Effect of adding 0.3 wt% Ni into the Sn–0.7 wt%Cu solder: part I: wetting behavior on Cu and Ni substrates

Comparative wetting behavior of Sn-0.7Cu and Sn-0.7Cu-0.3Ni solders on Cu and Ni substrates were assessed through the wetting balance test. No-clean (NC), non-activated (R) and water soluble organic acid (WS) fluxes were used to assess the wetting behavior for three different solder bath temperatures of 255, 275 and 295 °C. Experimental results unveiled that adding of 0.3 wt% Ni into Sn-0.7Cu solder can improve the wetting on Cu substrate when NC and WS fluxes are used. However, such addition of Ni did not improve the wetting of Sn-0.7Cu solder for R-type flux. In the case of Ni substrate, addition of Ni helped to improve the wetting for all three types of fluxes as higher wetting forces were documented for Sn-0.7Cu-0.3Ni solder compared to the Sn-0.7Cu solder. Among the fluxes, worst performance was observed for R-type flux. Very large contact angles were recorded for both solders with this kind of flux. Experimental results also revealed that higher solder bath temperature played an important role to lower the contact angle, to increase the wetting force and to enhance the wetting. Computer modeling of wetting balance test also revealed that both the wetting force and meniscus height are inversely proportional to the contact angles. Besides, solder bath depth and radius do not affect significantly on the wetting behavior.

Effect of adding 0.3wt% Ni into the Sn-0.7wt% Cu solder - Part II: Growth of intermetallic layer with Cu during wetting and aging

The growth behavior of intermetallic layer with or without adding 0.3 wt% Ni into the Sn-0.7Cu solder was studied during the wetting reaction on Cu-substrate and thereafter in solid-state aging condition. The Cu-solder reaction couple was prepared at 255, 275 and 295 °C for 10 s. The samples reacted at 255 °C were then isothermally aged for 2-14 days at 150 °C. The reaction species formed for the Sn-0.7Cu/Cu and Sn-0.7Cu-0.3Ni/Cu soldering systems were Cu6Sn5 and (CuNi)6Sn5, respectively. The thickness of the intermetallic compounds formed at the solder/Cu interfaces and also in the bulk of both solders increased with the increase of reaction temperature. It was found that Ni-containing Sn-0.7Cu solder exhibited lower growth of intermetallic layer during wetting and in the early stage of aging and eventually exceeded the intermetallic layer thickness of Sn-0.7Cu/Cu soldering system after 6 days of aging. As the aging time proceeds, a non-uniform intermetallic layer growth tendency was observed for the case of Sn-0.7Cu-0.3Ni solder. The growth behavior of intermetallic layer during aging for both solders followed the diffusion-controlled mechanism. The intermetallic layer growth rate constants for Sn-0.7Cu and Sn-0.7Cu-0.3Ni solders were calculated as 1.41 × 10-17 and 1.89 × 10-17 m2/s, respectively which indicated that adding 0.3 wt% Ni with Sn-0.7Cu solder contributed to the higher growth of intermetallic layer during aging. © 2006 Elsevier B.V. All rights reserved.

Modeling the diffusion of solid copper into liquid solder alloys

During the soldering process, the copper atoms diffuse into liquid solders. The diffusion process determines integrity and the reworking possibility of a solder joint. In order to capture the diffusion scenarios of solid copper into liquid Sn–Pb and Sn–Cu solders, a computer modeling has been performed for 10 s. An analytical model has also been proposed for calculating the diffusion coefficient of copper into liquid solders. It is found that the diffusion coefficient for Sn–Pb solder is 2.74 × 10− 10 m2/s and for Sn–Cu solder is 6.44 × 10−9 m2/s. The modeling results reveal that the diffusion coefficient is one of the major factors that govern the rate at which solid Cu dissolve in the molten solder. The predicted dissolved amounts of copper into solders have been validated with the help of scanning electron microscopic analysis.