in these cements than in resin-modified glass-ionomers. Fick's law plots were found not to pass through the origin. This implies that, in each case, there is a small water loss that does not involve diffusion. This was concluded to be water at the surface of the specimens, and was termed "superficial water". As such, it represents a fraction of the previously identified unbound (loose) water. Superficial water levels were: Chemflex 0.56%, Fuji IX 0.23%, Aquacem 0.87%. Equilibrium mass loss values were shown to be unaffected by temperature, and allowed ratios of bound:unbound water to be determined for all three cements. These showed wide variation, ranging from 1:5.26 for Chemflex to 1:1.25 for Fuji IX.

The kinetics of water loss from zinc phosphate and zinc polycarboxylate dental cements

The water desorption behaviour of three different zinc oxide dental cements (two polycarboxylates, one phosphate) has been studied in detail. Disc-shaped specimens of each material were prepared and allowed to lose water by being subjected to a low humidity desiccating atmosphere over concentrated sulfuric acid. In all three cements, water loss was found to follow Fick's second law for at least 6 h (until M(t)/M(infinity) values were around 0.5), with diffusion coefficients ranging from 6.03 x 10(-8 )cm(2 )s(-1) (for the zinc phosphate) to 2.056 x 10(-7 )cm(2 )s(-1) (for one of the zinc polycarboxylates, Poly F Plus). Equilibration times for desorption were of the order of 8 weeks, and equilibrium water losses ranged from 7.1% for zinc phosphate to 16.9% and 17.4% for the two zinc polycarboxylates.

The interaction of zinc oxide-based dental cements with aqueous solutions of potassium fluoride

The ability of zinc oxide-based dental cements (zinc phosphate and zinc polycarboxylate) to take up fluoride from aqueous solution has been studied. Only zinc phosphate cement was found to take up any measurable fluoride after 5 h exposure to the solutions. The zinc oxide filler of the zinc phosphate also failed to take up fluoride from solution. The key interaction for this uptake was thus shown to involve the phosphate groups of the set cement. However, whether this took the form of phosphate/fluoride exchange, or the formation of oxyfluoro-phosphate groups was not clear. Fluoride uptake followed radicaltime kinetics for about 2 h in some cases, but was generally better modelled by the Elovich equation, dq(t)/dt = alpha exp(-beta q(t)). Values for alpha varied from 3.80 to 2.48 x 10(4), and for beta from 7.19 x 10(-3) to 0.1946, though only beta showed any sort of trend, becoming smaller with increasing fluoride concentration. Fluoride was released from the zinc phosphate cements in processes that were diffusion based up to M(t)/M(infinity) of about 0.4. No further release occurred when specimens were placed in fresh volumes of deionised water. Only a fraction of the fluoride taken up was re-released, demonstrating that most of the fluoride taken up becomes irreversibly bound within the cement.

Water transport in resin-modified glass-ionomer dental cement

Water uptake and water loss have been studied in a commercial resin-modified glass-ionomer cement, Fuji II LC, under a variety of conditions. Uptake was generally non-Fickian, but affected by temperature. At room temperature, the equilibrium water uptake values varied from 2.47 to 2.78% whereas at low temperature (12 degrees C), it varied from 0.85 to 1.18%. Cure time affected uptake values significantly. Water uptake was much lower than in conventional glass-ionomer restorative cements exposed to water vapor. Loss of water under desiccating conditions was found to be Fickian for the first 5 h loss at both 22 and 12 degrees C. Diffusion coefficients were between 0.45 and 0.76 x 10( -7) cm(2)/s, with low temperature diffusion coefficients slightly greater than those at room temperature. Plotting water loss as percentage versus s(-(1/2)) allowed activation energies to be determined from the Arrhenius equation and these were found to be 65.6, 79.8, and 7.7 kJ/mol respectively for 30, 20, and 10 s cure times. The overall conclusion is that the main advantage of incorporating HEMA into resin-modified-glass-ionomers is to alter water loss behavior. Rate of water loss and total amount lost are both reduced. Hence, resin-modified glass-ionomers are less sensitive to water loss than conventional glass-ionomers.