The influence of alkali metal chlorides on the loss of water from glass-ionomer dental cements

The water loss behaviour of a clinical glass-ionomer dental cement has been studied with and without the addition of alkali metal chlorides. Dehydrating conditions were provided by placing specimens in a desiccator over concentrated sulphuric acid. Cements were prepared using either pure water or an aqueous solution of metal chloride (LiCl, NaCl, KCl) at 1.0 mol/dm(3). In addition, NaCl at 0.5 mol/dm(3) was also used to fabricate cements. Disc-shaped specimens of size 6 mm diameter x 2 mm thickness were made, six performulation, and cured at 37 degrees C for 1 hour They were then exposed to desiccating conditions, and the mass measured at regular intervals. All formulations were found to lose water in a diffusion process that equilibrated after approximately 3 weeks. Diffusion coefficients ranged from 2.27 (0.13) x 10(9) with no additive to 1.85 (0.07) x 10(9) m(2)/s with 1.0 mol/dm(3) KCl. For the salts, diffusion coefficients decreased in the order LiCl > NaCl > KCl. There was no statistically significant difference between the diffusion coefficients for 1.0 and 0.5 mol/dm(3) NaCl. For all salts at 1.0 mol/dm(3) and also additive-free cements, equilibrium losses were, with statistical limits, the same, ranging from 6.23 to 6.34%. On the other hand, 0.5 mol/dm(3) NaCl lost significantly more water 7.05%.

Review paper: role of aluminum in glass-ionomer dental cements and its biological effects

The role of aluminum in glass-ionomers and resin-modified glass-ionomers for dentistry is reviewed. Aluminum is included in the glass component of these materials in the form of Al(2)O(3) to confer basicity on the glass and enable the glass to take part in the acid-base setting reactions. Results of studies of these reactions by FTIR and magic-angle spinning (MAS)-NMR spectroscopy are reported and the role of aluminum is discussed in detail. Aluminum has been shown to be present in the glasses in predominantly 4-coordination, as well as 5- and 6-coordination, and during setting a proportion of this is converted to 6-coordinate species within the matrix of the cement. Despite this, mature cements may contain detectable amounts of both 4- and 5-coordinate aluminum. Aluminum has been found to be leached from glass-ionomer cements, with greater amounts being released under acidic conditions. It may be associated with fluoride, with which it is known to complex strongly. Aluminum that enters the body via the gastro-intestinal tract is mainly excreted, and only about 1% ingested aluminum crosses the gut wall. Calculation shows that, if a glass-ionomer filling dissolved completely over 5 years, it would add only an extra 0.5% of the recommended maximum intake of aluminum to an adult patient. This leads to the conclusion that the release of aluminum from either type of glass-ionomer cement in the mouth poses a negligible health hazard.

Marginal adaptation and performance of bioactive dental restorative materials in deciduous and young permanent teeth

Objective: The aim of this study was to investigate the adaptation of different types of restorations towards deciduous and young permanent teeth. Materials and Methods: Class V cavities were prepared in deciduous and young permanent teeth and filled with different materials (a conventional glass-ionomer, a resin-modified glass-ionomer, a poly-acid-modified composite resin and a conventional composite resin). Specimens were aged in artificial saliva for 1, 6, 12 and 18 months, then examined by SEM. Results: The composite resin and the polyacid-modified composite had better marginal adaptation than the glass-ionomers,though microcracks developed in the enamel of the tooth. The glass-ionomers showed inferior marginal quality and durability, but no microcracking of the enamel. The margins of the resin-modified glass-ionomer were slightly superior to the conventional glass-ionomer. Conditioning improved the adaptation of the composite resin, but the type of tooth made little or no difference to the performance of the restorative material. All materials were associated with the formation of crystals in the gaps between the filling and the tooth; the quantity and shape of these crystals varied with the material. Conclusions: Resin-based materials are generally better at forming sound, durable margins in deciduous and young permanent teeth than cements, but are associated with microcracks in the enamel. All fluoride-releasing materials give rise to crystalline deposits.

The kinetics of water loss from zinc phosphate and zinc polycarboxylate dental cements

The water desorption behaviour of three different zinc oxide dental cements (two polycarboxylates, one phosphate) has been studied in detail. Disc-shaped specimens of each material were prepared and allowed to lose water by being subjected to a low humidity desiccating atmosphere over concentrated sulfuric acid. In all three cements, water loss was found to follow Fick's second law for at least 6 h (until M(t)/M(infinity) values were around 0.5), with diffusion coefficients ranging from 6.03 x 10(-8 )cm(2 )s(-1) (for the zinc phosphate) to 2.056 x 10(-7 )cm(2 )s(-1) (for one of the zinc polycarboxylates, Poly F Plus). Equilibration times for desorption were of the order of 8 weeks, and equilibrium water losses ranged from 7.1% for zinc phosphate to 16.9% and 17.4% for the two zinc polycarboxylates.