Reliability study of the electroless Ni–P layer against solder alloy

Copper (Cu) has been widely used in the under bump metallurgy of chip and substrate metallization for chip packaging. However, due to the rapid formation of Cu–Sn intermetallic compound (IMC) at the tin-based solder/Cu interface during solder reaction, the reliability of this type of solder joint is a serious concern. In this work, electroless nickel–phosphorous (Ni–P) layer was deposited on the Cu pad of the flexible substrate as a diffusion barrier between Cu and the solder materials. The deposition was carried out in a commercial acidic sodium hypophosphite bath at 85 °C for different pH values. It was found that for the same deposition time period, higher pH bath composition (mild acidic) yields thicker Ni–P layer with lower phosphorous content. Solder balls having composition 62%Sn–36%Pb–2%Ag were reflowed at 240 °C for 1 to 180 min on three types of electroless Ni–P layers deposited at the pH value of 4, 4.8 and 6, respectively. Thermal stability of the electroless Ni–P barrier layer against the Sn–36%Pb–2%Ag solder reflowed for different time periods was examined by scanning electron microscopy equipped with energy dispersed X-ray. Solder ball shear test was performed in order to find out the relationship between the mechanical strength of solder joints and the characteristics of the electroless Ni–P layer deposited. The layer deposited in the pH 4 acidic bath showed the weak barrier against reflow soldering whereas layer deposited in pH 6 acidic bath showed better barrier against reflow soldering. Mechanical strength of the joints were deteriorated quickly in the layer deposited at pH 4 acidic bath, which was found to be thin and has a high phosphorous content. From the cross-sectional studies and fracture surface analyses, it was found that the appearance of the dark crystalline phosphorous-rich Ni layer weakened the interface and hence lower solder ball shear strength. Ni–Sn IMC formed at the interfaces was found to be more stable at the low phosphorous content (∼14 at.%) layer. Electroless Ni–P deposited at mild acidic bath resulting phosphorous content of around 14 at.% is suggested as the best barrier layer for Sn–36%Pb–2%Ag solder.

Effect of adding 0.3 wt% Ni into the Sn–0.7 wt%Cu solder: part I: wetting behavior on Cu and Ni substrates

Comparative wetting behavior of Sn-0.7Cu and Sn-0.7Cu-0.3Ni solders on Cu and Ni substrates were assessed through the wetting balance test. No-clean (NC), non-activated (R) and water soluble organic acid (WS) fluxes were used to assess the wetting behavior for three different solder bath temperatures of 255, 275 and 295 °C. Experimental results unveiled that adding of 0.3 wt% Ni into Sn-0.7Cu solder can improve the wetting on Cu substrate when NC and WS fluxes are used. However, such addition of Ni did not improve the wetting of Sn-0.7Cu solder for R-type flux. In the case of Ni substrate, addition of Ni helped to improve the wetting for all three types of fluxes as higher wetting forces were documented for Sn-0.7Cu-0.3Ni solder compared to the Sn-0.7Cu solder. Among the fluxes, worst performance was observed for R-type flux. Very large contact angles were recorded for both solders with this kind of flux. Experimental results also revealed that higher solder bath temperature played an important role to lower the contact angle, to increase the wetting force and to enhance the wetting. Computer modeling of wetting balance test also revealed that both the wetting force and meniscus height are inversely proportional to the contact angles. Besides, solder bath depth and radius do not affect significantly on the wetting behavior.

Performance and reliability of flexible substrates when subjected to lead-free processing

The use of flexible substrates is growing in many applications such as computer peripherals, hand held devices, telecommunications, automotive, aerospace, etc. The drive to adopt flexible circuits is due to their ability to reduce size, weight, assembly time and cost of the final product.They also accommodate flexibility by allowing relative movement between component parts and provide a route for three dimensional packaging. This paper will describe some of the current research results from the Flex-No-Lead project, a European Commission sponsored research program. The principle aim of this project is to investigate the processing, performance, and reliability of flexible substrates when subjected to new environmentally friendly, lead-free soldering technologies. This paper will discuss the impact of specific design variables on performance and reliability. In particular the paper will focus on copper track designs, substrate material, dielectric material and solder-mask defined joints.

Effect of current stressing on the reliability of 63Sn37Pb solder joints

The effect of current stressing on the reliability of 63Sn37Pb solder joints with Cu pads was investigated at temperatures of −5 °C and 125 °C up to 600 h. The samples were stressed with 3 A current (6.0 × 102 A/cm2 in the solder joint with diameter of 800 μm and 1.7 × 104 A/cm2 in the Cu trace with cross section area of 35 × 500 μm). The temperatures of the samples and interfacial reaction within the solder joints were examined. The microstructural change of the solder joints aged at 125 °C without current flow was also evaluated for comparison. It was confirmed that the current flow could cause the temperature of solder joints to rise rapidly and remarkably due to accumulation of massive Joule heat generated by the Cu trace. The solder joints stressed at 125 °C with 3 A current had an extensive growth of Cu6Sn5 and Cu3Sn intermetallic compounds (IMC) at both top and bottom solder-to-pad interfaces. It was a direct result of accelerated aging rather than an electromigration or thermomigration effect in this experiment. The kinetic is believed to be bulk diffusion controlled solid-state reaction, irrespective of the electron flow direction. When stressed at −5 °C with 3 A current, no significant change in microstructure and composition of the solder joints had occurred due to a very low diffusivity of the atoms as most Joule heat was eliminated at low temperature. The IMC evolution of the solder joints aged at 125 °C exhibited a subparabolic growth behavior, which is presumed to be a combined mechanism of grain boundary diffusion and bulk diffusion. This is mainly ascribed to the retardant effect against the diffusion course by the sufficiently thick IMC layer that was initially formed during the reflow soldering.

Modeling the diffusion of solid copper into liquid solder alloys

During the soldering process, the copper atoms diffuse into liquid solders. The diffusion process determines integrity and the reworking possibility of a solder joint. In order to capture the diffusion scenarios of solid copper into liquid Sn–Pb and Sn–Cu solders, a computer modeling has been performed for 10 s. An analytical model has also been proposed for calculating the diffusion coefficient of copper into liquid solders. It is found that the diffusion coefficient for Sn–Pb solder is 2.74 × 10− 10 m2/s and for Sn–Cu solder is 6.44 × 10−9 m2/s. The modeling results reveal that the diffusion coefficient is one of the major factors that govern the rate at which solid Cu dissolve in the molten solder. The predicted dissolved amounts of copper into solders have been validated with the help of scanning electron microscopic analysis.

Investigation of wall-slip behaviour in lead-free solder pastes and isotropic conductive adhesives

Slippage due to wall depletion effect is well-known in rheological investigation. The aim of this study was to investigate the influence of the paste microstructure on slip formation for the paste materials (lead-free solder paste and isotropic conductive adhesives). The effect of different flowgeometries, gap heights and surface roughness on the paste viscosity was investigated. The utilisation of different measuring geometries has not clearly showed the presence of wall-slip in the paste samples. The existence of wall-slip was found to be pronounced when gap heights were varied using the parallel plate geometry. It was also found that altering the surface roughness of the parallel plate measuring geometry did not significantly eliminate wall-slip as expected. But results indicate that the use of a relatively rough surface helps to increase paste adhesion to the plates and to a certain extent inducing structural breakdown in the paste. Most importantly, the study also demonstrated on how the wall-slip formation in the paste material could be utilised for understanding of the paste microstructure and its flow behaviour.

Investigation of wall-slip effect on lead-free solder paste and isotropic conductive adhesives

Wall-slip plays an important role in characterising the flow behaviour of solder paste materials. The wall slip arises due to the various attractive and repulsive forces acting between the solder particles and the walls of the measuring geometry.These interactions could lead to the presence of a thin solvent layer adjacent to the wall, which gives rise to slippage. The wall slip effect can play an important role in ensure successfulpaste release after the printing process. Wall-slip plays animportant role in characterising the flow behaviour of solderpastes and isotropic conductive adhesives. The study investigates the wall-slip formation in solder paste andisotropic conductive adhesives using flow visualisation technique. The slip distance was measured for parallel plate with different surface roughness in order to quantify the wallslip formations in these paste materials. An ink marker line was drawn between the parallel plate and the free surface of the sample. The parallel was rotated slowly at a constant shear rate of 0.05 sec-1 and the displacement of the ink marker was observed using a video microscope and image capturing software was utilised to capture the displacement of ink marker. From this study, it was found that the wall-slip effect was evident in all the paste materials. In addition, the different surface roughness of the parallel plates did not prevent the formation of wall-slip. This study has revealed that the wallslip effect could used to understand the flow behaviour of the paste in the stencil printing process.

Rheological characterisation and printing performance of Sn/Ag/Cu solder pastes

Lead-free solder paste printing process accounts for majority of the assembly defects in the electronic manufacturing industry. The study investigates rheological behaviour and stencil printing performance of the lead-free solder pastes (Sn/Ag/Cu). Oscillatory stress sweep test was carried out to study the visco-elastic behaviour of the lead-free solder pastes. The visco-elastic behaviour of the paste encompasses solid and liquid characteristic of the paste, which could be used to study the flow behaviour experienced by the pastes during the stencil printing process. From this study, it was found that the solid characteristics (G0) is higher than the liquid characteristic (G0 0) for the pastes material. In addition, the results from the study showed that the solder paste with a large G0 = G0 0 has a higher cohesiveness resulting in poor withdrawal of the paste during the stencil printing process. The phase angles (d) was used to correlate the quality of the dense suspensions to the formulation of solder paste materials. This study has revealed the value of having a rheological measurement for explaining and characterising solder pastes for stencil printing. As the demand for lead free pastes increases rheological measurements can assist with the formulation or development of new pastes.

Rheological characterisation of solder pastes and isotropic conductive adhesives used for flip-chip assembly

Solder pastes and isotropic conductive adhesives (ICAs) are widely used as a principal bonding medium in the electronic industry. This study investigates the rheological behaviour of the pastes (solder paste and isotropic conductive adhesives) used for flip-chip assembly. Oscillatory stress sweep test are performed to evaluate solid characteristic and cohesiveness of the lead-free solder pastes and isotropic conductive adhesive paste materials. The results show that the G' (storage modulus) is higher than G '' (loss modulus) for the pastes material indicating a solid like behaviour. It result shows that the linear visco-elastic region for the pastes lies in a very small stress range, below 10 Pa. in addition, the stress at which the value of storage modulus is equal to that of loss modulus can be used as an indicator of the paste cohesiveness. The measured cross-over stress at G'=G '' shows that the solder paste has higher stress at G'=G '' compared to conductive adhesives. Creep-recovery test method is used to study the slump behaviour in the paste materials. The conductive adhesive paste shows a good recovery when compared to the solder pastes. (C) 2008 Elsevier B.V. All rights reserved.

Study of the rheological behaviour of Sn-Ag-Cu solder pastes and their correlation with printing performance

Solder paste plays an important role in the electronic assembly process by providing electrical, mechanical and thermal bonding between the components and the substrate. The rheological characterisation of pastes is an important step in the design and development of new paste formulations. With the ever increasing trend of miniaturisation of electronic products, the study of the rheological properties of solder pastes is becoming an integral part in the R&D of new paste formulations and in the quality monitoring and control during paste manufacture and electronic assembly process. This research work outlines some of the novel techniques which can be successfully used to investigate the rheology of leadfree solder pastes. The report also presents the results of the correlation of rheological properties with solder paste printing performance. Four different solder paste samples (namely paste P1, P2, P3 and P4) with different flux vehicle systems and particle size distributions were investigated in the study. As expected, all the paste samples showed shear thinning behaviour. Although the samples displayed similar flow behaviour at high shear rates, differences were observed at low shear rates. In the stencil printing trials, round deposits showed better results than rectangular deposits in terms of paste heights and aperture filling. Our results demonstrate a good correlation between higher paste viscosity and good printing performance. The results of the oscillatory and thixotropy tests were also successfully correlated to the printing behaviour of solder paste.

Viscoelastic properties of solder paste and isotropic conductive adhesives used for flip-chip assembly

The printing of pastes (solder pastes and isotropic conductive adhesives) through very small stencil apertures required for flip-chip pitch sizes is expected to result in increased stencil clogging and incomplete transfer of paste to the printed circuit board pads. There is wide agreement in industry that the paste printing process accounts for the majority of assembly defects, and most defects originate from poor understanding of the effect of printing process parameters on printing performance.

Solder paste characterisation: towards the development of quality control (QC) tool

Purpose – The purpose of this paper is to develop a quality control tool based on rheological test methods for solder paste and flux media. Design/methodology/approach – The rheological characterisation of solder pastes and flux media was carried out through the creep-recovery, thixotropy and viscosity test methods. A rheometer with a parallel plate measuring geometry of 40mm diameter and a gap height of 1mm was used to characterise the paste and associated flux media. Findings – The results from the study showed that the creep-recovery test can be used to study the deformation and recovery of the pastes, which can be used to understand the slump behaviour in solder pastes. In addition, the results from the thixotropic and viscosity test were unsuccessful in determining the differences in the rheological flow behaviour in the solder pastes and the flux medium samples. Research limitations/implications – More extensive rheological and printing testing is needed in order to correlate the findings from this study with the printing performance of the pastes. Practical implications – The rheological test method presented in the paper will provide important information for research and development, quality control and production staff to facilitate the manufacture of solder pastes and flux media. Originality/value – The paper explains how the rheological test can be used as a quality control tool to identify the suitability of a developmental solder paste and flux media used for the printing process.

Effect of long-term aging on the rheological characteristics and printing performance of lead-free solder pastes used for flip-chip assembly

Stencil printing of solder pastes is a critical stage in the SMT assembly process as a high proportion of the solder-related defects can be attributed to this stage. As the trend towards product miniaturization continues, there is a greater need for better understanding of the rheological behaviour and printing performance of new paste formulations. This fundamental understanding is crucial for achieving the repeatable solder paste deposits from board-to-board and pad-to-pad required for more reliable solder interconnections. The paper concerns a study on the effect of ageing on the rheological characteristics and printing performance of new lead-free solder pastes formulations used for flip-chip assembly applications. The objective is to correlate the rheological characteristics of aged paste samples to their printing performance. The methodology developed can be used for bench-marking new lead-free paste formulations in terms of shelf life, the potential deterioration in rheological characteristics and their printing performance.

An investigation into the rheological properties of different lead-free solder pastes for surface mount applications

Purpose – The purpose of this paper is to investigate the rheological behaviour of three different lead-free solder pastes used for surface mount applications in the electronic industry.Design/methodology/approach – This study concerns the rheological measurements of solder paste samples and is made up of three parts. The first part deals with the measurement of rhelogical properties with three different measuring geometries, the second part looks into the effect of frequencies on oscillatory stress sweep measurements and the final part reports on the characterisation and comparison of three different types of Pb-free solder pastes. Findings – Among the three geometries, the serrated parallel plate was found effective in minimising the wall-slip effect. From the oscillatory stresssweep data with different frequencies; it was observed that the linear visco-elastic region is independent of frequency for all the solder paste samples. To understand the shear thinning behaviour of solder paste, the well known Cross and Carreau models were fitted to the viscosity data. Moreover,creep-recovery and dynamic frequency-sweep tests were also carried out without destroying the sample’s structure and have yielded useful information on the pastes behaviour.Research limitations/implications – More extensive research is needed to fully characterise the wall-slip behaviour during the rheological measurements of solder pastes. Practical implications – The rheological test results presented in this paper will be of important value for research and development, quality control and facilitation of the manufacturing of solder pastes and flux mediums. Originality/value – This paper shows how wall-slip effects can be effectively avoided during rheological measurements of solder pastes. The paper also outlines how different rheological test methods can be used to characterise solder paste behaviours

Effect of temperature on slumping behaviour of lead-free solder paste and its rheological simulation

Variation in temperature can have a significant impact on the rheological characterisation of solder pastes used in the electronic assembly of surface mount devices. This paper concerns the study of the effect of temperature on slumping characteristics of lead-free solder pastes. The identification of the slumping characteristics can help in the correlation of the pastes characteristics to its printing performance. Further issues, which aid in justifying the undertaking of such a study, include the temperature differences identified both at the squeegee during the print, and during reflow. Due to these temperature variations, it is imperative to understand how slump differs with a temperature gradient