Role of bonding time and temperature on the physical properties of coupled anisotropic conductive–nonconductive adhesive film for flip chip on glass technology

Using thermosetting epoxy based conductive adhesive films for the flip chip interconnect possess a great deal of attractions to the electronics manufacturing industries due to the ever increasing demands for miniaturized electronic products. Adhesive manufacturers have taken many attempts over the last decade to produce a number of types of adhesives and the coupled anisotropic conductive-nonconductive adhesive film is one of them. The successful formation of the flip chip interconnection using this particular type of adhesive depends on, among factors, how the physical properties of the adhesive changes during the bonding process. Experimental measurements of the temperature in the adhesive have revealed that the temperature becomes very close to the required maximum bonding temperature within the first 1s of the bonding time. The higher the bonding temperature the faster the ramp up of temperature is. A dynamic mechanical analysis (DMA) has been carried out to investigate the nature of the changes of the physical properties of the coupled anisotropic conductive-nonconductive adhesive film for a range of bonding parameters. Adhesive samples that are pre-cured at 170, 190 and 210°C for 3, 5 and 10s have been analyzed using a DMA instrument. The results have revealed that the glass transition temperature of this type of adhesive increases with the increase in the bonding time for the bonding temperatures that have been used in this work. For the curing time of 3 and 5s, the maximum glass transition temperature increases with the increase in the bonding temperature, but for the curing time of 10s the maximum glass transition temperature has been observed in the sample which is cured at 190°C. Based on these results it has been concluded that the optimal bonding temperature and time for this kind of adhesive are 190°C and 10s, respectively.

Failure mechanisms of ACF joints under isothermal ageing

The possible failure mechanisms of anisotropic conductive film (ACF) joints under isothermal ageing conditions have been identified through experiments. It has been found that ACF joints formed at higher bonding temperatures can prevent increases in the contact resistance for any ageing temperature. The higher the ageing temperature the higher the electrical failure rate is. The formation of conduction gaps between the conductive particles and the pads and damages to the metal coatings of the particle have been identified as the reasons behind the electrical failures during ageing. In order to understand the mechanism for the formation of the conduction gap and damages in metal coatings during the isothermal ageing, computer modelling has been carried out and the results are discussed extensively. The computer analysis shows that stresses concentrate at the edges of the particle–pad interface, where the adhesive matrix meets the particle. This could lead to subsequent damages and reductions in the adhesion strength in that region and it is possible for the conductive particle to be detached from the pad and the adhesive matrix. It is believed that because of this a conduction gap appears. Furthermore, under thermal loading the thermal expansion of the adhesive matrix squeezes the conductive particle and damages the metal coatings. Experimental evidences support this computational finding. It is, therefore, postulated that if an ACF-based electronic component operates in a high temperature aging condition, its electrical and mechanical functionalities will be at risk.