Reinforcement corrosion initiation and activation times in concrete structures exposed to severe marine environments

The corrosion of steel reinforcement bars in reinforced concrete structures exposed to severe marine environments usually is attributed to the aggressive nature of chloride ions. In some cases in practice corrosion has been observed to commence already within a few years of exposure even with considerable concrete cover to the reinforcement and apparently high quality concretes. However, there are a number of other cases in practice for which corrosion initiation took much longer, even in cases with quite modest concrete cover and modest concrete quality. Many of these structures show satisfactory long-term structural performance, despite having high levels of localized chloride concentrations at the reinforcement. This disparity was noted already more than 50 years ago, but appears still not fully explained. This paper presents a systematic overview of cases reported in the engineering and corrosion literature and considers possible reasons for these differences. Consistent with observations by others, the data show that concretes made from blast furnace cements have better corrosion durability properties. The data also strongly suggest that concretes made with limestone or non-reactive dolomite aggregates or sufficiently high levels of other forms of calcium carbonates have favourable reinforcement corrosion properties. Both corrosion initiation and the onset of significant damage are delayed. Some possible reasons for this are explored briefly.

A preliminary investigation of the in vitro bioactivity of white Portland cement

Freshly-mixed and partially-cured ordinary Portland cement (OPC) pastes have been shown to exhibit good biological compatibility with a range of cells and tissue-types; particularly those associated with bone formation. Formulations based on OPC have been used as dental restoratives and are now being investigated for their potential use in orthopaedic repair. Despite the current clinical interest in OPCs, very little is known about their chemistry in the physiological environment. In this respect, research to investigate aspects of the interactions between a white Portland cement (WPC) paste and simulated body fluid (SBF) has been carried out in vitro. Exposure to SBF has been found to promote the precipitation of a layer of 'bone-like' hydroxyapatite on the surface of WPC paste which underpins its ability to integrate with living tissue. The dissolution of portlandite and formation of calcite were also observed on contact with SBF.

The use of mineral trioxide aggregate in endodontics - status report

Mineral trioxide aggregate (MTA) is a clinical product comprising a mixture of Portland cement and bismuth oxide which is currently used as a root−filling material in dentistry. It has good biological compatibility, is capable of promoting both osteogenesis and cementogensis, and is finding increasing use in endodontic therapy. It is dimensionally stable, and provides an acceptable and durable seal for endodontically treated teeth. This article reviews the chemistry and applications of MTA, and highlights the fact that very little is currently known about the hydration chemistry, phase evolution and stability of this cement in physiological environments. However, biological effects of MTA have been well documented and are considered in detail. The article concludes that this material is a useful addition to the range of materials available for clinical application in endodontics.